Characterization of a Novel TiF4 Inclusion Complex and in vitro Evaluation of Its Effect on Inhibiting Enamel Demineralization.

INTRODUCTION: Titanium tetrafluoride (TiF4) is an anticariogenic agent with high remineralizing potential. However, the acidic pH of TiF4 solution can limit its clinical application. The present study aimed to prepare and characterize a new TiF4-dendrimer inclusion complex and evaluate its ability to inhibit enamel demineralization under pH cycling conditions. METHODS: PEG-citrate dendrimer and TiF4-dendrimer inclusion complex were synthesized and their molecular structures were evaluated using Fourier-transform Infrared Spectroscopy (FTIR), Hydrogen Nuclear Magnetic Resonance (HNMR), and Liquid Chromatography-Mass Spectrometry (LC-MS) tests. Forty-eight enamel samples were prepared and randomly divided into four groups: distilled water (negative control), TiF4 solution (T), dendrimer solution (D), and TiF4-dendrimer solution (TD). The microhardness of the samples was measured initially. Next, the samples underwent pH cycling, were exposed to the solutions, the microhardness was measured again, and microhardness loss was calculated. EDX analysis was performed on the surface and cross-sectional segments of the samples. RESULTS: The microhardness loss was significantly higher in control (-65.1 ± 6.0) compared to other groups. No significant difference was observed between T (-47.9 ± 5.6) and D (-41.7 ± 12.0) and also D and TD (-40.5 ± 9.4) in this regard. Microhardness loss was significantly higher in T compared to TD group. The TD samples showed similar fluoride and titanium content in both surface and subsurface regions, while the T group had higher concentrations in the surface region. Moreover, the TD solution had a higher pH of 3.4 compared to the T solution's pH of 1.1. CONCLUSION: No significant difference was observed between the efficacy of TiF4-dendrimer and TiF4 solution in inhibiting demineralization while TiF4-dendrimer solution had the added advantage of having a higher pH.

Vickers micro-hardness study of the effect of fluoride mouthwash on two types of CAD/CAM ceramic materials erosion.

BACKGROUND: The aim of this study was to evaluate the protective effects of fluoride mouthwash on the surface micro-hardness of two types of CAD/CAM ceramics after exposure to acidic solutions. METHODS: 40 samples (5 × 5 × 3 mm3) were prepared from two different ceramics: Vitabloc Mark II CAD, and IPS e.max CAD. The samples were randomly divided into 5 groups in each ceramic (n = 8) immersed in different solutions: Gs: saliva: GGA: gastric acid, GAA: acetic acid, GFGA: sodium fluoride + gastric acid, GFAA: sodium fluoride + acetic acid. The microhardness of samples was measured before and after immersion in different solutions by Vickers microhardness tester. By subtracting the microhardness values after and before immersion, the microhardness changes of the samples were obtained. Data were analyzed by Two-way analysis of variance, one-way analysis of variance, and Tukey test (α = 0.05). RESULTS: Immersion in different solutions reduced the microhardness. Microhardness loss was significantly affected in G FAA and G FGA groups in both types of ceramics (P < 0.05). For Vitabloc Mark II groups, the microhardness loss was significantly higher in GFAA and GFGA compared to IPS e.max CAD P < 0.001). CONCLUSION: Fluoride mouthwash in conjunction with acidic solutions may adversely affect microhardness of Vitabloc Mark II CAD, and IPS e.max CAD that may consequently compromise the clinical service. Vitabloc Mark II CAD was significantly more affected than IPS e.max CAD.

Effect of charcoal-based dentifrices on surface roughness of an aged resin composite.

