Poly(3,4-Ethylenedioxythiophene):Sulfamic Acid Modified Aramid Nanofibers: An Innovative Conductive Polymer With Enhanced Electromagnetic Interference Shielding and Thermoelectric Performance.

The development of alternative conductive polymers for the well-known poly (3,4-ethylenedioxythiophene):polystyrene sulfonate (PEDOT:PSS) is of great significance for improving the stability in long-term using and high-temperature environments. Herein, an innovative PEDOT:S-ANF aqueous dispersion is successfully prepared by using sulfamic acid (SA) to modified aramid nanofibers (S-ANF) as an alternative dispersant for PSS and the subsequent in situ polymerization of PEDOT. Thanks to the excellent film forming ability and surface negative groups of S-ANF, the PEDOT:S-ANF films show comparable tensile strength and elongation to unmodified PEDOT:ANF. Meanwhile, PEDOT:S-ANF has a high conductivity of 27.87 S cm-1, which is more than 20 times higher than that of PEDOT:PSS. The film exhibits excellent electromagnetic interference (EMI) shielding and thermoelectric performance, with a shielding effectiveness (SE) of 31.14 dB and a power factor (PF) of 0.43 µW m-1K-2. As a substitute for PSS, S-ANF exhibits significant structural and physicochemical properties, resulting in excellent chemical and thermal stability. Even under harsh conditions such as immersing to 0.1 M HCl, 0.1 M NaOH, and 3.5% NaCl solution, or high temperature conditions, the PEDOT:S-ANF films still maintain exceptional EMI shielding performance. Therefore, this multifunctional conductive polymer exhibits enormous potential and even proves its reliability in extreme situations.

Designing Nanofluidic Channels of Boron Nitride Nanosheets/Aramid Nanofibers/Covalent Organic Frameworks Nanofiltration Membrane for Ultrafast Mass Transport.

2D lamellar nanofiltration membrane is considered to be a promising approach for desalinating seawater/brackish water and recycling sewage. However, its practical feasibility is severely constrained by the lack of durability and stability. Herein, a ternary nanofiltration membrane via a mixed-dimensional assembly of 2D boron nitride nanosheets (BNNS) is fabricated, 1D aramid nanofibers (ANF), and 2D covalent organic frameworks (COF). The abundant 2D and 1D nanofluid channels endow the BNNS/ANF/COF membrane with a high flux of 194 L·m‒2·h‒1. By the synergies of the size sieving and Donnan effect, the BNNS/ANF/COF membrane demonstrates high rejection (among 98%) for those dyes whose size exceeds 1.0 nm. Moreover, the BNNS/ANF/COF membrane also exhibits remarkable durability and mechanical stability, which are attributed to the strong adhesion and interactions between BNNS, ANF, and COF, as well as the superior mechanical robustness of ANF. This work provides a novel strategy to develop robust and durable 2D lamellar nanofiltration membranes with high permeance and selectivity simultaneously.

Tailoring the ion storage of MXene by aramid nanofibers towards self-standing electrodes for flexible solid-state supercapacitors.

Two-dimensional (2D) transition metal carbides and nitrides (MXenes) are a class of 2D nanomaterials that can offer excellent properties for high-performance supercapacitors. Nevertheless, irreversible restacking of MXene sheets decreases the interlayer spacing, which inhibits the ion intercalation between the MXene nanosheets and finally deteriorates the electrochemical performance of supercapacitors. Herein, aramid nanofibers (ANFs) are mixed with Ti3C2TxMXene to prepare MXene/ANFs composite films. The restacking of MXene sheets is inhibited by the electrostatic repulsion between ANFs and MXene. The ANFs act as intercalation agents to increase the interlayer spacing of the composite films, which can improve the ion storage ability of supercapacitors. Furthermore, the ANFs enhance the mechanical strength of the composite films due to the strong hydrogen bonding interaction and nanomechanical interlocking between ANFs and MXene, endowing the composite films with self-standing property. The resultant composite films are used as electrodes for flexible solid-state supercapacitors to achieve high specific capacitance (996.5 mF cm-2at 5 mV s-1) and outstanding cycling stability. Thus, this work provides a potential strategy to regulate the properties of 2D nanomaterials, which may expand the application of them in energy storage, ionic separation, osmotic energy conversion and beyond.

Nacre-like Anisotropic Multifunctional Aramid Nanofiber Composites for Electromagnetic Interference Shielding, Thermal Management, and Strain Sensing.

Developing multifunctional flexible composites with high-performance electromagnetic interference (EMI) shielding, thermal management, and sensing capacity is urgently required but challenging for next-generation smart electronic devices. Herein, novel nacre-like aramid nanofibers (ANFs)-based composite films with an anisotropic layered microstructure were prepared via vacuum-assisted filtration and hot-pressing. The formed 3D conductive skeleton enabled fast electron and phonon transport pathways in the composite films. As a result, the composite films showed a high electrical conductivity of 71.53 S/cm and an outstanding thermal conductivity of 6.4 W/m·K when the mass ratio of ANFs to MXene/AgNWs was 10:8. The excellent electrical properties and multi-layered structure endowed the composite films with superior EMI shielding performance and remarkable Joule heating performance, with a surface temperature of 78.3 °C at a voltage of 2.5 V. Additionally, it was found that the composite films also exhibited excellent mechanical properties and outstanding flame resistance. Moreover, the composite films could be further designed as strain sensors, which show great promise in monitoring real-time signals for human motion. These satisfactory results may open up a new opportunity for EMI shielding, thermal management, and sensing applications in wearable electronic devices.

Bioinspired Impact-Resistant and Self-Monitoring Nanofibrous Composites.

Lightweight and impact-resistant materials with self-monitoring capability are highly desired for protective applications, but are challenging to be artificially fabricated. Herein, a scalable-manufactured aramid nanofiber (ANF)-based composite combining these key properties is presented. Inspired by the strengthening and toughening mechanisms relying on recoverable interfaces commonly existing in biological composites, mechanically weak but dense hydrogen bonds are introduced into the ANF interfaces to achieve simultaneously enhanced tensile strength (300 MPa), toughness (55 MJ m-3 ), and impact resistance of the nanofibrous composite. The achieved mechanical property combination displays attractive advantages compared with that of most of previously reported nanocomposites. Additionally, the nanofibrous composite is designed with a capability for real-time self-monitoring of its structural safety during both quasi-static tensile and dynamic impact processes, based on the strain/damage-induced resistance variations of a conductive nanowire network inside it. These comprehensive properties enable the present nanofibrous composite with promising potential for protective applications.

Cellulose nanocrystal functionalized aramid nanofiber reinforced epoxy nanocomposites with high strength and toughness.

The mechanical properties of polymer nanocomposites can be improved by incorporating various types of nanofillers. The hybridization of nanofillers through covalent linkages between nanofillers with different dimensions and morphology can further increase the properties of nanocomposites. In this work, aramid nanofibers (ANFs) are modified using chlorinated cellulose nanocrystals (CNCs) and functionalized with 3-glycidoxypropyltrimethoxysilane to improve the chemical and mechanical interaction in an epoxy matrix. The integration of CNC functionalized ANFs (fACs) in the epoxy matrix simultaneously improves Young's modulus, tensile strength, fracture properties, and viscoelastic properties. The test results show that 1.5 wt% fAC reinforced epoxy nanocomposites improve Young's modulus and tensile strength by 15.1% and 10.1%, respectively, and also exhibit 2.5 times higher fracture toughness compared to the reference epoxy resin. Moreover, the glass transition temperature and storage modulus are found to increase when fACs are incorporated. Thus, this study demonstrates that the enhanced chemical and mechanical interaction by the CNC functionalization on the ANFs can further improve the static and dynamic mechanical properties of polymer nanocomposites.

Multifunctional Thermally Conductive Composite Films Based on Fungal Tree-like Heterostructured Silver Nanowires@Boron Nitride Nanosheets and Aramid Nanofibers.

