Bio-cement is a green and energy-saving building material that has attracted much attention in the field of ecological environment and geotechnical engineering in recent years. The aim of this study is to investigate the use of bio-cement (enzyme-induced calcium carbonate precipitation-EICP) in combination with admixtures for the improvement of desert sands, which can effectively improve the mechanical properties of desert sands and is particularly suitable for sand-rich countries. In addition, the suitability of tap water in bio-cement was elucidated and the optimum ratio of each influencing factor when tap water is used as a solvent was derived. The results showed that peak values of unconfined compressive strength (maximum increase of about 130 times), shear strength (increase of 27.09%), calcium carbonate precipitation value (increase of about 4.39 times), and permeability (decrease of about 93.72 times) were obtained in the specimens modified by EICP combined with admixture as compared to the specimens modified by EICP only. The incorporation of skimmed milk powder, though significantly increasing the strength, is not conducive to cost control. The microscopic tests show that the incorporation of admixtures can provide nucleation sites for EICP, thus improving the properties of desert sand. This work can provide new research ideas for cross-fertilization between the disciplines of bio-engineering, ecology, and civil engineering.
RESUMO
In order to promote the development and utilization of desert sand, this study is based on researching the most suitable ratio of bio-cement, analyzing the shear strength and permeability of improved desert sand by combining bio-cement and fly ash, and clarifying the applicability of tap water in bio-cement. The relationship between the two and the microstructural properties was investigated using the results of the straight shear test and the permeability test. The results showed that the urease solution prepared with tap water had a more pronounced temperature resistance. The urea concentration and the corresponding pH environment had a direct effect on the urease activity. The calcium carbonate yield was positively correlated with the calcium concentration, and the urea concentration was higher in the ranges of 1.0-1.5 mol/L. As the enzyme-to-gel ratio decreased, the calcium carbonate precipitate produced per unit volume of urease solution gradually converged to a certain value. The shear strength (increased by 37.9%) and permeability (decreased by about 8.9-68.5%) of the modified desert sand peaked with the increase in fly ash content. The microscopic test results indicated that the fly ash could provide nucleation sites for the bio-cement, effectively improving the mechanical properties of the desert sand. The crystal types of calcium carbonate in the modified desert sand were calcite and aragonite, which were the most stable crystal types. This study provides innovative ideas for interdisciplinary research in the fields of bioengineering, ecology and civil engineering.