Ion Microbeam Analyses of Dust Particles and Codeposits from JET with the ITER-Like Wall.

Generation of metal dust in the JET tokamak with the ITER-like wall (ILW) is a topic of vital interest to next-step fusion devices because of safety issues with plasma operation. Simultaneous Nuclear Reaction Analysis (NRA) and Particle-Induced X-ray Emission (PIXE) with a focused four MeV 3He microbeam was used to determine the composition of dust particles related to the JET operation with the ILW. The focus was on "Be-rich particles" collected from the deposition zone on the inner divertor tile. The particles found are composed of a mix of codeposited species up to 120 µm in size with a thickness of 30-40 µm. The main constituents are D from the fusion fuel, Be and W from the main plasma-facing components, and Ni and Cr from the Inconel grills of the antennas for auxiliary plasma heating. Elemental concentrations were estimated by iterative NRA-PIXE analysis. Two types of dust particles were found: (i) larger Be-rich particles with Be concentrations above 90 at% with a deuterium presence of up to 3.4 at% and containing Ni (1-3 at%), Cr (0.4-0.8 at%), W (0.2-0.9 at%), Fe (0.3-0.6 at%), and Cu and Ti in lower concentrations and (ii) small particles rich in Al and/or Si that were in some cases accompanied by other elements, such as Fe, Cu, or Ti or W and Mo.

Dust Monitors in JET with ITER-like Wall for Diagnosis of Mobilized Particles and Co-Deposited Layers.

Silicon plates were installed above the inner and outer divertor of the JET with the ITER-like wall (ILW) after the second and third ILW campaigns to monitor dust generation and deposition with the aim to determine the morphology and content of individual particles and co-deposits, including deuterium content. Particular interest was in metal-based particles: Be, W, steel, Cu. Ex-situ examination after two ILW campaigns was performed by a set of microscopy and ion beam methods including micro-beam nuclear reaction analysis and particle-induced X-ray emission. Different categories of Be-rich particles were found: co-deposits peeled-off from plasma-facing components (PFC), complex multi-element spherical objects, and solid metal splashes and regular spherical droplets. The fuel content on the two latter categories was at the level of 1 × 1016 at/cm-2 indicating that Be melting and splashing occurred in the very last phase of the second experimental campaign. The splashes adhere firmly to the substrate thus not posing risk of Be dust mobilisation. No tungsten droplets were detected. The only W-containing particles were fragments of tungsten coatings from the divertor tiles.

A combined segmented anode gas ionization chamber and time-of-flight detector for heavy ion elastic recoil detection analysis.

A dedicated detector system for heavy ion elastic recoil detection analysis at the Tandem Laboratory of Uppsala University is presented. Benefits of combining a time-of-flight measurement with a segmented anode gas ionization chamber are demonstrated. The capability of ion species identification is improved with the present system, compared to that obtained when using a single solid state silicon detector for the full ion energy signal. The system enables separation of light elements, up to Neon, based on atomic number while signals from heavy elements such as molybdenum and tungsten are separated based on mass, to a sample depth on the order of 1 µm. The performance of the system is discussed and a selection of material analysis applications is given. Plasma-facing materials from fusion experiments, in particular metal mirrors, are used as a main example for the discussion. Marker experiments using nitrogen-15 or oxygen-18 are specific cases for which the described improved species separation and sensitivity are required. Resilience to radiation damage and significantly improved energy resolution for heavy elements at low energies are additional benefits of the gas ionization chamber over a solid state detector based system.