RESUMO
The search for alternative materials that can be used for parts of aircraft hydraulic systems has led to the idea of applying S32750 duplex steel for this purpose. This steel is mainly used in the oil and gas, chemical, and food industries. The reasons for this lie in this material's exceptional welding, mechanical, and corrosion resistance properties. In order to verify this material's suitability for aircraft engineering applications, it is necessary to investigate its behaviour at various temperatures since aircrafts operate at a wide range of temperatures. For this reason, the effect of temperatures in the range from +20 °C to -80 °C on impact toughness was investigated in the case of S32750 duplex steel and its welded joints. Testing was performed using an instrumented pendulum to obtain force-time and energy-time diagrams, which allowed for more detailed assessment of the effect of testing temperature on total impact energy and its components of crack initiation energy and crack propagation energy. Testing was performed on standard Charpy specimens extracted from base metal (BM), welded metal (WM), and the heat-affected zone (HAZ). The results of these tests indicated high values of both crack initiation and propagation energies at room temperature for all the zones (BM, WM, and HAZ) and sufficient levels of crack propagation and total impact energies above -50 °C. In addition, fractography was conducted through optical microscopy (OM) and scanning electron microscopy (SEM), indicating ductile vs. cleavage fracture surface areas, which corresponded well with the impact toughness values. The results of this research confirm that the use of S32750 duplex steel in the manufacturing of aircraft hydraulic systems has considerable potential, and future work should confirm this.
RESUMO
Current standards related to welded joint defects (EN ISO 5817) only consider individual cases (i.e., single defect in a welded joint). The question remains about the behaviour of a welded joint in the simultaneous presence of several different types of defects, so-called multiple defects, which is the topic of this research. The main focus is on defects most commonly encountered in practice, such as linear misalignments, undercuts, incomplete root penetration, and excess weld metal. The welding procedure used in this case was metal active gas welding, a common technique when it comes to welding low-alloy low-carbon steels, including those used for pressure equipment. Different combinations of these defects were deliberately made in welded plates and tested in a standard way on a tensile machine, along with numerical simulations using the finite element method (FEM), based on real geometries. The goal was to predict the behaviour in terms of stress concentrations caused by geometry and affected by multiple defects and material heterogeneity. Numerical and experimental results were in good agreement, but only after some modifications of numerical models. The obtained stress values in the models ranged from noticeably lower than the yield stress of the used materials to slightly higher than it, suggesting that some defect combinations resulted in plastic strain, whereas other models remained in the elastic area. The stress-strain diagram obtained for the first group (misalignment, undercut, and excess root penetration) shows significantly less plasticity. Its yield stress is very close to its ultimate tensile strength, which in turn is noticeably lower compared with the other three groups. This suggests that welded joints with misalignment and incomplete root penetration are indeed the weakest of the four groups either due to the combination of the present defects or perhaps because of an additional unseen internal defect. From the other three diagrams, it can be concluded that the test specimens show very similar behaviour with nearly identical ultimate tensile strengths and considerable plasticity. The diagrams shows the most prominent yielding, with an easily distinguishable difference between the elastic and plastic regions. The diagrams are the most similar, having the same strain of around 9% and with a less obvious yield stress limit.