The aim of this work is to investigate and characterize the photo-ignition process of dry multi-walled carbon nanotubes (MWCNTs) mixed with ferrocene (FeCp2) powder, using an LED (light-emitting diode) as the light source, a combination that has never been used, to the best of our knowledge. The ignition process was improved by adding a lipophilic porphyrin (H2Pp) in powder to the MWCNTs/FeCp2 mixtures-thus, a lower ignition threshold was obtained. The ignition tests were carried out by employing a continuous emission and a pulsed white LED in two test campaigns. In the first, two MWCNT typologies, high purity (HP) and industrial grade (IG), were used without porphyrin, obtaining, for both, similar ignition thresholds. Furthermore, comparing ignition thresholds obtained with the LED source with those previously obtained with a Xenon (Xe) lamp, a significant reduction was observed. In the second test campaign, ignition tests were carried out by means of a properly driven and controlled pulsed XHP70 LED source. The minimum ignition energy (MIE) of IG-MWCNTs/FeCp2 samples was determined by varying the duration of the light pulse. Experimental results show that ignition is obtained with a pulse duration of 110 ms and a MIE density of 266 mJ/cm². The significant reduction of the MIE value (10-40%), observed when H2Pp in powder form was added to the MWCNTs/FeCp2 mixtures, was ascribed to the improved photoexcitation and charge transfer properties of the lipophilic porphyrin molecules.
RESUMO
This work aims to investigate and characterize the photo-ignition phenomenon of MWCNT/ferrocene mixtures by using a continuous wave (CW) xenon (Xe) light source, in order to find the power ignition threshold by employing a different type of light source as was used in previous research (i.e., pulsed Xe lamp). The experimental photo-ignition tests were carried out by varying the weight ratio of the used mixtures, luminous power, and wavelength range of the incident Xe light by using selective optical filters. For a better explanation of the photo-induced ignition process, the absorption spectra of MWCNT/ferrocene mixtures and ferrocene only were obtained. The experimental results show that the luminous power (related to the entire spectrum of the Xe lamp) needed to trigger the ignition of MWCNT/ferrocene mixtures decreases with increasing metal nanoparticles content according to previously published results when using a different type of light source (i.e., pulsed vs CW Xe light source). Furthermore, less light power is required to trigger photo-ignition when moving towards the ultraviolet (UV) region. This is in agreement with the measured absorption spectra, which present higher absorption values in the UV-vis region for both MWCNT/ferrocene mixtures and ferrocene only diluted in toluene. Finally, a chemo-physical interpretation of the ignition phenomenon is proposed whereby ferrocene photo-excitation, due to photon absorption, produces ferrocene itself in its excited form and is thus capable of promoting electron transfer to MWCNTs. In this way, the resulting radical species, FeCp2 +â and MWCNT-, easily react with oxygen giving rise to the ignition of MWCNT/ferrocene samples.