BACKGROUND: Recently, the use of whitening dentifrice has increased among patients. However, these products might increase the surface roughness of composite restorations and make them more susceptible to discoloration and plaque accumulation. This study aimed to compare the effects of two charcoal-based dentifrices and other whitening dentifrices with different mechanisms of action on the surface roughness of an aged resin composite. METHODS: Forty-five composite specimens were made (2 × 7mm) and their initial surface roughness was obtained using a Profilometer. The specimens were subjected to the Accelerated Artificial Aging (AAA) process for 300 hours. Then, the surface roughness of the specimens was reevaluated using the Profilometer. The specimens were randomly divided into 5 groups (N.=9), namely Control (Gc), Bencer (Gb; Sormeh Company, Tehran, Iran), Perfect White Black (Gp), Colgate Total Whitening (Gt), and Colgate Optic White (Go) (Colgate-Palmolive Company, New York, NY, USA). The specimens were brushed for 14 minutes with respective dentifrices. In the Gc group, the specimens were only brushed with distilled water. The surface roughness of the specimens was measured again. The data were analyzed using repeated measure ANOVA at a significance level of 0.05. RESULTS: There was no significant difference in surface roughness parameters (Ra, Rq, Rz) between the groups, but in each group, the roughness parameters decreased after the aging procedure and increased after brushing significantly except for Rz parameter in Gb group which increased after aging and decreased after brushing. CONCLUSIONS: None of the whitening dentifrices used in the present study had an adverse effect on the surface roughness of an aged composite resin.

Effect of Laser and Conventional Office Bleaching and Polishing on the Color Change of Stained Nanohybrid and Microhybrid Composite Resin.

Aim: The present study investigated the effects of laser and conventional in-office bleaching, and polishing on the color of stained composite resin. Materials and Methods: A microhybrid composite (Clearfil AP-X) and a nanohybrid composite (Grandio) were selected. Twenty-four discs (2 × 10 mm) for each composite were prepared. The samples were immersed in coffee solution (25 g of coffee in 250 mL water) for seven days. Then the samples were divided into three groups (n = 8) and the stains were removed using bleaching (with Opalescence Xtra Boost), diode laser irradiation with Heydent material and a Sof-Lex polishing kit. The L ∗a ∗b ∗ color parameters were determined using a spectrophotometer before and after immersion and after stain removal procedures, and the overall color changes (ΔE) were calculated. The data were analyzed with two-way analysis of variance. Results: In the Clearfil composite resin group, the mean ΔE compared to the baseline using in-office bleaching, laser irradiation, and Sof-Lex polishing kit were 3.31, 3.35, and 4.93, respectively. These values with the Grandio composite resin were 3.31, 6.35, and 4.57, respectively. The highest capacity to remove stains was related to the conventional in-office bleaching method. Grandio composite resin underwent more color changes than Clearfil composite resin significantly (P-value < 0.05). Conclusion: Both composite resins exhibited color changes after immersion in the discoloring solution. However, after staining-removing procedures, the ΔE values decreased. Decreases in the ΔE values were not sufficient to restore the color to that before immersion in the discoloring solution with any stain-removing methods.

Effect of Different Bleaching Methods on Monomer Release from Aged Microhybrid and Nanohybrid Resin Composites.

Introduction: Recently, the application of laser-assisted bleaching has increased in dental practice. This method might affect the physical and chemical properties of resin composite and its monomer release. This study aimed to evaluate the effect of in-office, at-home, and laser-assisted bleaching on the monomer release (bisphenol A diglycidyl dimethacrylate (BisGMA), triethylene glycol dimethacrylate (TEGDMA), and urethane dimethacrylate (UDMA)) from aged nanohybrid (Grandio, Voco) and microhybrid (Clearfil AP-X Esthetics, Kuraray) resin composites. Methods: Thirty-two samples of each composite were prepared. The samples underwent aging procedure with UV light at 65°C for 100 hr. The samples were divided into 4 groups: OB: conventional in-office bleaching with Opalescence Boost PF 40% gel; HB: home bleaching with Opalescence PF 15% gel; LB: bleaching with JW Power bleaching gel followed by diode laser application; and C: control group without bleaching. Then, the samples were immersed in a solution containing 75% ethanol + 25% distilled water. The medium was renewed after 8, 16, 24 hr, and 7 days and was analyzed using high-performance liquid chromatography method to evaluate the monomer release. The data were analyzed using Two-way ANOVA and Post hoc Tukey test. Results: The bleaching method had no effect on TEGDMA and BisGMA release in both composites while it affected UDMA release in nanohybrid composite; UDMA release was significantly higher in LB compared to control and also higher in OB and LB compared to HB. No difference was observed in the microhybrid composite in this regard. Conclusion: Laser-assisted bleaching did not affect monomer release from microhybrid composite while it increased UDMA release from nanohybrid composite. The bleaching method had no effect on TEGDMA and BisGMA release.

