CsPbBr3:xEu3+ perovskite QD borosilicate glass: a new member of the luminescent material family.
Yuan, Rongrong; Shen, Lingli; Shen, Chenyang; Liu, Jianming; Zhou, Lei; Xiang, Weidong; Liang, Xiaojuan.
Afiliação
  • Yuan R; College of Chemistry and Materials Engineering, Wenzhou University, