Preparation and Performances of Warp-Knitted Hernia Repair Mesh Fabricated with Chitosan Fiber.

In this paper, warp-knitted knitted fabrics with chitosan fibers for ventral hernia repair were fabricated with three kinds of structures. The properties of chitosan fiber, yarns, and fabrics were tested. The results demonstrated that the properties of a mesh fabricated with 1-0/1-2/2-3/2-1// structure were slightly better than those of other fabrics. The mechanical properties of the three produced fabrics were weak. However, the results demonstrated that chitosan meshes have many advantages, such as excellent hygroscopicity, and thermal and antimicrobial properties, which makes them one of the best materials for ventral hernia repair. The findings have theoretical and practical significance for the industrial uses of chitosan in ventral hernia repair.

Experimental Study on Bi-Axial Mechanical Properties of Warp-knitted Meshes with and without Initial Notches.

Warp-knitted meshes have been widely used for structural reinforcement of rigid, semi-rigid, and flexible composite materials. In order to meet the performance requirements of different engineering applications, four typical warp-knitted meshes (rectangular, square, circular, and diamond) were designed and developed. The mechanical behaviors of these meshes under mono-axial and multi-axial tensile loads were compared. The influence of the initial notch length and orientation on the mechanical performance was also analyzed. The results showed that the biaxial tensile behavior of warp-knitted meshes tended to be more isotropic. The anisotropy level of the diamond warp-knitted mesh was the lowest (λ = 0.099), while the rectangular one was the highest (λ = 0.502). The notch on a significantly anisotropic mesh was propagated along the direction of larger modulus, while for a not remarkably anisotropic mesh, notch propagation was probably consistent with the initial notch orientation. The breaking strength of warp-knitted meshes with the same initial notch orientation decreased with the increase in notch length in both the wale and course directions. For warp-knitted meshes with the same initial notch length, the breaking strength in the wale direction was kept stable at different notch orientations, while that in the course direction decreased remarkably with notch orientation from 0° to 90°.