Thermal conduction for electronic equipment has grown in importance in light of the burgeoning of 5G communication. It is imperatively desired to design highly thermally conductive fillers and polymer composite films with prominent Joule heating characteristics and extensive mechanical properties. In this work, "solvothermal & in situ growth" method is carried out to prepare "Fungal tree"-like hetero-structured silver nanowires@boron nitride nanosheet (AgNWs@BNNS) thermally conductive fillers. The thermally conductive AgNWs@BNNS/ANF composite films are obtained by the method of "suction filtration self-assembly and hot-pressing". When the mass fraction of AgNWs@BNNS is 50 wt%, AgNWs@BNNS/ANF composite film presents the optimal thermal conductivity coefficient of 9.44 W/(m ⋅ K) and excellent tensile strength of 136.6 MPa, good temperature-voltage response characteristics, superior electrical stability and reliability, which promise a wide application potential in 5G electronic devices.

Phase Separation-Controlled Assembly of Hierarchically Porous Aramid Nanofiber Films for High-speed Lithium-Metal Batteries.

The growth of lithium (Li) dendrites reduces the lifespan of Li-metal batteries and causes safety issues. Herein, hierarchically porous aramid nanofiber separators capable of effectively suppressing the Li dendrite growth while maintaining highly stable cycle performances at high charge/discharge rates are reported. A two-step solvent exchange process combined with reprotonation-mediated self-assembly is utilized to control the bimodal porous structure of the separators. In particular, when ethanol and water are used sequentially, aramid nanofibers form hierarchical porous structures containing nanopores in macroporous polymer frameworks to yield a mechanically robust membrane with high porosity of 97% or more. The optimized samples exhibit high ionic conductivities of 1.87-4.04 mS cm-1 and high Li-ion transference numbers of 0.77-0.84 because of the ultrahigh porosity and selective affinity to anions. Li-metal symmetric cells do not show any noticeable presence of dendrites after 100 cycles, and they operate stably for more than 1500 cycles even under extreme conditions with a high current density of >20 mA cm-2 . In addition, the LiFePO4 /Li full cell retains 86.3% of its capacity after 1000 cycles at a charge rate of 30 C.

Branched Aramid Nanofibers.

Interconnectivity of components in three-dimensional networks (3DNs) is essential for stress transfer in hydrogels, aerogels, and composites. Entanglement of nanoscale components in the network relies on weak short-range intermolecular interactions. The intrinsic stiffness and rod-like geometry of nanoscale components limit the cohesive energy of the physical crosslinks in 3DN materials. Nature realizes networked gels differently using components with extensive branching. Branched aramid nanofibers (BANFs) mimicking polymeric components of biological gels were synthesized to produce 3DNs with high efficiency stress transfer. Individual BANFs are flexible, with the number of branches controlled by base strength in the hydrolysis process. The extensive connectivity of the BANFs allows them to form hydro- and aerogel monoliths with an order of magnitude less solid content than rod-like nanocomponents. Branching of nanofibers also leads to improved mechanics of gels and nanocomposites.

Preparation of a colorimetric hydrogel indicator reinforced with modified aramid nanofiber employing natural anthocyanin to monitor shrimp freshness.

The pH-responsive hydrogels have potential applications in food visualization detection, but their fragile mechanical properties limit their applicability. The excellent mechanical properties and thermal stability of aramid nanofibers (ANFs) can improve the structural stability of hydrogels. In this study, the surface properties of ANFs were enhanced through modification to improve their surface activity. The modified ANFs, designated as ANF-SN, were produced following treatment with a mixture of sulfuric acid (H2SO4) and nitric acid (HNO3), which led to increased reactivity and dispersibility of the ANFs due to the proliferation of active groups on their nanofiber surface. The preferred anthocyanin extract from purple sweet potatoes (purple sweet potato extract [PSPE]) had significant color responses to pH (2-12) and ammonia vapor. A stable dual-network colorimetric hydrogel was fabricated by combining ANF-SN, polyvinyl alcohol/sodium alginate (PVA/SA), and PSPE through a two-step method (freeze-thawing and staining). Characterization analysis showed that the strong acid modification of ANFs effectively improved their chemical reactivity. ANF-SN was better than ANF in promoting the formation of hydrogen bond networks, enhancing hydrogel network structures, and improving the viscoelasticity of hydrogels. The optimal hydrogel indicator PVA/SA/ANF-SN/PSPE had good color responsiveness and sensitivity to ammonia. It can also be used to further determine shrimp freshness value using a smartphone and RGB color-picking software.