Evaluation of cytotoxicity and antibacterial activity of different pulp capping liners.

This study compares the cytotoxicity and antibacterial activity of five pulp capping liners. This in vitro study was conducted on Fuji II LC glass ionomer, Dycal, Calcimol LC, TheraCal LC, and ACTIVA BioACTIVE. For cytotoxicity, the (MTT) methyl thiazolyl tetrazolium assay was performed on 3 samples from each group of human dental pulp cells (HDPSCs) after 24 h of incubation. The direct contact test (DCT) for antibacterial activity, 6 samples (3 for each material, and 3 for negative control), from each liner were made to evaluate Streptococcus mutans (S. mutans), Lactobacillus casei (L. casei), and Lactobacillus acidophilus (L. acidophilus). Data were analyzed by one-way ANOVA and Tukey's post-hoc test (alpha = 0.05). Data analysis showed that the cytotoxicity of the materials was significantly different (p < 0.001). Fuji II LC and ACTIVA BioACTIVE showed strong cytotoxicity, TheraCal LC moderate cytotoxicity, and Dycal and Calcimol LC slight cytotoxicity. The analysis also revealed a significant difference among the materials regarding antibacterial activity (p < 0.001). Tukey's test showed that the mean percentage of reduction in colony count was significant for all liners compared with the positive control (p < 0.001). The mean percentage of reduction in colony count for Dycal was significantly greater than that of Fuji II LC (p = 0.014), Calcimol LC (p = 0.003), and TheraCal LC (p = 0.001). ACTIVA BioACTIVE did not significantly differ from the other materials as regards antibacterial activity. Dycal showed significantly higher antibacterial activity than the other materials.

Marginal microleakage and modified microtensile bond strength of Activa Bioactive, in comparison with conventional restorative materials.

OBJECTIVES: This study aimed to assess the enamel and dentin marginal microleakage and dentin microtensile bond strength (µTBS) of ACTIVA BioACTIVE Restorative with and without a bonding agent compared with conventional restorative materials. MATERIAL AND METHODS: For enamel and dentin microleakage, Class II boxes were prepared in the mesial (1 mm under the cementoenamel junction) and distal (1 mm above the cementoenamel junction) surfaces of 90 extracted human third molars. The teeth were randomly divided into five groups (n = 18): Group Z (G-Premio Bond + Filtek Z250 XT), Group X (G-Premio Bond + X-tra fil bulk-fill), Group AA (G-Premio Bond + Activa Bioactive restorative), Group A (Activa Bioactive restorative), and Group G (dentin conditioner + Fuji II LC Improve). The teeth were thermocycled, and their microleakage was quantified using the dye penetration test under a stereomicroscope. For dentin µTBS measurement, 12 specimens were fabricated in metal molds (1 × 1 × 12 mm³) for each group mentioned above, and a universal testing machine measured their µTBS. Data were analyzed using one-way analysis of variance (ANOVA), the Kruskal-Wallis test, and multiple comparisons tests. RESULTS: Significant differences were noted among the groups in marginal microleakage and µTBS (p < .001). The highest mean microleakage scores at the enamel and dentin margins were noted in Group A, which had significant differences with other groups (p < .001). The highest µTBS was found in Group X, with significant differences with Group G and Group A (p < .05). The lowest µTBS was noted in Group A, with significant differences with Groups X, Group AA, and Group Z (p < .001). CONCLUSIONS: Activa Bioactive without a bonding agent showed significantly lower µTBS to dentin, and higher microleakage at the enamel and dentin margins. Application of adhesive resin with Activa Bioactive provided a dentine bond strength and marginal seal comparable to other restorative materials.

