Poly(Vinylidene Fluoride-co-Hexafluoropropylene) Films Filled in Iron Nanoparticles for Infrared Shielding Applications.

In order to use the infrared (IR) radiation shielding materials, they should take a form of thin film coatings deposited on glass/polymer substrates or be used as fillers of glass/polymer. The first approach usually suffers from several technological problems. Therefore, the second strategy gains more and more attention. Taking into account this trend, this work presents the usage of iron nanoparticles (Fe NPs) embedded into the poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP) films as the shielding material in near-infrared (NIR) and mid-infrared (MIR) region. The performed investigations show that the transmittance of copolymer films decreases with increasing content of the Fe NPs inside them. It is found that the average fade of IR transmittance for 1, 2.5, 5, 10, and 50 mg of Fe NPs is about 13%, 24%, 31%, 77%, and 98%, respectively. Moreover, it is observed that the PVDF-HFP films filled in the Fe NPs almost does not reflect the NIR and MIR radiation. Hence, the IR shielding properties of the PVDF-HFP films can be effectively tuned by the addition of proper amount of the Fe NPs. This, in turn, shows that the PVDF-HFP films filled in the Fe NPs constitute a great option for IR antireflective and shielding applications.

Graphene Oxide with Controlled Content of Oxygen Groups as a Filler for Polymer Composites Used for Infrared Radiation Shielding.

Infrared (IR) shielding materials are commonly used for different applications, such as smart windows or optical filters. Infrared radiation is responsible for about 50% of the energy coming from the sun. During a hot summer or cold winter a lot of energy is needed to keep the optimal temperature inside buildings and means of transport. To reduce the heat transmission and save energy IR shielding materials can be used as coatings made of polymer composites. Graphene oxide (GO) and its reduced forms have interesting IR absorption properties and might be used as a filler in a polymer matrix for IR shielding applications. Graphene oxide can be reduced by different methods. Depending on the reduction method reduced graphene oxide (rGO) with a different content of oxygen can be obtained exhibiting different properties. In this work we propose new polymer nanocomposites with poly(vinyl alcohol) as the matrix and 0.1 wt.% addition of graphene materials with different oxygen content to be used for IR shielding applications. The results show that the properties of the graphene filler strongly influence the infrared shielding properties of the obtained nanocomposites. The best IR shielding properties were obtained for the composites where rGO with the lowest oxygen content was used.