Oxhide gelatin-regulated aramid nanofiber/liquid metal films with sandwiched structure for electromagnetic interference shielding.

Liquid metal (LM) based electromagnetic interference (EMI) shielding materials with high conductivity and continuous deformation capacity are important needs for meeting modern advanced electronic equipment. However, an independent free-standing film with LM is difficult to achieve due to its unique fluidity properties. Here, a simple alternating filtration film-forming method was utilized to orderly construct a sandwiched EMI shielding film with LM stabilized by bio-based oxhide gelatin (gel) as the intermediate conductive layer, and two films of aramid nanofibers/oxhide gel (ANF/gel) as the external insulating protective layers. This design not only prevents LM from being exposed to environmental conditions, but also reduces the risk of chemical corrosion in practical applications. Under optimal LM addition conditions, the sandwiched film (0.3-3 L) exhibited better EMI shielding performance of 50.4 dB in the X-band than the blended film (0.7 dB), as well as excellent mechanical properties (tensile strength of 65.8 MPa, strain 8.6 %). More importantly, the sandwiched film still maintained reliable EMI shielding performance after being experienced largely physical deformation. This study provides a new solution for preparing LM-based EMI shielding composites, and is expected to arouse pursuit of high EMI shielding effects of bio-based gel while also paying attention to their safety.

Aramid nanofiber membrane decorated with monodispersed silver nanoparticles as robust and flexible SERS chips for trace detection of multiple toxic substances.

Aramid nanofibers (ANFs) as an innovative nanoscale building block exhibit great potential for novel high-performance multifunctional membranes attributed to their extraordinary performance. However, the application of aramid nanofibers in the field of surface enhanced Raman scattering (SERS) sensing has been rarely reported. In this work, aramid nanofibers derived from commercial Kevlar fibers were synthesized by a facile dimethyl sulfoxide/potassium hydroxide (DMSO/KOH) solution treatment. The monodispersed silver nanoparticle-decorated aramid nanofiber (m-Ag@ANF) membranes were constructed by an efficient vacuum filtration technique. Taking advantages of unique intrinsic properties of ANF, the m-Ag@ANF substrates exhibit good flexibility, excellent mechanical properties and prominent thermal stability. Besides, due to the abundance of positively charged amino-group on the ANF substrates, the negatively charged m-AgNPs were uniformly and firmly deposited on the surface of ANF substrate through electrostatic interactions. As a result, the optimal flexible m-Ag-9@ANF SERS substrate exhibits high sensitivity of 10-9 M for methylene blue (MB) and excellent signal reproducibility (RSD = 6.37 %), as well as outstanding signal stability (up to 15 days). Besides, the 2D Raman mapping and FDTD simulations further reveal prominent signal homogeneity and strong electric field distribution for flexible m-Ag-9@ANF SERS substrate. Finally, it is demonstrated that the flexible m-Ag-9@ANF SERS substrate can also be used for detection of toxic molecules on irregular surfaces by a feasible paste-and-read process. The m-Ag@ANF paper exhibits potential applications as a flexible, low-cost, robust and stable SERS sensing platform for trace detection of toxic materials.

Aramid Nanodielectrics for Ultraconformal Transparent Electronic Skins.

