RESUMO
White light-emitting diodes (WLEDs) based on all-inorganic perovskite CsPbX3 (X = Cl, Br, I) quantum dots (QDs) have attracted much attention and rely on mixing several colors of perovskites. However, this inevitably leads to a non-uniform light distribution and serious light loss. Here, a novel strategy was demonstrated to obtain white emission by combining the orange and blue emission from CsPb/Mn(Cl/Br)3 QDs. Notably, highly efficient white emission with a photoluminescence quantum yield of 94% was achieved by an anion exchange surface engineering (AESE) strategy. After AESE treatment the surface traps can be eliminated, resulting in improved exciton and Mn2+ emission. A prototype WLED device was fabricated and exhibited excellent optical stability, demonstrating great potential for perovskite QDs in the field of optoelectronics.
RESUMO
The poor light absorption of visible light for Cs4PbBr6 nanocrystals (NCs) has severely impeded their practical applications. Although the semiconductor/perovskite heterostructure holds great promise for enhancement in absorption, it has remained a serious challenge for synthesizing a semiconductor/perovskite heterostructure. In this work, monodispersed Janus heterostructures composed of Cs4PbBr6 decorated with either multiple Ag or single Ag on its surface (named as mAg/Cs4PbBr6 and sAg/Cs4PbBr6 respectively), are successfully prepared. The size of Ag seeds has an important effect on the shape of the products. Small-sized Ag seeds lead to the formation of mAg/Cs4PbBr6 Janus NCs, while relatively large-sized Ag seeds produce sAg/Cs4PbBr6 Janus NCs. It is noted that this work not only provides a novel method for the modification of individual Cs4PbBr6 NCs, but also enhances the absorption of the Cs4PbBr6 in the visible region, indicating great potential for optoelectronic applications, such as photocatalysis and solar cells.
RESUMO
CsPbX3 perovskite nanocrystals (NCs) are becoming a promising material for optoelectronic devices that possess an optically tunable bandgap, and bright photoluminescence. However, the toxic Pb is not environmentally friendly and the quantum yield (QY) of blue emitting NCs is relatively low. In addition, the red emitting perovskite containing iodine is not stable under light illumination. In this paper, high QY, blue emitting, non-toxic fluorescent nanomaterial carbon dots and orange-emitting CsPb0.81Mn0.19Cl3 NCs with partial Pb replacement are combined to fabricate white light-emitting diodes (WLEDs). A WLED with color coordinates of (0.337, 0.324) and a correlated color temperature of 4804 K is fabricated. Compared to red emitting perovskite containing iodine, the CsPb0.81Mn0.19Cl3 NCs are stable no matter whether they are stored in the air or exposed under ultraviolet light. Therefore, the as-fabricated WLED shows good color stability against increasing currents and long-term working stability.
RESUMO
Fingerprints form when fingers touch a solid surfaceand are considered the best way for individual identification. However, the current latent fingerprint (LFP) developing methods cannot meet the demand for high sensitivity and being convenient and healthy. Herein, bifunctional Fe3O4@SiO2-CsPbBr3 powders have been designed and fabricated and exhibit good magnetic and strong fluorescent properties. The magnetism of Fe3O4 can avoid dust flying, while the fluorescence of CsPbBr3 ensures the high definition of LFPs. Clear fingerprints have been detected on various solid substrates using the Fe3O4@SiO2-CsPbBr3 powders instead of eikonogen. Detailed characterization studies suggest that the ammonium cationic groups on the surface of nanoparticles (NPs) have strong adhesive interactions with the residues of fingerprints because of the electrostatic attraction between them. Therefore, the convenient operation and excellent resolution offer great opportunity in the practical application of fingerprint detection and other areas.
RESUMO
For data security applications, the use of fluorescent inks has become the most promising approach because of their convenience and low cost. However, traditional fluorescent inks are usually visible either under ambient light or UV light, whereas the improved stimuli-responsive inks are restricted to a single color. For the first time, full-color stimuli-responsive inks for information coding, encryption, and decryption are reported, which rely on the facile preparation and conversion of perovskite quantum dots. The information printed by the halide salt solution is invisible under ambient and UV light but becomes readable under UV light after spraying a unique developer. Besides, the primitive information can be stored for many years, even decades. Even after the decryption process, it still can be stored for at least several weeks. Most importantly, using butyl amine and acetic acid as encryption and decryption reagents, respectively, can switch off/on the luminescence. In this way, the printed information can be encrypted and decrypted, which shows great potential for information security applications.
RESUMO
Lead halide perovskites are emerging as promising candidates for high-efficiency light-emitting diode (LED) applications because of their tunable band gaps and high quantum yield (QY). However, it remains a challenge to obtain stable red emitting materials with high QY. Herein, we report a facile and convenient hot-injection strategy to synthesize Mn-doped two-dimensional (2D) perovskite nanosheets. The emission peak can be tuned from 597 to 658 nm by manipulating the crystal field strength. In particular, a QY as high as 97% for 2D perovskite is achieved. The as-prepared perovskite also possesses excellent stability, whose emission property can be maintained for almost one year. A monochrome LED is further fabricated by employing the as-prepared perovskite as phosphor, which also shows high long-term stability. We believe that these highly efficient and stable perovskites will open up new opportunities in LED applications.
RESUMO
Perovskite quantum dots (QDs) have been widely used in white light-emitting diodes (WLEDs), due to their high quantum yield (QY), tunable bandgap, and simple preparation. However, the red-emitting perovskite QDs are usually containing iodine (I), which is not stable under continuous light irradiation. Herein, perovskite-based WLED is fabricated by lead-free bismuth (Bi)-doped inorganic perovskites Cs2SnCl6 and less-lead Mn-doped CsPbCl3 QDs, which emits white light with color coordinates of (0.334, 0.297). The Bi-doped Cs2SnCl6 and Mn-doped CsPbCl3 QDs both show excellent stability when kept in the ambient air. As benefits from this desired characteristic, the as-prepared WLED shows excellent stability along with operating time. These results can promote the application of inorganic perovskite QDs in the field of WLEDs.