Microtensile Repair Bond Strength of a Composite After Accelerated Artificial Aging: Effect of the Air Abrasion, Bur, Er:YAG Laser, Two-Step Self-etch Bonding, and Universal Bonding Repair System.

Introduction: Repair of old composite restorations is a conservative approach. This study sought to compare the effects of two adhesive systems on the bond strength of repaired composites prepared by three different surface treatments: erbium-doped yttrium aluminum garnet (Er:YAG) laser irradiation, air-abrasion, and bur preparation. Methods: Eight microhybrid (Polofil Supra, VOCO, Germany) composite resin blocks were fabricated. The blocks were aged and assigned to four groups as stated by the surface treatment: (I) air-abrasion (50 µ aluminum oxide particles), (II) diamond bur (fine grit), (III) Er:YAG laser (3 W output power, 300 mJ energy) and (IV) control. After surface treatment, the blocks were acid-etched and salinized. Each group was divided two subgroups, and the Clearfil SE Bond or All-Bond Universal was applied on their surface. Composite resin was bonded to the aged composites. The blocks were cut into eight samples, and the microtensile bond strength (MTBS) was measured. Results: The maximum MTBS was noted in the air-abrasion (25.1+6 MPa) group, followed by the Er:YAG laser (21.2+4.7 MPa). The mean MTBS in laser and air-abrasion groups was significantly higher than that in other groups (P<0.05). The mean MTBS was not significantly different between the laser and air-abrasion groups (P>0.05). Composite resin conditioning by All-Bond Universal in laser and air-abrasion groups yielded significantly higher MTBS than the Clearfil SE Bond (P<0.05). Conclusion: All surface treatments created acceptable bond strength. The surface treatment of the aged composite by the Er:YAG laser or air-abrasion along with the application of silane and All-Bond Universal provide high bond strength.

Effect of Bioinductive Cavity Liners on Shear Bond Strength of Dental Composite to Dentin.

Background: The aim of the current study was to evaluate and compare the influence of Dycal, Lime-Lite, TheraCal LC, Biodentine, resin-modified glass ionomer cement (RMGIC), and Activa BioActive as the pulp capping material on the shear bond strength of resin composite to dentin. Methods: A total of 70 extracted caries-free molars were randomly assigned to seven groups. Six test groups were covered with various protective liners: Dycal, TheraCal LC, Lime-Lite, Activa BioActive, Biodentine, and RMGIC. The control group received no liner pretreatment. Each sample was bonded to resin composite using the total-etch Tetric N bond adhesive. The samples were then tested for shear bond strength using the universal testing machine at a cross-head speed of 1 mm/min until bond failure occurred. The data were analyzed using the one-way ANOVA test followed by the Tamhane post hoc test for pairwise comparisons of the groups. Results: Independent of the type of the applied liner, all groups exhibited inferior SBS to dentin compared to the control group. TheraCal and RMGIC showed significantly higher shear bond strength than Biodentine and Dycal, which showed the lowest shear bond strength. Lime-Lite and Activa also had significantly lower SBS results than TheraCal. The mode of fracture was predominantly cohesive in Dycal, Biodentine, and TheraCal and adhesive in Activa. Conclusion: This present study concludes that the bond strength of resin composite to dentin can be affected differently using various types of liners.

In Vitro Effect of Acidic Solutions and Sodium Fluoride on Surface Roughness of Two Types of CAD-CAM Dental Ceramics.