On-skin electronics require minimal thicknesses and decent transparency for conformal contact, imperceptible wearing, and visual aesthetics. It is challenging to search for advanced ultrathin dielectrics capable of supporting the active components while maintaining bending softness, easy handling, and wafer-scale processability. Here, self-delaminated aramid nanodielectrics (ANDs) are demonstrated, enabling any skin-like electronics easily exfoliated from the processing substrates after complicated nanofabrication. In addition, ANDs are mechanically strong, chemically and thermally stable, transparent and breathable, therefore are ideal substrates for soft electronics. As demonstrated, compliant epidermal electrodes comprising silver nanowires and ANDs can successfully record high-quality electromyogram signals with low motion artifacts and satisfying sweat and water resistance. Furthermore, ANDs can serve as both substrates and dielectrics in single-walled carbon nanotube field-effect transistors (FETs) with a merely 160-nm thickness, which can be operated within 4 V with on/off ratios of 1.4 ± 0.5 × 105 , mobilities of 39.9 ± 2.2 cm2 V-1 s-1 , and negligible hysteresis. The ultraconformal FETs can function properly when wrapped around human hair without any degradation in performance.

Polymer Fiber Rigid Network with High Glass Transition Temperature Reinforces Stability of Organic Photovoltaics.

Organic photovoltaics (OPVs) need to overcome limitations such as insufficient thermal stability to be commercialized. The reported approaches to improve stability either rely on the development of new materials or on tailoring the donor/acceptor morphology, however, exhibiting limited applicability. Therefore, it is timely to develop an easy method to enhance thermal stability without having to develop new donor/acceptor materials or donor-acceptor compatibilizers, or by introducing another third component. Herein, a unique approach is presented, based on constructing a polymer fiber rigid network with a high glass transition temperature (Tg) to impede the movement of acceptor and donor molecules, to immobilize the active layer morphology, and thereby to improve thermal stability. A high-Tg one-dimensional aramid nanofiber (ANF) is utilized for network construction. Inverted OPVs with ANF network yield superior thermal stability compared to the ANF-free counterpart. The ANF network-incorporated active layer demonstrates significantly more stable morphology than the ANF-free counterpart, thereby leaving fundamental processes such as charge separation, transport, and collection, determining the device efficiency, largely unaltered. This strategy is also successfully applied to other photovoltaic systems. The strategy of incorporating a polymer fiber rigid network with high Tg offers a distinct perspective addressing the challenge of thermal instability with simplicity and universality.

Controlled Structural Relaxation of Aramid Nanofibers for Superstretchable Polymer Fibers with High Toughness and Heat Resistance.

Polymer fibers that combine high toughness and heat resistance are hard to achieve, which, however, hold tremendous promise in demanding applications such as aerospace and military. This prohibitive design task exists due to the opposing property dependencies on chain dynamics because traditional heat-resistant materials with rigid molecular structures typically lack the mechanism of energy dissipation. Aramid nanofibers have received great attention as high-performance nanoscale building units due to their intriguing mechanical and thermal properties, but their distinct structural features are yet to be fully captured. We show that aramid nanofibers form nanoscale crimps during the removal of water, which primarily resides at the defect planes of pleated sheets, where the folding can occur. The precise control of such a structural relaxation can be realized by exerting axial loadings on hydrogel fibers, which allows the emergence of aramid fibers with varying angles of crimps. These crimped fibers integrate high toughness with heat resistance, thanks to the extensible nature of nanoscale crimps with rigid molecular structures of poly(p-phenylene terephthalamide), promising as a template for stable stretchable electronics. The tensile strength/modulus (392-944 MPa/11-29 GPa), stretchability (25-163%), and toughness (154-445 MJ/cm3) are achieved according to the degree of crimping. Intriguingly, a toughness of around 430 MJ/m3 can be maintained after calcination below the relaxation temperature (259 °C) for 50 h. Even after calcination at 300 °C for 10 h, a toughness of 310 MJ/m3 is kept, outperforming existing polymer materials. Our multiscale design strategy based on water-bearing aramid nanofibers provides a potent pathway for tackling the challenge for achieving conflicting property combinations.

Biomimetic Aramid Nanofiber/ß-FeOOH Composite Coating for Polypropylene Separators in Lithium-Sulfur Batteries.

