Crystal Chemistry and Photoluminescent Aspects of Bright Orange Light Emitting Sm3+- Activated Ba2BiV3O11 Nanomaterials for Advanced Illuminating Applications.

In the present system, Sm3+ activated Ba2BiV3O11 nanomaterial series radiating orange-red light was developed via an efficient approach of solution combustion method. The structural examinations using XRD analysis indicate that the sample is crystallized into the monoclinic phase with the P21/a (14) space group. The elemental composition and morphological conduct were studied via energy dispersive spectroscopy (EDS) and scanning electron microscopy (SEM) respectively. Also, the formation of nanoparticles was confirmed by transmission electron microscopy (TEM). Photoluminescent (PL) examinations reveal the orange-red emission from the developed nanocrystals via documenting the emission spectra, which reveals the peak at 606 nm due to the 4G5/2 → 6H7/2 transition. Further, the decay time, non-radiative rates, quantum efficiency, and band gap of the optimal sample were computed as 1.3263 ms, 219.5 s- 1, 70.88%, and 3.41 eV respectively. Finally, the chromatic parameters including color - coordinates (0.5565, 0.4426), 1975 K color correlated temperature (CCT), and color purity (85.58%) reflected their excellent luminous performance. The above-mentioned outcomes endorsed the relevancy of the developed nanomaterials as a propitious agent in the engineering of advanced illuminating optoelectronic appliances.

Combustion Synthesis and Study of Double Charge Transfer in Highly Efficient Cool White-emitting Dy3+ Activated Vanadate-based Nanophosphor for Advanced Solid-state Lighting.

A series of Ca9Gd(VO4)7: Dy3+ (x = 0.01-0.20) nanophosphor crystals emitting a cool white light were synthesized by solution combustion methodology. The X-ray diffraction patterns were analyzed and processed using Rietveld refinement. The fabricated nanophosphor was found to crystallize in a trigonal crystal lattice with space group R3c(161). The morphological behavior of the prepared nanophosphor was investigated using transmission electron microscopy (TEM) and scanning electron microscopy (SEM). The photoluminescence properties of the nanophosphor correspond to cool white emission upon near-ultraviolet (NUV) excitation at 327 nm due to 4F9/2 → 6H15/2 (bluish) and 4F9/2 → 6H13/2 (yellowish) radiative relaxations at 487 nm and 576 nm respectively. Also, there is a strong occurrence of double charge transfer from O2- ions to Dy3+ and V5+ ions with the latter being stronger due to the high positive charge of V5+ ions. Color coordinates (x = 0.2878, y = 0.3259) are consistent with white emission. Auzel's model was implemented to examine the non-radiative relaxation (113.5 ms-1), radiative lifetime (1.4856 ms), and quantum efficiency (83.13%) values. The crystalline and optical behavior of the synthesized cool white emitting nanophosphor facilitates its use in near-UV-based WLEDs and other advanced solid-state lighting.