OBJECTIVES: This study assessed the effect of immersion in acidic solutions and sodium fluoride on surface roughness of dental ceramics. MATERIALS AND METHODS: 40 blocks of Vitablocs Mark II and IPS e.max CAD (5 × 5 × 3) were prepared. The samples were divided into five groups (n = 8) for immersion in artificial saliva (control), artificially prepared gastric acid, acetic acid, 0.02% sodium fluoride + gastric acid, and 0.02% sodium fluoride + acetic acid. The samples were immersed for 168 hours in the respective solutions except for sodium fluoride, in which the samples were immersed for 69 hours. The surface roughness of samples was measured before and after immersion using a profilometer. The surface roughness changes of three specimens of each group were evaluated by scanning electron microscopy (SEM). Data were analyzed using one-way and two-way ANOVA, Tukey's test, and independent t-test. RESULTS: Significant changes were noted in Ra (P=0.002) and Rq (P < 0.0001) in both types of ceramics. The lowest changes in Ra and Rq parameters were seen in artificial saliva and gastric acid and highest changes occurred following immersion in 0.02% sodium fluoride + acetic acid and 0.02% sodium fluoride + gastric acid, respectively. Changes in Rz were also significant following immersion in Vitablocs Mark II (P < 0.05). Immersion in 0.02% sodium fluoride + gastric acid and 0.02% sodium fluoride + acetic acid produced a rougher surface on both types of ceramics (SEM). CONCLUSION: Exposure of Vitablocs Mark II CAD and IPS e.max CAD to 0.02% sodium fluoride + gastric acid and 0.02% sodium fluoride + acetic acid significantly increased their surface roughness, while for Vitablocs Mark II, lager defects were seen on its surface.

Cytotoxic Effect of Addition of Different Concentrations of Nanohydroxyapatite to Resin Modified and Conventional Glass Ionomer Cements on L929 Murine Fibroblasts.

Objectives: In this study we assessed the cytotoxic effect of nanohydroxyapatite (NHA) incorporated into resin modified and conventional glass ionomer cements (RMGICs and CGICs) on L929 murine fibroblasts. Materials and Methods: In this in vitro study, 0wt%, 1wt%, 2wt%, 5wt%, 7wt% and 10wt% concentrations of NHA were added to Fuji II LC RMGIC and Fuji IX CGIC powders. Eighteen samples (5×3mm) were fabricated from each type of glass ionomer, in six experimental groups (n=3): CG0, CG1, CG2, CG5, CG7, CG10, RMG0, RMG1, RMG2, RMG5, RMG7, and RMG10. Samples were incubated for 72h. The overlaying solution was removed and added to L929 fibroblasts. The methyl thiazolyl tetrazolium bromide (MTT) assay was performed at 24, 48 and 72h. The wavelength was read by a spectrophotometer. Data were analyzed by ANOVA and Tukey's test. Results: There was no significant difference in cytotoxicity of the two types of glass ionomers, with and without NHA, except for CG0 and RMG0 groups after 72h. RMG0 group was significantly more cytotoxic than the CG0 group (P<0.05). In CG groups during the first 24h, the cytotoxicity of CG5 and CG7 groups was significantly higher than that of CG1; while, there was no significant difference between the RMG groups. Cytotoxicity significantly decreased in all groups after 24h (P<0.05). Conclusion: Incorporation of NHA into Fuji II LC RMGIC and Fuji IX CGIC did not affect their biocompatibility and therefore its addition to these materials can provide favorable biological properties, especially considering its beneficial effects on the other properties of GICs.

In vitro antibacterial activity and durability of a nano-curcumin-containing pulp capping agent combined with antimicrobial photodynamic therapy.

BACKGROUND: Considering the antibacterial properties of nano-curcumin (nCur) reinforced with antimicrobial photodynamic therapy (aPDT), this study aimed to assess the antibacterial activity and durability of Activa BioActive Base/Liner (ABBL) containing nCur (nCur-ABBL) as a pulp capping agent against Streptococcus mutans, the most common cause of secondary caries. MATERIALS AND METHODS: In this in vitro experimental study, ABBL discs containing 0.5 %, 1%, 2%, and 5% (w/w) concentrations of nCur were fabricated. After aPDT using light emitting diode (LED) at 435 ± 20 nm wavelength for 5 min, the discs were undergone aging in artificial saliva for 90 days. The antibacterial activity of the discs against S. mutans was evaluated by the disc agar diffusion test, and the number of bacterial colonies present in the biofilm formed on the disc surfaces was counted after 0, 15, 30, and 60 days of aging. RESULTS: The maximum growth inhibition zone was noted around the 5% nCur-ABBL discs. Increasing the concentration of nCur from 0.5 % to 5% combined with aPDT significantly decreased the number of S. mutans colonies in the biofilm over time (P < 0.05). nCur-ABBL discs containing 2% and 5% nCur had no difference in antibacterial activity at any time point up to 60 days (P > 0.05). CONCLUSION: According to our data, 5% nCur-ABBL revealed the largest growth inhibition zone in S. mutans culture. Moreover, 5% nCur can serve as an excellent ABBL additive in aPDT producer against S. mutans biofilms up to 60 days of aging period.

