RESUMO
The atomic arrangement of the terminating facets on spinel Co3 O4 nanocrystals is strongly linked to their catalytic performance. However, the spinel crystal structure offers multiple possible surface terminations depending on the synthesis. Thus, understanding the terminating surface atomic structure is essential in developing high-performance Co3 O4 nanocrystals. In this work, we present direct atomic-scale observation of the surface terminations of Co3 O4 nanoparticles supported on hollow carbon spheres (HCSs) using exit wavefunction reconstruction from aberration-corrected transmission electron microscopy focal-series. The restored high-resolution phases show distinct resolved oxygen and cobalt atomic columns. The data show that the structure of {100}, {110}, and {111} facets of spinel Co3 O4 exhibit characteristic active sites for carbon monoxide (CO) adsorption, in agreement with density functional theory calculations. Of these facets, the {100} and {110} surface terminations are better suited for CO adsorption than the {111}. However, the presence of oxygen on the {111} surface termination indicates this facet also plays an essential role in CO adsorption. Our results demonstrate direct evidence of the surface termination atomic structure beyond the assumed stoichiometry of the surface.
RESUMO
The Co3O4 nanoparticle-modified indium tin oxide-coated glass slide (ITO) electrodes are successfully prepared using dicarboxylic acid as the self-assembled monolayer through a surface esterification reaction. The ITO-SAM-Co3O4 (SAM = dicarboxylic acid) are active to electrochemically catalyze oxygen evolution reaction (OER) in acid. The most active assembly, with Co loading at 3.31 × 10-8 mol cm-2, exhibits 374 mV onset overpotential and 497 mV overpotential to reach 1 mA cm-2 OER current in 0.1 M HClO4. The electron transfer rate constant (k) is acquired using Laviron's approach, and the results show that k is not affected by the carbon chain lengths of the SAM (up to 18 -CH2 groups) and that an increase in the average diameter of Co3O4 nanoparticles enhances the k. In addition, shorter carbon chains and smaller Co3O4 nanoparticles can increase the turn-over frequency (TOF) of Co sites toward OER. The Co3O4 nanoparticles tethered to the ITO surface show both a higher number of electrochemically active Co sites and a higher TOF of OER than the Co3O4 nanoparticles bound to ITO using Nafion.
RESUMO
The present work addresses the influence of the support on the catalytic behavior of Co3O4-based catalysts in the combustion of lean methane present in the exhaust gases from natural gas vehicular engines. Three different supports were selected, namely γ-alumina, magnesia and ceria and the corresponding catalysts were loaded with a nominal cobalt content of 30 wt. %. The samples were characterized by N2 physisorption, wavelength dispersive X-ray fluorescence (WDXRF), X-ray diffraction (XRD), Raman spectroscopy, X-ray photoelectron spectroscopy (XPS) and temperature-programmed reduction with hydrogen and methane. The performance was negatively influenced by a strong cobalt-support interaction, which in turn reduced the amount of active cobalt species as Co3O4. Hence, when alumina or magnesia supports were employed, the formation of CoAl2O4 or Co-Mg mixed oxides, respectively, with a low reducibility was evident, while ceria showed a lower affinity for deposited cobalt and this remained essentially as Co3O4. Furthermore, the observed partial insertion of Ce into the Co3O4 lattice played a beneficial role in promoting the oxygen mobility at low temperatures and consequently the catalytic activity. This catalyst also exhibited a good thermal stability while the presence of water vapor in the feedstream induced a partial inhibition, which was found to be completely reversible.