RESUMO
Organosilicon materials have shown potential as dehydration agents for waterlogged wooden artifacts. These materials can polymerize under normal conditions to form polymers with favorable mechanical strength, antibacterial properties, and aging resistance. However, the insolubility of most organosilicon hindered their penetration into waterlogged wood, which may lead to an unwanted cracking. This study aimed to evaluate the effectiveness of polydimethylsiloxane (PDMS) and hydroxy-terminated polydimethylsiloxane (PDMS-OH) with low viscosity and moderate reactivity for dehydrating waterlogged wooden artifacts from the Nanhai No.1 shipwreck. Four surfactants ((3-aminopropyl) triethoxysilane (APTES), alkyl polyoxyethylene ether (APEO), tri-methylstearylammonium chloride (STAC), and fatty alcohol polyoxyethylene ether (AEO)) and cosurfactant were employed to transform the two kinds of water-repellent silicone oils into eight groups of highly permeable oil-in-water (O/W) emulsions. Under the catalysis of a neutral catalyst, in situ polymerization occurred within the wood cells. Group P2-2 formulated with PDMS-OH and APEO showed the best efficiency in maintaining the dimensions of the wood during dehydration. The dehydrated wood exhibited a natural color and texture with a minimal volume shrinkage rate of 1.89%. The resulting polymer adhered uniformly to the cell walls, effectively reinforcing the wood cell structure. The weight percent gain of the wood was only 218%, and the pores of the cell lumen were well maintained for future retreatment. This method effectively controlled the sol-gel reaction process of the organosilicon and prevented damage to the wooden artifact during the dehydration process. Moreover, the dehydrated wood samples only experienced a low weight gain of 17% at 95% relative humidity (RH), indicating their great environmental stability.
RESUMO
Tetraethoxysilane (TEOS) is the most commonly used silicon-based reinforcement agent for conserving art relics due to its cost-effectiveness and commercial maturity. However, the resulting silica gel phase is prone to developing cracks as the gel shrinks during the sol-gel process, potentially causing severe damage to the objects being treated. In this study, dodecyltrimethoxysilane (DTMS) was introduced into TEOS to minimize this shrinkage by adding elastic long chains to weaken the capillary forces. The gel formed from the DTMS/TEOS hybrid material was transparent and crack-free, featuring a dense microstructure without mesopores or micropores. It exhibited excellent thermal stability, with a glass transition temperature of up to 109.64 °C. Evaluation experiments were conducted on artificially aged, handmade bamboo paper. The TEOS-based hybrid material effectively combined with the paper fibers through the sol-gel process, polymerizing into a network structure that enveloped the paper surface or penetrated between the fibers. The surface of the treated paper displayed excellent hydrophobic properties, with no significant changes in appearance, color, or air permeability. The mechanical properties of the treated bamboo paper improved significantly, with longitudinal and transverse tensile strengths increasing by up to 36.63% and 44.25%, respectively. These research findings demonstrate the promising potential for the application of DTMS/TEOS hybrid materials in reinforcing paper relics.