Effect of fluoride varnish on glass ionomer microhardness changes in endogenous acid erosion challenge.

OBJECTIVE: This study aimed to assess the effect of fluoride varnish on glass ionomer microhardness changes after endogenous acid erosion challenge. METHODOLOGY: In this study, 40 conventional glass ionomer (CGI; Fuji IX) and 40 resin-modified glass ionomer (RMGI; Fuji IILC) discs were fabricated and divided into 4 subgroups (n = 10) for immersion in synthetic gastric acid or saliva for 27 h with/without fluoride varnish application. The surface microhardness was measured at baseline and after immersion, and the change in microhardness was calculated. Data were analyzed using analysis of variance and T-test. RESULTS: A reduction in microhardness was noted in all subgroups following immersion. The lowest change in microhardness of both CGI and RMGI occurred in artificial saliva. In CGI groups, the highest reduction in microhardness occurred in synthetic gastric acid with fluoride varnish application, and the reduction was significantly different from that of the CGI group with fluoride varnish application (p value = .01). In RMGI groups, the highest reduction in microhardness was noted in synthetic gastric acid without fluoride varnish application, and the reduction was significantly different from that of the other groups (p value < .05). CONCLUSIONS: Exposure to synthetic gastric acid caused a significant reduction in microhardness of RMGI. Varnish application significantly decreased the acid susceptibility of RMGI, but not that of CGI.

Evaluation of Compressive Strength of Several Pulp Capping Materials.

STATEMENT OF THE PROBLEM: Adequate compressive strength is an important characteristic for an ideal liner. PURPOSE: This study aimed to assess the compressive strength of several commonly used liners. MATERIALS AND METHOD: This in vitro, experimental study evaluated 120 samples fabricated of Dycal, Calcimol LC, Vitrebond, Activa Bioactive, and TheraCal LC (n=24) liners according to the manufacturers' instructions. The samples were fabricated using a cylindrical stainless steel mold with 6±0.1 mm height and 4±0.1 mm internal diameter. Half of the samples in each group (n=12) underwent compressive strength test immediately after completion of their primary setting while the other half (n=12) underwent compressive strength test after 24 h. During this period, the samples were immersed in deionized water (grade 3) and incubated at 37±1°C and 100% humidity for 24 h. The compressive strength was measured using a universal testing machine. Data were analyzed using two-way ANOVA followed by Tukey's post-hoc test. RESULTS: The compressive strength of the five liners was significantly different (p< 0.05). Calcimol LC showed maximum compressive strength both immediately after setting and after 24 h. The compressive strength at 24 h was significantly higher than the primary compressive strength in all groups (p< 0.05). CONCLUSION: Within the limitations of this study, it seems that Calcimol LC, Activa Bioactive Liner, and TheraCal LC have adequate compressive strength and can be used alone to provide adequate support for the restorative materials.

Effect of Root Dentin Pretreatment on Micro-Push-Out Bond Strength of Fiber Posts to Root Canal Dentin: Cold Atmospheric Argon Plasma (CAAP) and Ethylenediaminetetraacetic Acid (EDTA).

