Lithiophilic Nanowire Guided Li Deposition in Li Metal Batteries.

Lithium (Li) metal batteries (LMBs) provide superior energy densities far beyond current Li-ion batteries (LIBs) but practical applications are hindered by uncontrolled dendrite formation and the build-up of dead Li in "hostless" Li metal anodes. To circumvent these issues, we created a 3D framework of a carbon paper (CP) substrate decorated with lithiophilic nanowires (silicon (Si), germanium (Ge), and SiGe alloy NWs) that provides a robust host for efficient stripping/plating of Li metal. The lithiophilic Li22 Si5 , Li22 (Si0.5 Ge0.5 )5, and Li22 Ge5 formed during rapid Li melt infiltration prevented the formation of dead Li and dendrites. Li22 Ge5 /Li covered CP hosts delivered the best performance, with the lowest overpotentials of 40 mV (three times lower than pristine Li) when cycled at 1 mA cm-2 /1 mAh cm-2 for 1000 h and at 3 mA cm-2 /3 mAh cm-2 for 500 h. Ex situ analysis confirmed the ability of the lithiophilic Li22 Ge5 decorated samples to facilitate uniform Li deposition. When paired with sulfur, LiFePO4, and NMC811 cathodes, the CP-LiGe/Li anodes delivered 200 cycles with 82%, 93%, and 90% capacity retention, respectively. The discovery of the highly stable, lithiophilic NW decorated CP hosts is a promising route toward stable cycling LMBs and provides a new design motif for hosted Li metal anodes.

Improved Compatibility of α-NaMnO2 Cathodes at the Interface with Ionic Liquid Electrolytes.

The behaviour and compatibility of monoclinic sodium manganite, α-NaMnO2, cathodes at the interface with electrolytes based on the 1-ethyl-3-methylimidazolium bis(fluorosulfonyl)imide (EMIFSI) and N-trimethyl-N-butylammonium bis(fluorosulfonyl)imide (N1114FSI) ionic liquids is presented and discussed. The Na+ insertion process was analysed through cyclic voltammetry tests combined with impedance spectroscopy measurements and the cell performance was tested by charge-discharge cycles. XPS and FIB-SEM measurements allowed analysis of the surface composition and the morphology of post-mortem cathodes. Overall, the α-NaMnO2 cathode showed high reversibility in N1114FSI-based electrolyte, delivering 60 % of the initial capacity after 1200 cycles in conjunction with a Coulombic efficiency above 99 %. To our knowledge, these very promising results are the best result obtained till now for monolithic α-NaMnO2 cathodes, are ascribable to the formation of a stable passive layer onto the electrode surface, as confirmed by spectroscopic analysis.