Synthesis of galactoglucomannan-based latex via emulsion polymerization.

This is the first time to report a facile strategy to fabricate galactoglucomannan-based latex with highly transparent, hydrophobic and flexible characteristics by combining etherification with subsequent emulsion polymerization. The allylated galactoglucomannans (A-GGM) and galactoglucomannan-based latexes (GGM-L) were prepared and their chemical structure, substitution degree, molecular weight, conversion rate, particle size and zeta potential were characterized by ATR-FTIR, 1HNMR, quantitative 13CNMR, HP-SEC, HPLC and zeta-sizer nanometer analyzer, respectively. Furthermore, the effects of substitution degree on film surface roughness and homogeneity, water vapor permeability (WVP) and thermal stability were evaluated by AFM, SEM, WVP and TGA, respectively. The optimal GGM-L film exhibited 91.3% transmittance and 0.43% haze, 117° water contact angle, 31.2% elongation at break and 30.9 MPa ultimate tensile stress. The bio-based content of the GGM-L may reach about 99 wt%, which provides a promising avenue for polyolefin-based latex replacement for paper and paperboard applications.

The Synthesis of Low-Viscosity Organotin-Free Moisture-Curable Silane-Terminated Poly(Urethane-Urea)s.

This work explores the possibility of synthesizing moisture-curable silane-terminated poly(urethane-urea)s (SPURs) of low viscosity. First, NCO-terminated urethane prepolymers were prepared, followed by silane end-capping. The impact of polyol molecular weight and the ratio of isocyanate to polyol (NCO/OH) on viscosity and the properties of SPUR were examined. As alternatives to the organotin catalysts traditionally used for the polyurethane synthesis and curing processes, bismuth carboxylate catalysts were evaluated. In addition, the effect of organofunctional groups in the aminosilane structure (R1⁻NH⁻R2⁻Si(OR3)3), i.e., R1 (alkyl, aryl or trimethoxysilyl-propyl), the spacer R2 (α or γ) and alkyl group R3 (methyl or ethyl), was examined. The chemical and physical structures of the SPUR were investigated by nuclear magnetic resonance spectroscopy (NMR), Fourier transform infrared spectroscopy (FT-IR) and the mechanical properties were evaluated by tensile tests. The results reveal that silane-terminated, moisture-curable polyurethanes can be successfully synthesized and cured with bismuth carboxylate catalysts. SPUR exhibiting low viscosity, with adequate tensile strength and elongation can be prepared using environmentally benign bismuth carboxylate catalyst having a high metal content of 19%⁻21%, by utilizing secondary aminosilane end-cappers and an optimal combination of the polyol molecular weight and NCO/OH ratio.

Investigation on the Influence of Chain Extenders on the Performance of One-Component Moisture-Curable Polyurethane Adhesives.

In this work, a number of chain extended moisture-curable urethane prepolymers were synthesized in order to develop isocyanate terminated urethane prepolymer formulations that would simultaneously display both high adhesive strength and low viscosity. Proton nuclear magnetic resonance spectroscopy (¹H-NMR), size exclusion chromatography (SEC), differential scanning calorimetry (DSC), and Brookfield viscometry were utilized for characterizing the prepared urethane prepolymers. In addition, the adhesion strength of the cured prepolymers was determined by tensile shear strength test according to the DIN EN (Deutsches Institut für Normung, the German Institute for Standardization) 1465 standard. Especially, the role of different types of linear (butanediol, pentanediol) and branched chain extenders (dipropyleneglycol (di-PPG), tripropyleneglycol (tri-PPG) and the influence of their dosage on the degree of microphase separation between hard segments (HS) and soft segments (SS) in urethane prepolymers were studied. Furthermore, the benefits of utilizing either a one-step versus a two-step polymerization process were investigated. The results revealed that the extent of phase separation of different urethane prepolymers was dependent on the extent of hydrogen bonding interactions which was extensively studied by attenuated total reflectance infrared spectroscopy (ATR-FTIR). The incorporation of branched chain extenders (di-PPG and tri-PPG) did not result in notable phase separation between hard segments and soft segments, while linear chain extenders (pentanediol and butanediol) readily promoted phase separation. The degree of phase separation was particularly pronounced for butanediol, and when the linear chain extender ratio was higher than or equal to 0.74. Compared with a two-stage process, one-stage process produced more randomly distributed polymer chains with highly dispersed hard segments. Thus, urethane prepolymers exhibiting strong adhesive strength with simultaneously low viscosity were successfully developed by systematic adjustment of structural parameters.

Structure⁻Property Studies on a New Family of Halogen Free Flame Retardants Based on Sulfenamide and Related Structures.

A wide variety of molecules containing S⁻N or S⁻N⁻S cores were synthesized, and their flame retardant properties in polypropylene (PP), low density polyethylene (LDPE) and polystyrene (PS) were investigated. In addition, polymers or oligomers bearing the sulfenamide functionality (SN) were also synthesized. It was shown that this radical generator family based on sulfenamides is very versatile in terms of structural modifications, and the thermal decomposition range can be easily adjusted by changing the R groups attached to the core. The thermal stabilities of the different sulfenamides were examined by thermogravimetric analysis (TGA). Radicals generated by the homolytic cleavage of the S⁻N or S⁻N⁻S bonds at an elevated temperature can effectively interact with the intermediate products of polymer thermolysis and provide excellent flame retardant properties. The choice of most suitable SN-structure varies depending on the polymer type. For polypropylene DIN 4102-1 B2 and UL94 VTM-2 classifications were achieved with only 0.5 to 1 wt % of sulfenamide, and, in some cases, no flaming dripping was observed. Also for LDPE thin films, sulfenamides offered the DIN 4102-1 B2 rating at low dosage. In the case of polystyrene, the very stringent UL94 V-0 classification was even achieved at a loading of 5 wt % of sulfenamide.