Optimizing the Production of Antioxidant and Antibacterial Alkaloids from Macleaya cordata by Subcritical Water Extraction Technology.

In this work, the subcritical water extraction technology was used to extract alkaloids from Macleaya cordata, and the effects of extraction temperature and time on its yield were investigated to find the best extraction conditions. Moreover, the antioxidant capacity and antibacterial activity of Macleaya cordata extract were studied. Furthermore, through the single-factor method, it was found that properly increasing the extraction temperature and prolonging the extraction time was conducive to increasing alkaloid yield. Still, a considerable amount of alkaloids might be decomposed by heat, resulting in a decrease in their yield. The results showed that the optimal extraction temperature of alkaloids from Macleaya cordata with subcritical water is 190 °C, the time is 45 min, and the corresponding maximum yield is 35.19±0.12 mg/g (sanguinarine equivalent in raw materials). In addition, the antioxidation and bacteriostasis abilities of subcritical water extract are better than those of traditional hot water extract, indicating that it is a feasible method to extract alkaloids from Macleaya cordata with subcritical water.

A Binary Ionogel Electrolyte for the Realization of an All Solid-State Electrical Double-Layer Capacitor Performing at Low Temperature.

Over the last years, solid-state electrolytes made of an ionic liquid (IL) confined in a solid (inorganic or polymer) matrix, also known as ionogels, have been proposed to solve the leakage problems occurring at high temperatures in classical electrical double-layer capacitors (EDLCs) with an organic electrolyte, and thereof improve the safety. However, making ionogel-based EDLCs perform with reasonable power at low temperature is still a major challenge due to the high melting point of the confined IL. To overcome these limitations, the present contribution discloses ionogel films prepared in a totally oxygen/moisture-free atmosphere by encapsulating 70 wt % of an equimolar mixture of 1-ethyl-3-methylimidazolium bis(fluorosulfonyl)imide and 1-ethyl-3-methylimidazolium tetrafluoroborate - [EMIm][BF4]0.5[FSI]0.5 - into a poly(vinylidene fluoride-co-hexafluoropropylene) (PVdF-HFP) network. The further called "binary ionogel" films demonstrated a high flexibility and a good ionic conductivity of 5.8 mS cm-1 at 20 °C. Contrary to the ionogels prepared from either [EMIm][FSI] or [EMIm][BF4], displaying melting at Tm=-16 °C and -7 °C, respectively, the crystallization of confined [EMIm][BF4]0.5[FSI]0.5 is quenched in the binary ionogel, which shows only a glass transition at -101 °C. This quenching enables an increased ionicity and ionic diffusion at the interface with the PVdF host network, leading the binary ionogel membrane to display higher ionic conductivity below -20 °C than the parent binary [EMIm][BF4]0.5[FSI]0.5 liquid. Laminate EDLCs were built with a 100 µm thick binary ionogel separator and electrodes made from a hierarchical micro-/mesoporous MgO-templated carbon containing a reasonable proportion of mesopores to enhance the mass transport of ions, especially at low temperature where the ionic diffusion noticeably decreases. The EDLCs operated up to 3.0 V with ideal EDL characteristics from -40 °C to room temperature. Their output specific energy under a discharge power of 1 kW kg-1 is ca. 4 times larger than with a cell implementing the same carbon electrodes together with the binary [EMIm][BF4]0.5[FSI]0.5 liquid. Hence, this binary ionogel electrolyte concept paves the road for developing safe and flexible solid-state energy storage devices operating at subambient temperatures in extreme environments.

Black goes green: single-step solvent exchange for sol-gel synthesis of carbon spherogels as high-performance supercapacitor electrodes.

Nanoporous carbon materials with customized structural features enable sustainable and electrochemical applications through improved performance and efficiency. Carbon spherogels (highly porous carbon aerogel materials consisting of an assembly of hollow carbon nanosphere units with uniform diameters) are desirable candidates as they combine exceptional electrical conductivity, bespoke shell porosity, tunability of the shell thickness, and a high surface area. Herein, we introduce a novel and more environmentally friendly sol-gel synthesis of resorcinol-formaldehyde (RF) templated by polystyrene spheres, forming carbon spherogels in an organic solvent. By tailoring the molar ratio of resorcinol to isopropyl alcohol (R/IPA) and the concentration of polystyrene, the appropriate synthesis conditions were identified to produce carbon spherogels with adjustable wall thicknesses. A single-step solvent exchange process from deionized water to isopropyl alcohol reduces surface tension within the porous gel network, making this approach significantly time and cost-effective. The lower surface tension of IPA enables solvent extraction under ambient conditions, allowing for direct carbonization of RF gels while maintaining a specific surface area loss of less than 20% compared to supercritically dried counterparts. The specific surface areas obtained after physical activation with carbon dioxide are 2300-3600 m2 g-1. Transmission and scanning electron microscopy verify the uniform, hollow carbon sphere network morphology. Specifically, those carbon spherogels are high-performing electrodes for energy storage in a supercapacitor setup featuring a specific capacitance of up to 204 F g-1 at 200 mA g-1 using 1 M potassium hydroxide (KOH) solution as the electrolyte.

Novel Sb-SnO2 Electrode with Ti3+ Self-Doped Urchin-Like Rutile TiO2 Nanoclusters as the Interlayer for the Effective Degradation of Dye Pollutants.

Stable and efficient SnO2 electrodes are very promising for effectively degrading refractory organic pollutants in wastewater treatment. In this regard, we firstly prepared Ti3+ self-doped urchin-like rutile TiO2 nanoclusters (TiO2-x NCs) on a Ti mesh substrate by hydrothermal and electroreduction to serve as an interlayer for the deposition of Sb-SnO2 . The TiO2-x NCs/Sb-SnO2 anode exhibited a high oxygen evolution potential (2.63 V vs. SCE) and strong ⋅OH generation ability for the enhanced amount of absorbed oxygen species. Thus, the degradation results demonstrated its good rhodamine B (RhB), methylene blue (MB), alizarin yellow R (AYR), and methyl orange (MO) removal performance, with the rate constant increased 5.0, 1.9, 1.9, and 4.7 times, respectively, compared to the control Sb-SnO2 electrode. RhB and AYR degradation mechanisms are also proposed based on the results of high-performance liquid chromatography coupled with mass spectrometry and quenching experiments. More importantly, this unique rutile interlayer prolonged the anode lifetime sixfold, given its good lattice match with SnO2 and the three-dimensional concave-convex structure. Consequently, this work paves a new way for designing the crystal form and structure of the interlayers to obtain efficient and stable SnO2 electrodes for addressing dye wastewater problems.