Aramid nanofibers (ANFs), with attractive mechanical and thermal properties, have attracted much attention as key building units for the design of high-performance composite materials. Although great progress has been made, the potential of ANFs as fibrous protein mimetics for controlling the growth of inorganic materials has not been fully revealed, which is critical for avoiding phase separation associated with typical solution blending. In this work, we show that ANFs could template the oriented growth of ß-FeOOH nanowhiskers, which enables the synthesis of ANFs/ß-FeOOH hybrids as composite coatings for polypropylene (PP) separators in Li-S batteries. The modified PP separator exhibits enhanced mechanical properties, heightened thermal performance, optimized electrolyte wettability, and improved ion conductivity, leading to superior electrochemical properties, including high initial specific capacity, better rate capability, and long cycling stability, which are superior to those of the commercial PP separators. Importantly, the addition of ß-FeOOH to ANFs could further contribute to the suppression of lithium polysulfide shuttling by chemical immobilization, inhibition of the growth of lithium dendrites because of the intrinsic high modulus and hardness, and promotion of reaction dynamics due to the catalytic effect. We believe that our work may provide a potent biomimetic pathway for the development of advanced battery separators based on ANFs.

Ultrastrong Nanopapers with Aramid Nanofibers and Silver Nanowires Reinforced by Cellulose Nanofibril-Assisted Dispersed Graphene Nanoplates for Superior Electromagnetic Interference Shielding.

High-strength, lightweight, ultrathin, and flexible electromagnetic interference (EMI) shielding materials with a high shielding effectiveness (SE) are essential for modern integrated electronics. Herein, cellulose nanofibrils (CNFs) are employed to homogeneously disperse graphene nanoplates (GNPs) into an aramid nanofiber (ANF) network and silver nanowire (AgNW) network, respectively, producing high-performance nanopapers. These nanopapers, featuring nacre-mimetic microstructures and layered architectures, exhibited high tensile strength (601.11 MPa) and good toughness (103.56 MJ m-3) with a thickness of only 24.58 µm. Their specific tensile strength reaches 447.59 MPa·g-1·cm3, which is 1.74 times that of titanium alloys (257 MPa·g-1·cm3). The AgNW/GNP composite conductive layers exhibit an electrical conductivity of 12010.00 S cm-1, providing the nanopapers with great EMI shielding performance, achieving an EMI SE of 63.87 dB and an EMI SE/t of 25978.80 dB cm-1. The nanopapers also show reliable durability, retaining a tensile strength of 500.96 MPa and an EMI SE of 57.59 dB after 120,000 folding cycles. Additionally, they have a good electrical heating performance with a fast response time, low driving voltage, effective deicing capability, and reliable heating capacity in water. This work presents a strategy to develop a high-performance nanopaper, showing great potential for applications in electromagnetic compatibility, national defense, smart electronics, and human health.

Strong, Tough, and Biocompatible Poly(vinyl alcohol)-Poly(vinylpyrrolidone) Multiscale Network Hydrogels Reinforced by Aramid Nanofibers.

Poly(vinyl alcohol) (PVA) hydrogels are water-rich, three-dimensional (3D) network materials that are similar to the tissue structure of living organisms. This feature gives hydrogels a wide range of potential applications, including drug delivery systems, articular cartilage regeneration, and tissue engineering. Due to the large amount of water contained in hydrogels, achieving hydrogels with comprehensive properties remains a major challenge, especially for isotropic hydrogels. This study innovatively prepares a multiscale-reinforced PVA hydrogel from molecular-level coupling to nanoscale enhancement by chemically cross-linking poly(vinylpyrrolidone) (PVP) and in situ assembled aromatic polyamide nanofibers (ANFs). The optimized ANFs-PVA-PVP (APP) hydrogels have a tensile strength of ≈9.7 MPa, an elongation at break of ≈585%, a toughness of ≈31.84 MJ/m3, a compressive strength of ≈10.6 MPa, and a high-water content of ≈80%. It is excellent among all reported PVA hydrogels and even comparable to some anisotropic hydrogels. System characterizations show that those performances are attributed to the particular multiscale load-bearing structure and multiple interactions between ANFs and PVA. Moreover, APP hydrogels exhibit excellent biocompatibility and a low friction coefficient (≈0.4). These valuable performances pave the way for broad potential in many advanced applications such as biological tissue replacement, flexible wearable devices, electronic skin, and in vivo sensors.