PURPOSE: Debonding from the root canal dentin is the most common failure mode of fiber posts. This study aimed to assess the effects of cold atmospheric argon plasma (CAAP) and ethylenediaminetetraacetic acid (EDTA) on micro-push-out bond strength of fiber posts to root canal dentin. MATERIALS AND METHODS: Forty maxillary canine teeth were decoronated, underwent endodontic treatment, and were stored in an incubator for 7 days. After post space preparation, the teeth were randomly divided into four groups for different surface treatments: (I) saline, (II) 17% EDTA, (III) CAAP, and (IV) 17% EDTA + CAAP. Fiber posts (Whitepost no. 2, FGM) were cemented into the root canals using Panavia F2.0 resin cement, and 1 mm-thick sections were made at the coronal, middle, and apical thirds of the roots. The samples underwent micro-push-out bond strength test. The mode of failure was also determined under a stereomicroscope. Data were analyzed using three-way ANOVA and Tukey's post hoc test (α = 0.05). The mode of failure data were analyzed using the chi-square test. RESULTS: The mean micro-push-out bond strength of fiber posts was not significantly different in the four groups (P > 0.05). However, the bond strength values in the coronal third were significantly higher than the corresponding values in the apical third (P=0.01). There was no significant difference in the modes of failure between the groups (P > 0.05). CONCLUSION: Application of CAAP alone or in combination with 17% EDTA could not successfully increase the bond strength of fiber posts to root canal dentin.

Efficacy of cavity liners with/without atmospheric cold helium plasma jet for dentin remineralization.

Aim: This study aimed to assess the efficacy of cavity liners with/without the atmospheric cold plasma jet (ACPJ) for dentin remineralization. MATERIAL AND METHODS: The occlusal third of 24 extracted third molars was cut. An occlusal cavity was prepared in the dentin of each tooth with 1 mm depth and 2 mm diameter and demineralized with 37% phosphoric acid for 1 min. The teeth were randomly divided into 8 groups (n = 3). The first control group only underwent demineralization with phosphoric acid. The second control group underwent demineralization and helium plasma jet. Groups 3 to 5 were filled with calcium hydroxide (CH), RetroMTA (MTA) and Biodentine. Groups 6 to 8 were subjected to ACPJ, and all the groups were sealed with polycarboxylate. After 2 weeks of immersion in water, the teeth were longitudinally sectioned and their mineral content was analyzed using energy-dispersive X-ray spectroscopy (EDX). RESULTS: The interaction effect of ACPJ and type of liner was not significant (p > 0.05). Application of ACPJ in combination with liner had a significant effect on calcium and phosphorous contents (p < .05). The calcium and phosphorous contents in the control groups were significantly lower than other groups (p < .05). The calcium and phosphorous contents in the CH group were higher than the control but significantly lower than the MTA and Biodentine groups. The values in the MTA and Biodentine groups were the same and higher than other groups. CONLUSION: All three cavity liners significantly increased the calcium and phosphorous contents of dentin. This increase was significantly greater by the MTA and Biodentine and enhanced by the ACPJ.

Restoration of a Nonvital Tooth with Fiber Reinforce Composite (Wallpapering Technique).

INTRODUCTION: Reconstruction of endodontically treated tooth (ETT) is one of the greatest challenges in dentistry. Clinical success of fiber reinforcement composite (FRC) restorations in ETT depends on many factors like remaining tooth structure, knowing advantages of adhesive dentistry besides its drawbacks, and the correct use of fibers in combination with resin composite. Case Report. This article presents a case in which fibers have been used in composite buildup in order to increase the toughness and strength of the ETT direct restoration. In addition, this technique does not require root canal enlargement to eliminate the risk of root perforation. Also, this one visit treatment can be helpful for patients that could not pay the cost of indirect restoration and/or have no time. CONCLUSION: It seems in selected patients with special considerations, FRC composite restoration is valid alternatives for indirect restoration.

Direct Pulp Capping With ProRoot MTA Alone and in Combination With Er:YAG Laser Irradiation: A Clinical Trial.

