Thermal hazard evaluation of lauroyl peroxide mixed with nitric acid.

Many thermal runaway incidents have been caused by organic peroxides due to the peroxy group, -O-O-, which is essentially unstable and active. Lauroyl peroxide (LPO) is also sensitive to thermal sources and is incompatible with many materials, such as acids, bases, metals, and ions. From the thermal decomposition reaction of various concentrations of nitric acid (HNO3) (from lower to higher concentrations) with LPO, experimental data were obtained as to its exothermic onset temperature (T0), heat of decomposition (ΔHd), isothermal time to maximum rate (TMRiso), and other safety parameters exclusively for loss prevention of runaway reactions and thermal explosions. As a novel finding, LPO mixed with HNO3 can produce the detonation product of 1-nitrododecane. We used differential scanning calorimetry (DSC), thermal activity monitor III (TAM III), and gas chromatography/mass spectrometer (GC/MS) analyses of the reactivity for LPO and itself mixed with HNO3 to corroborate the decomposition reactions and reaction mechanisms in these investigations.

Improvement of the mechanical property and thermal stability of polypropylene/recycled rubber composite by chemical modification and physical blending.

The binary blend materials containing the modified recycled rubber powder with maleic a hydride modified polypropylene thermoplastic elastomer were prepared by dynamic vulcanization and blended with a variety of additives such as activated agent, accelerator, solubilizer, and the crosslinking agent. The thermal properties and mechanical properties including tensile strengths and impact strengths of pristine rubber, polypropylene and their corresponding binary blends were investigated. Besides, the effects of the amount of rubber powder, polypropylene, crosslinking agent, accelerator, activator, and solvent were studied and the microstructures of the pristine rubber, pristine polypropylene, and their corresponding binary blends were observed by scanning electron microscopy. It was found that the compatibilizer could effectively disperse the size of 120 mesh of recycled rubber powder into the polypropylene in the same manner and the homogeneous tear section of the rubber/polypropylene thermoplastic elastomer was obtained. The results on the effects of additives on mechanical and morphological properties of recycled rubber/polypropylene binary blends guide the rational design of novel polymeric composites from recycled polymeric materials.