Small ; 15(49): e1904399, 2019 Dec.
Artigo em Inglês | MEDLINE | ID: mdl-31592571

RESUMO

As the hole transport layer (HTL) for perovskite solar cells (PSCs), poly(3-hexylthiophene) (P3HT) has been attracting great interest due to its low-cost, thermal stability, oxygen impermeability, and strong hydrophobicity. In this work, a new doping strategy is developed for P3HT as the HTL in triple-cation/double-halide ((FA1-x-y MAx Csy )Pb(I1-x Brx )3 ) mesoscopic PSCs. Photovoltaic performance and stability of solar cells show remarkable enhancement using a composition of three dopants Li-TFSI, TBP, and Co(III)-TFSI reaching power conversion efficiencies of 19.25% on 0.1 cm2 active area, 16.29% on 1 cm2 active area, and 13.3% on a 43 cm2 active area module without using any additional absorber layer or any interlayer at the PSK/P3HT interface. The results illustrate the positive effect of a cobalt dopant on the band structure of perovskite/P3HT interfaces leading to improved hole extraction and a decrease of trap-assisted recombination. Non-encapsulated large area devices show promising air stability through keeping more than 80% of initial efficiency after 1500 h in atmospheric conditions (relative humidity ≈ 60%, r.t.), whereas encapsulated devices show more than >500 h at 85 °C thermal stability (>80%) and 100 h stability against continuous light soaking (>90%). The boosted efficiency and the improved stability make P3HT a good candidate for low-cost large-scale PSCs.

2.
Nanotechnology ; 26(49): 494002, 2015 Dec 11.
Artigo em Inglês | MEDLINE | ID: mdl-26574237

RESUMO

The past few years have witnessed remarkable progress in solution-processed methylammonium lead halide (CH3NH3PbX3, X = halide) perovskite solar cells (PSCs) with reported photoconversion efficiency (η) exceeding 20% in laboratory-scale devices and reaching up to 13% in their large area perovskite solar modules (PSMs). These devices mostly employ mesoporous TiO2 nanoparticles (NPs) as an electron transport layer (ETL) which provides a scaffold on which the perovskite semiconductor can grow. However, limitations exist which are due to trap-limited electron transport and non-complete pore filling. Herein, we have employed TiO2 nanorods (NRs), a material offering a two-fold higher electronic mobility and higher pore-filing compared to their particle analogues, as an ETL. A crucial issue in NRs' patterning over substrates is resolved by using precise Nd:YVO4 laser ablation, and a champion device with η ∼ 8.1% is reported via a simple and low cost vacuum-vapor assisted sequential processing (V-VASP) of a CH3NH3PbI3 film. Our experiments showed a successful demonstration of NRs-based PSMs via the V-VASP technique which can be applied to fabricate large area modules with a pin-hole free, smooth and dense perovskite layer which is required to build high efficiency devices.

3.
ACS Nano ; 9(8): 8420-9, 2015 Aug 25.
Artigo em Inglês | MEDLINE | ID: mdl-26208221

RESUMO

Perovskite solar cells employing CH3NH3PbI3-xClx active layers show power conversion efficiency (PCE) as high as 20% in single cells and 13% in large area modules. However, their operational stability has often been limited due to degradation of the CH3NH3PbI3-xClx active layer. Here, we report a perovskite solar module (PSM, best and av. PCE 10.5 and 8.1%), employing solution-grown TiO2 nanorods (NRs) as the electron transport layer, which showed an increase in performance (∼5%) even after shelf-life investigation for 2500 h. A crucial issue on the module fabrication was the patterning of the TiO2 NRs, which was solved by interfacial engineering during the growth process and using an optimized laser pulse for patterning. A shelf-life comparison with PSMs built on TiO2 nanoparticles (NPs, best and av. PCE 7.9 and 5.5%) of similar thickness and on a compact TiO2 layer (CL, best and av. PCE 5.8 and 4.9%) shows, in contrast to that observed for NR PSMs, that PCE in NPs and CL PSMs dropped by ∼50 and ∼90%, respectively. This is due to the fact that the CH3NH3PbI3-xClx active layer shows superior phase stability when incorporated in devices with TiO2 NR scaffolds.