RESUMO
Blue afterglow constitutes of one of the primary afterglow colors and can convert into other afterglow colors through energy transfer. The reported studies show the fabrication of blue afterglow emitters, but most of them are formed by room-temperature phosphorescence mechanism and require UVB lights as excitation source (these high-energy lights may damage organic systems). Here we report visible-light-excitable blue thermally activated delayed fluorescence type (TADF-type) afterglow materials via delicate control of excited states in difluoroboron ß-diketonate (BF2bdk) systems. Tiny change of the substituents in BF2bdk system has been found to pose significant influence on excited state energy levels and consequently narrow the singlet-triplet splitting energy of the system. As a result, both forward and reverse intersystem crossing have been accelerated, leading to the emergence of BF2bdk's TADF-type organic afterglow in rigid crystalline matrices. The resultant TADF-type afterglow materials exhibit emission lifetimes of several hundred milliseconds, photoluminescence quantum yield (PLQY) of 24.7 % and display temperature responsive property.
RESUMO
Narrowband afterglow materials display interesting functions in high-quality anti-counterfeiting and multiplexed bioimaging. However, there is still a limited exploration of these afterglow materials, especially for those with a full width at half maxima (FWHM) around 30 nm. Here, we report the fabrication of narrowband organic/inorganic hybrid afterglow materials via energy transfer technology. Coronene (Cor) with a long phosphorescence feature and broad phosphorescence band is selected as the donor for energy transfer, and inorganic quantum dots (QDs) of CdSe/ZnS with a narrowband emission are used as acceptors. Upon doping into the organic matrix, the resultant three-component materials exhibit a narrowband afterglow with an afterglow lifetime of approximately 3.4 s and an FWHM of 31 nm. The afterglow wavelength of the afterglow materials can be controlled by the QDs. This work based on organic/inorganic hybrids provides a facile approach for developing multicolor and narrowband afterglow materials, as well as opens a new way for expanding the features of organic afterglow for multifunctional applications. It is expected to rely on narrowband afterglow emitters to solve the "spectrum congestion" problem of high-density information storage in optical anti-counterfeiting and information encryption.
RESUMO
Polyurethane (PU) prepared by blending rosin base and CO2-polyol already has good mechanical properties and hydrophobic effect and has powerful benefits in acid and alkali resistance and salt resistance. In this study, mussel bionic rosin-based benzoxazine (BZ) was synthesized using dehydroabietylamine, catechol, and paraformaldehyde. Mixing BZ into PU can endow the resulting PU/BZ with special effects such as zero curing shrinkage, excellent mechanical behavior, and flame retardancy through a 3D interpenetrating network system. From the results, the modulus of rupture (MOR) and modulus of elasticity (MOE) of PU wood coatings are 97.04 and 2601.97 MPa, respectively; in contrast, the PU/BZ wood coatings exhibited higher values of MOR and MOE of 110.87 and 2738.11 MPa. PU/BZ wood coatings show higher flexural strength and elastic modulus. They are also stronger than PU coatings in terms of acid/alkali and aging resistance. At the same time, the coating is endowed with flame retardant properties, and the LOI is 30.2 due to the presence of BZ. Thus, PU/BZ can be a versatile and practical wood coating. The interpenetrating network system of PU/BZ has an innovative impact on the preparation of wood coatings.