Microscale Electrochemical Corrosion of Uranium Oxide Particles.

Understanding the corrosion of spent nuclear fuel is important for the development of long-term storage solutions. However, the risk of radiation contamination presents challenges for experimental analysis. Adapted from the system for analysis at the liquid-vacuum interface (SALVI), we developed a miniaturized uranium oxide (UO2)-attached working electrode (WE) to reduce contamination risk. To protect UO2 particles in a miniatured electrochemical cell, a thin layer of Nafion was formed on the surface. Atomic force microscopy (AFM) shows a dense layer of UO2 particles and indicates their participation in electrochemical reactions. Particles remain intact on the electrode surface with slight redistribution. X-ray photoelectron spectroscopy (XPS) reveals a difference in the distribution of U(IV), U(V), and U(VI) between pristine and corroded UO2 electrodes. The presence of U(V)/U(VI) on the corroded electrode surface demonstrates that electrochemically driven UO2 oxidation can be studied using these cells. Our observations of U(V) in the micro-electrode due to the selective semi-permeability of Nafion suggest that interfacial water plays a key role, potentially simulating a water-lean scenario in fuel storage conditions. This novel approach offers analytical reproducibility, design flexibility, a small footprint, and a low irradiation dose, while separating the α-effect. This approach provides a valuable microscale electrochemical platform for spent fuel corrosion studies with minimal radiological materials and the potential for diverse configurations.

Studying Corrosion Using Miniaturized Particle Attached Working Electrodes and the Nafion Membrane.

We developed a new approach to attach particles onto a conductive layer as a working electrode (WE) in a microfluidic electrochemical cell with three electrodes. Nafion, an efficient proton transfer molecule, is used to form a thin protection layer to secure particle electrodes. Spin coating is used to develop a thin and even layer of Nafion membrane. The effects of Nafion (5 wt% 20 wt%) and spinning rates were evaluated using multiple sets of replicates. The electrochemical performance of various devices was demonstrated. Additionally, the electrochemical performance of the devices is used to select and optimize fabrication conditions. The results show that a higher spinning rate and a lower Nafion concentration (5 wt%) induce a better performance, using cerium oxide (CeO2) particles as a testing model. The WE surfaces were characterized using atomic force microscopy (AFM), scanning electron microscopy-focused ion beam (SEM-FIB), time-of-flight secondary ion mass spectrometry (ToF-SIMS), and X-ray photoelectron spectroscopy (XPS). The comparison between the pristine and corroded WE surfaces shows that Nafion is redistributed after potential is applied. Our results verify that Nafion membrane offers a reliable means to secure particles onto electrodes. Furthermore, the electrochemical performance is reliable and reproducible. Thus, this approach provides a new way to study more complex and challenging particles, such as uranium oxide, in the future.