RESUMO
The flammability of various materials used in industry is an important issue in the modern world. This work is devoted to the study of the effect of flame retardants, graphene and DDM-DOPO (9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide-4,4'-diamino-diphenyl methane), on the flammability of glass-fiber-reinforced epoxy resin (GFRER). Samples were made without additives and with additives of fire retardants: graphene and DDM-DOPO in various proportions. To study the flammability of the samples, standard flammability tests were carried out, such as thermogravimetric analysis, the limiting oxygen index (LOI) test, and cone calorimetry. In addition, in order to test the effectiveness of fire retardants under real fire conditions, for the first time, the thermal structure of downward flame propagation over GFRER composites was measured using thin thermocouples. For the first time, the measured thermal structure of the flame was compared with the results of numerical simulations of flame propagation over GFRER.
Assuntos
Incêndios , Retardadores de Chama , Grafite , Resinas Epóxi , CalorimetriaRESUMO
Due to the high flammability and smoke toxicity of polyurethane foams (PUFs) during burning, distinct efficient combinations of flame retardants are demanded to improve the fire safety of PUFs in practical applications. This feature article focuses on one of the most impressive halogen-free combinations in PUFs: expandable graphite (EG) and phosphorus-based flame retardants (P-FRs). The synergistic effect of EG and P-FRs mainly superimposes the two modes of action, charring and maintaining a thermally insulating residue morphology, to bring effective flame retardancy to PUFs. Specific interactions between EG and P-FRs, including the agglutination of the fire residue consisting of expanded-graphite worms, yields an outstanding synergistic effect, making this approach the latest champion to fulfill the demanding requirements for flame-retarded PUFs. Current and future topics such as the increasing use of renewable feedstock are also discussed in this article.
RESUMO
While plastics are regarded as the most resourceful materials nowadays, ranging from countless utilities including protective or decorating coatings, to adhesives, packaging materials, electronic components, paintings, furniture, insulating composites, foams, building blocks and so on, their critical limitation is their advanced flammability, which in fire incidents can result in dramatic human fatalities and irreversible environmental damage. Herein, epoxy-based composites with improved flame-resistant characteristics have been prepared by incorporating two flame retardant additives into epoxy resin, namely 6-(hydroxy(phenyl)methyl)-6H-dibenzo[c,e][1,2]oxaphosphinine-6-oxide (PFR) and boric acid (H3BO3). The additional reaction of 9,10-dihydro-oxa-10-phosphophenanthrene-10-oxide (DOPO) to the carbonyl group of benzaldehyde yielded PFR, which was then used to prepare epoxy composites having a phosphorus content ranging from 1.5 to 4 wt%, while the boron content was 2 wt%. The structure, morphology, thermal stability and flammability of resulted epoxy composites were investigated by FTIR spectroscopy, scanning electron microscopy (SEM), thermogravimetric analysis, differential scanning calorimetry, and microscale combustion calorimetry (MCC). Thermogravimetric analysis indicated that the simultaneous incorporation of PFR and H3BO3 improved the thermal stability of the char residue at high temperatures. The surface morphology of the char residues, studied by SEM measurements, showed improved characteristics in the case of the samples containing both phosphorus and boron atoms. The MCC tests revealed a significant reduction in flammability as well as a significant decrease in heat release capacity for samples containing both PFR and H3BO3 compared to the neat epoxy thermoset.
RESUMO
In this study, the flame retardant effect of the Zn salt of 10-hydroxy-9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (Zn-DOPOx), melamine polyphosphate (MPP) and their mixture was investigated towards the mode of action in glass fiber-reinforced polyamide 66 (PA 66 GF). The flammability was evaluated using UL 94 V and cone calorimetry. Influence on char formation was analyzed by SEM. Thermal decomposition of Zn-DOPOx and MPP was studied by TGA and ATR-FTIR. The release of gaseous PA 66 decomposition products was investigated using TGA-DTA-FTIR. Combining Zn-DOPOx and MPP leads to an improvement in flame retardancy, most pronounced for equal parts of weight. Mode of action changes significantly for Zn-DOPOx:MPP (1:1) compared to the sole components and a strong interaction between Zn-DOPOx and MPP is revealed, resulting in a more open char structure. Fuel dilution as well as less exothermic decomposition are essential for the mode of action of the combination. Through low HRR values and high CO/CO2 ratio during cone calorimetry measurements, a significant increase in gas phase activity was proven. Therefore, it is concluded that Zn-DOPOx:MPP (1:1) leads to a significant increase in flame retardancy through a combination of mode of actions in the gas and condensed phase resulting from the change in thermal stability.
RESUMO
From a set of around 100 phosphorus-containing polymers tested in pyrolysis-combustion flow calorimetry, the contributions to flammability of two phosphorus-containing pendant groups (called 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) and PO3) were calculated using an advanced method previously proposed and validated. The flammability properties include total heat release (THR) and heat release capacity (HRC) measured in standard conditions, i.e., anaerobic pyrolysis and complete combustion. The calculated contributions are in good agreement with the main modes of action of both phosphorus groups, i.e., flame inhibition for DOPO and char promotion for PO3. Moreover, the results provide first conclusions about the cooperative interaction between phosphorus and nitrogen, as well as the influence of the architecture of tested co-polymers.