The UV-B component of sunlight damages the DNA in skin cells, which can lead to skin cancer and premature aging. Therefore, it is necessary to use creams that also contain UV-active substances. Many sunscreens contain titanium dioxide due to its capacity to absorb UV-B wavelengths. In the present study, titan dioxide was introduced in alginate and chitosan-alginate hydrogel composites that are often involved as scaffold compositions in tissue engineering applications. Alginate and chitosan were chosen due to their important role in skin regeneration and skin protection. The composites were cross-linked with calcium ions and investigated using FT-IR, Raman, and UV-Vis spectroscopy. The stability of the obtained samples under solar irradiation for skin protection and regeneration was analyzed. Then, the hydrogel composites were assayed in vitro by immersing them in simulated body fluid and exposing them to solar simulator radiation for 10 min. The samples were found to be stable under solar light, and a thin apatite layer covered the surface of the sample with the two biopolymers and titanium dioxide. The in vitro cell viability assay suggested that the anatase phase in alginate and chitosan-alginate hydrogel composites have a positive impact.
RESUMO
Calcium titanate (CTO) photocatalysts were synthesized using a sol-gel method by adopting a cost-efficient, rapid calcination technique. The CTOs were characterized by X-ray diffractometry, X-ray photoelectron spectroscopy, infrared spectroscopy, nitrogen adsorption, porosimetry measurements, scanning/transmission electron microscopy, and diffuse reflectance spectroscopy. Their photocatalytic activity was assessed through the photocatalytic degradation of phenol, oxalic acid, and chlorophenol under UV light exposure, using a commercial CTO as a reference. The stability of the samples was evaluated using compounds with -OH, -COOH, and -Cl functional groups. Characterization results showed that CTO composites containing anatase, rutile, and brookite titania were obtained. Increasing the calcination temperature led to various crystalline compositions, higher crystallinity, larger primary crystallite sizes, and smaller specific surface areas. The photocatalytic activity of all CTO/TiO2 composites was superior compared to the commercial CTO we used as a reference. The high photocatalytic activity of the best-performing composites was attributed to their higher specific surface areas and the synergistic effect between the crystal phases. A cost comparison was also made between our unique calcination technique and conventional calcination, and it was found that our method is approximately 35% more cost-effective, while retaining the photocatalytic activity.