Suitability and Modification of Different Renewable Materials as Feedstock for Sustainable Flame Retardants.

Due to their chemical structure, conventional flame retardants are often toxic, barely biodegradable and consequently neither healthy nor environmentally friendly. Their use is therefore increasingly limited by regulations. For this reason, research on innovative flame retardants based on sustainable materials is the main focus of this work. Wheat starch, wheat protein, xylan and tannin were modified with phosphate salts in molten urea. The functionalization leads to the incorporation of phosphates (up to 48 wt.%) and nitrogen (up to 22 wt.%). The derivatives were applied on wood fibers and tested as flame retardants. The results indicate that these modified biopolymers can provide the same flame-retardant performances as commercial compounds currently used in the wood fiber industry. Besides, the flame retardancy smoldering effects may also be reduced compared to unmodified wood fibers depending on the used biopolymer. These results show that different biopolymers modified in phosphate/urea systems are a serious alternative to conventional flame retardants.

Flame Retardancy of Wood Fiber Materials Using Phosphorus-Modified Wheat Starch.

Biopolymer-based flame retardants (FR) are a promising approach to ensure adequate protection against fire while minimizing health and environmental risks. Only a few, however, are suitable for industrial purposes because of their poor flame retardancy, complex synthesis pathway, expensive cleaning procedures, and inappropriate application properties. In the present work, wheat starch was modified using a common phosphate/urea reaction system and tested as flame retardant additive for wood fibers. The results indicate that starch derivatives from phosphate/urea systems can reach fire protection efficiencies similar to those of commercial flame retardants currently used in the wood fiber industry. The functionalization leads to the incorporation of fire protective phosphates (up to 38 wt.%) and nitrogen groups (up to 8.3 wt.%). The lowest levels of burning in fire tests were measured with soluble additives at a phosphate content of 3.5 wt.%. Smoldering effects could be significantly reduced compared to unmodified wood fibers. The industrial processing of a starch-based flame retardant on wood insulating materials exhibits the fundamental applicability of flame retardants. These results demonstrate that starch modified from phosphate/urea-systems is a serious alternative to traditional flame retardants.