Decay and Termite Resistance of Wood Modified by High-Temperature Vapour-Phase Acetylation (HTVPA), a Simultaneous Acetylation and Heat Treatment Modification Process.

High-temperature vapour-phase acetylation (HTVPA) is a simultaneous acetylation and heat treatment process for wood modification. This study was the first investigation into the impact of HTVPA treatment on the resistance of wood to biological degradation. In the termite resistance test, untreated wood exhibited a mass loss (MLt) of 20.3%, while HTVPA-modified wood showed a reduced MLt of 6.6-3.2%, which decreased with an increase in weight percent gain (WPG), and the termite mortality reached 95-100%. Furthermore, after a 12-week decay resistance test against brown-rot fungi (Laetiporus sulfureus and Fomitopsis pinicola), untreated wood exhibited mass loss (MLd) values of 39.6% and 54.5%, respectively, while HTVPA-modified wood exhibited MLd values of 0.2-0.9% and -0.2-0.3%, respectively, with no significant influence from WPG. Similar results were observed in decay resistance tests against white-rot fungi (Lenzites betulina and Trametes versicolor). The results of this study demonstrated that HTVPA treatment not only effectively enhanced the decay resistance of wood but also offered superior enhancement relative to separate heat treatment or acetylation processes. In addition, all the HTVPA-modified wood specimens prepared in this study met the requirements of the CNS 6717 wood preservative standard, with an MLd of less than 3% for decay-resistant materials.

Biological Durability of Wood-Polymer Composites-The Role of Moisture and Aging.

Knowledge about the resistance of wood-polymer composites (WPCs) to biological attack is of high importance for purpose-oriented use in outdoor applications. To gain this knowledge, uniform test methods are essential. EN 15534-1 (2018) provides a general framework, including the recommendation of applying a pre-weathering procedure before the biological laboratory tests. However, the procedure's manner is not specified, and its necessity assumes that a durability test without such pre-weathering will not produce the structural changes that occur during outdoor use. To verify this assumption, this study examined the influence of natural, ground-level pre-weathering on the material properties of different WPC variants, which were tested at intervals of six months in four durability tests under laboratory conditions in accordance with EN 15534-1 (2018). Weathering factors were calculated from determined characteristic values such as mass loss, and loss in moduli of elasticity (MOE) and rupture (MOR). The weathering factors based on mechanical properties tended to decrease with increasing weathering duration. The expected negative influence of pre-weathering on these material properties was thus not confirmed. The weathering factors based on mass loss were subject to high variation. No significant effect of pre-weathering on mass loss due to fungal attack became evident. Overall, the necessity of a pre-weathering step in biological durability tests shall be questioned based on the presented results.