Influence of Er:YAG laser irradiation distance on the bond strength of a restorative system to enamel.
J Dent
; 34(3): 245-51, 2006 Mar.
Article
em En
| MEDLINE
| ID: mdl-16153764
ABSTRACT
OBJECTIVES:
The aim of the present study was to investigate in vitro the effect of ErYAG laser on bonding to enamel, varying the irradiation distance.METHOD:
Tensile bond strength of an adhesive restorative system to non-irradiated and irradiated enamel surfaces was evaluated. Thirty caries-free human third molars were sectioned in mesio-distal direction and embedded in acrylic resin. Enamel was flattened, and a 3-mm-diameter bonding area was demarcated. Specimens were randomly assigned into six groups groups I-V were treated with the ErYAG laser (80 mJ/2 Hz), varying the irradiation distance (11, 12 mm-focused, 14, 16 and 17 mm, respectively), followed by 35% phosphoric acid etching. Control group (VI) received treatment with phosphoric acid alone. Single Bond adhesive system was applied on the conditioned enamel, and composite resin cones, bonded to enamel, were fabricated with Z250. After storage, samples were tested in tensile to failure (50 kgf and 0.5 mm/min).RESULTS:
Means in MPa were I-9.67 (+/-3.44); II-13.29 (+/-2.65); III-13.33 (+/-2.22); IV-14.87 (+/-3.58); V-16.43 (+/-4.52); VI-22.90 (+/-3.03). ANOVA and Tukey test revealed statistically significant decrease of bond strength in group I (P < 0.05). Groups II-IV presented similar results, as did groups IV and V. Control group (VI) yielded the best overall performance (P < 0.05).CONCLUSION:
ErYAG laser irradiation adversely affected adhesion to enamel. However, bond strength was influenced by the irradiation distance, thus being stronger with the increase of distance to the target tissue.
Buscar no Google
Coleções:
01-internacional
Base de dados:
MEDLINE
Assunto principal:
Colagem Dentária
/
Adesivos Dentinários
/
Esmalte Dentário
/
Lasers
Tipo de estudo:
Clinical_trials
Limite:
Humans
Idioma:
En
Ano de publicação:
2006
Tipo de documento:
Article