Lithium Diffusion Pathway in Li(1.3)Al(0.3)Ti(1.7)(PO4)3 (LATP) Superionic Conductor.

The Al-substituted LiTi2(PO4)3 powders Li(1+x)Al(x)Ti(2-x)(PO4)3 (LATP) were successfully prepared by a water-based sol-gel process with subsequent calcination and sintering. The crystal structure of obtained samples was characterized at different temperatures using high-resolution synchrotron-based X-ray and neutron powder diffraction. Possible lithium diffusion pathways were initially evaluated using the difference bond-valence approach. Experimental 3D lithium diffusion pathway in LATP was extracted from the negative nuclear density maps reconstructed by the maximum entropy method. Evaluation of the energy landscape determining the lithium diffusion process in NASICON-type superionic conductor is shown for the first time.

Two-Photon Polymerization of Nanocomposites for Additive Manufacturing of Transparent Magnesium Aluminate Spinel Ceramics.

Transparent polycrystalline magnesium aluminate (MAS) spinel ceramics are of great interest for industry and academia due to their excellent optical and mechanical properties. However, shaping of MAS is notoriously challenging especially on the microscale requiring hazardous etching methods. Therefore, a photochemically curable nanocomposite is demonstrated that can be structured using high-resolution two-photon lithography. The printed nanocomposites are converted intro transparent MAS by subsequent debinding, sintering, and hot isostatic pressing. The resulting transparent spinel ceramics exhibit a surface roughness Sq of only 10 nm and can be shaped with minimum feature sizes of down to 13 µm. This technology will be important for the production of microstructured ceramics used for optics, photonics, or photocatalysis.

Injection Molding of Magnesium Aluminate Spinel Nanocomposites for High-Throughput Manufacturing of Transparent Ceramics.

Transparent ceramics like magnesium aluminate spinel (MAS) are considered the next step in material evolution showing unmatched mechanical, chemical and physical resistance combined with high optical transparency. Unfortunately, transparent ceramics are notoriously difficult to shape, especially on the microscale. Therefore, a thermoplastic MAS nanocomposite is developed that can be shaped by polymer injection molding at high speed and precision. The nanocomposite is converted to dense MAS by debinding, pre-sintering, and hot isostatic pressing yielding transparent ceramics with high optical transmission up to 84 % and high mechanical strength. A transparent macroscopic MAS components with wall thicknesses up to 4 mm as well as microstructured components with single micrometer resolution are shown. This work makes transparent MAS ceramics accessible to modern high-throughput polymer processing techniques for fast and cost-efficient manufacturing of macroscopic and microstructured components enabling a plethora of potential applications from optics and photonics, medicine to scratch and break-resistant transparent windows for consumer electronics.