Ultrafine Aramid Nanofiber-Assisted Large-Area Dense Stacking of MXene Films for Electromagnetic Interference Shielding and Multisource Thermal Conversion.

Polymers are often used as adhesives to improve the mechanical properties of flexible electromagnetic interference (EMI) shielding layered films, but the introduction of these insulating adhesives inevitably reduces the EMI performance. Herein, ultrafine aramid nanofibers (UANF) with a diameter of only 2.44 nm were used as the binder to effectively infiltrate and minimize the insulating gaps in MXene films, for balancing the EMI shielding and mechanical properties. Combining the evaporation-induced scalable assembly assisted by blade coating, flexible large-scale MXene/UANF films with highly aligned and compact MXene stacking are successfully fabricated. Compared with the conventional ANF with a larger diameter of 7.05 nm, the UANF-reinforced MXene film exhibits a "brick-mortar" structure with higher orientation and compacter stacking MXene nanosheets, thus showing the higher mechanical properties, electrical conductivity, and EMI shielding performance. By optimizing MXene content, the MXene/UANF film can achieve the optimal tensile strength of 156.9 MPa, a toughness of 2.9 MJ m-3, satisfactory EMI shielding effectiveness (EMI SE) of 40.7 dB, and specific EMI SE (SSE/t) of 22782.4 dB cm2/g). Moreover, the composite film exhibits multisource thermal conversion functions including Joule heating and photothermal conversion. Therefore, the multifunctional MXene/UANF EMI shielding film with flexibility, foldability, and robust mechanical properties shows the practical potential in complex application environments.

Vapor deposition strategy for implanting isolated Fe sites into papermaking nanofibers-derived N-doped carbon aerogels for liquid Electrolyte-/All-Solid-State Zn-Air batteries.

Single-atom catalysts (SACs), with precisely controlled metal atom distribution and adjustable coordination architecture, have gained intensive concerns as efficient oxygen reduction reaction (ORR) electrocatalysts in Zn-air batteries (ZAB). The attainment of a monodispersed state for metallic atoms anchored on the carbonaceous substrate remains the foremost research priority; however, the persistent challenges lie in the relatively weak metal-support interactions and the instability of captured single atom active sites. Furthermore, in order to achieve rapid transport of O2 and other reactive substances within the carbon matrix, manufacturing SACs based on multi-stage porous carbon substrates is highly anticipated. Here, we propose a methodology for the fabrication of carbon aerogels (CA)-supported SACs utilizing papermaking nanofibers, which incorporates advanced strategies for N-atom self-doping, defect/vacancy introduction, and single-atom interface engineering. Specifically, taking advantages of using green and energy-efficient feedstocks, combining with a direct pore-forming template volatilization and chemical vapor deposition approach, we successfully developed N-doped carbon aerogels immobilized with separated iron sites (Fe-SAC@N/CA-Cd). The obtained Fe-SAC@N/CA-Cd exhibited substantially large specific surface area (SBET = 1173 m2/g) and a multi-level pore structure, which can effectively mitigate the random aggregation of Fe atoms during pyrolysis. As a result, it demonstrated appreciable activity and stability in catalyzing the ORR progress (E1/2 = 0.88 V, Eonset = 0.96 V). Furthermore, the assembled liquid electrolyte-state Zn-air batteries (LES-ZAB) and all-solid-state Zn-air battery (ASS-ZAB) also provides encouraging performance, with a peak power density of 169 mW cm-2 for LES-ZAB and a maximum power density of 124 mW cm-2 for ASS-ZAB.