Highly efficient and bendable organic solar cells using a three-dimensional transparent conducting electrode.

A three-dimensional (3D) transparent conducting electrode, consisting of a quasi-periodic array of discrete indium-tin-oxide (ITO) nanoparticles superimposed on a highly conducting oxide-metal-oxide multilayer using ITO and silver oxide (AgOx) as oxide and metal layers, respectively, is synthesized on a polymer substrate and used as an anode in highly flexible organic solar cells (OSCs). The 3D electrode is fabricated using vacuum sputtering sequences to achieve self-assembly of distinct ITO nanoparticles on a continuous ITO-AgOx-ITO multilayer at room-temperature without applying conventional high-temperature vapour-liquid-solid growth, solution-based nanoparticle coating, or complicated nanopatterning techniques. Since the 3D electrode enhances the hole-extraction rate in OSCs owing to its high surface area and low effective series resistance for hole transport, OSCs based on this 3D electrode exhibit a power conversion efficiency that is 11-22% higher than that achievable in OSCs by means of conventional planar ITO film-type electrodes. A record high efficiency of 6.74% can be achieved in a bendable OSC fabricated on a poly(ethylene terephthalate) substrate.

Fabrication of a completely transparent and highly flexible ITO nanoparticle electrode at room temperature.

We report the fabrication of a highly flexible indium tin oxide (ITO) electrode that is completely transparent to light in the visible spectrum. The electrode was fabricated via the formation of a novel ITO nanoarray structure, consisting of discrete globular ITO nanoparticles superimposed on an agglomerated ITO layer, on a heat-sensitive polymer substrate. The ITO nanoarray spontaneously assembled on the surface of the polymer substrate by a simple sputter coating at room temperature, without nanolithographic or solution-based assembly processes being required. The ITO nanoarray exhibited a resistivity of approximately 2.3 × 10(-3) Ω cm and a specular transmission of about 99% at 550 nm, surpassing all previously reported values of these parameters in the case of transparent porous ITO electrodes synthesized via solution-based processes at elevated temperatures. This novel nanoarray structure and its fabrication methodology can be used for coating large-area transparent electrodes on heat-sensitive polymer substrates, a goal unrealizable through currently available solution-based fabrication methods.

Preparation of flexible organic solar cells with highly conductive and transparent metal-oxide multilayer electrodes based on silver oxide.

We report that significantly more transparent yet comparably conductive AgOx films, when compared to Ag films, are synthesized by the inclusion of a remarkably small amount of oxygen (i.e., 2 or 3 atom %) in thin Ag films. An 8 nm thick AgOx (O/Ag=2.4 atom %) film embedded between 30 nm thick ITO films (ITO/AgOx/ITO) achieves a transmittance improvement of 30% when compared to a conventional ITO/Ag/ITO electrode with the same configuration by retaining the sheet resistance in the range of 10-20 Ω sq(-1). The high transmittance provides an excellent opportunity to improve the power-conversion efficiency of organic solar cells (OSCs) by successfully matching the transmittance spectral range of the electrode to the optimal absorption region of low band gap photoactive polymers, which is highly limited in OSCs utilizing conventional ITO/Ag/ITO electrodes. An improvement of the power-conversion efficiency from 4.72 to 5.88% is achieved from highly flexible organic solar cells (OSCs) fabricated on poly(ethylene terephthalate) polymer substrates by replacing the conventional ITO/Ag/ITO electrode with the ITO/AgOx/ITO electrode. This novel transparent electrode can facilitate a cost-effective, high-throughput, room-temperature fabrication solution for producing large-area flexible OSCs on heat-sensitive polymer substrates with excellent power-conversion efficiencies.