Background: Due to the complications of root canal treatment, conservative modalities to preserve pulp vitality are favorable. Direct pulp capping (DPC) refers to the coverage of the pulp tissue exposed by a biocompatible agent that can improve the prognosis of the tooth by 44% to 95%. Some recent studies have reported more predictable results (a success rate of about 90%) for DPC with laser and regenerative materials such as mineral trioxide aggregate (MTA). This study aimed to clinically compare DPC with ProRoot MTA alone and in combination with Er:YAG (erbium-doped yttrium aluminium garnet) laser irradiation (2940 nm). Methods: This clinical trial was conducted on 26 patients with a mean age of 29 years (in the range of 17 to 46 years) who required DPC following pulp exposure during deep caries removal. The teeth were divided into two groups. In the control group, the teeth underwent DPC with ProRoot MTA while in the test group, the teeth were first irradiated with a 2940 nm Er:YAG laser and then underwent DPC with ProRoot MTA. The patients were recalled at one, 3 and 6 months for the follow-up (clinical and radiographic examinations). The data were analyzed using Fisher exact test. Results: The success rate was 75% in the laser group and 93% in the control group. The groups were not significantly different (P>0.05). Conclusion: No significant difference was found in terms of the success rate of DPC with ProRoot MTA alone and in combination with Er:YAG laser irradiation.

Color Stability of Ceramic Veneers Cemented with Self-Adhesive Cements after Accelerated Aging.

OBJECTIVES: Color change of cements over time can be detected through translucent ceramic veneers, compromising the aesthetic appearance of restorations in the long-term. This study aimed to assess the color stability of ceramic laminate veneers cemented with self-adhesive resin cements after accelerated aging. MATERIALS AND METHODS: In this study, 21 IPS e.max ceramic discs, measuring 8mm in diameter and 0.7 mm in thickness, were fabricated and divided into three groups (n=7) for the application of Choice 2 total-etch light-cure resin cement, RelyX U200 dual-cure self-adhesive resin cement, and SpeedCEM self-cure self-adhesive resin cement. The ceramic discs in each group were cemented on the prepared facial surface of bovine teeth. The color parameters were assessed using a spectrophotometer. Subsequently, the samples were subjected to accelerated aging for 100 hours, and the color parameters were measured again. The data were analyzed using two-way repeated-measures analysis of variance (ANOVA) and Tamhane's post-hoc test (P<0.05). RESULTS: Aging significantly affected the ceramic laminate color parameters in all three groups (P<0.05). SpeedCEM cement showed the lowest color stability (ΔE=4.2) after aging, and its color change was clinically unacceptable (ΔE>3.5). The color change of the other two groups was clinically acceptable (1<ΔE<3.5). CONCLUSION: The self-adhesive dual-cure cement showed color stability comparable to that of the total-etch light-cure cement for cementation of IPS e.max ceramic laminates. The color stability of both cements was superior to that of the self-adhesive self-cure cement.

In Vitro Effect of Bleaching With 810 nm and 980 nm Diode Laser on Microhardness of Self-cure and Light-Cure Glass Ionomer Cements.

Introduction: This study sought to assess the effect of bleaching combined with irradiation of 810 nm and 980 nm diode laser on microhardness of 2 commonly used self-cure and light-cure glass ionomer cements (GICs) in comparison with conventional bleaching (without laser). Methods: In this in vitro, experimental study, 60 samples were fabricated of A2 shade of Fuji IX and Fuji II LC GICs (n=30) and each group was divided into 3 subgroups (n=10). The first subgroups were subjected to bleaching with Opalescence Xtra Boost plus 980 nm diode laser irradiation. The second subgroups were subjected to bleaching with Opalescence Boost plus 810 nm diode laser irradiation and the third subgroups were subjected to bleaching with Opalescence Xtra Boost without laser. Microhardness was measured at baseline and after the intervention using Vickers hardness tester. The data were analyzed using two-way analysis of variance (ANOVA) (P<0.05). Results: Microhardness decreased in all subgroups after the intervention (P<0.001) irrespective of the type of GIC (P=0.201) or surface treatment (P=0.570). The baseline microhardness of the three subgroups within each group of GIC was not significantly different (P=0.456), but the baseline microhardness of conventional GIC was significantly higher than that of resin modified GIC (P=0.004). Conclusion: Bleaching with/without laser irradiation decreases the microhardness of GICs. The baseline microhardness of conventional GIC is higher than that of resin modified GIC.