RESUMO
The purpose of this work is to quantify the effects of dissolved zinc cations on corrosion and release rates from a pre-filmed Alloy 690 steam generator tubing material that was subsequently exposed to water containing zinc. The corrosion tests were performed in circulating 2 ppm Li and 1000 ppm B water without and with 60 ppb zinc at 330 °C. Gravimetric analyses and oxide characterization revealed that the corrosion rates, release rates, and oxide thicknesses decreased by subsequent exposure of the pre-filmed Alloy 690 to zinc. These benefits are attributed to the formation of a chromium-rich inner oxide layer incorporating zinc.
RESUMO
The objective of this study was to investigate the behavior of zinc incorporation into newly forming fuel deposits and pre-formed deposits in a simulated pressurized water reactor coolant including 1000 ppm of boron and 2 ppm of lithium at 328 °C. Zinc was incorporated into fuel deposits that were being newly nucleated and grown on nuclear fuel cladding tubes in a zinc-containing coolant. The zinc incorporation resulted in a decrease in the lattice constant of the deposits, which was attributed to the decrease in larger iron content and the corresponding incorporation of smaller zinc in the deposits. However, zinc incorporation was not found, even after the fuel deposits pre-formed before zinc addition were subsequently exposed to the 60 ppb of zinc coolant for 500 h.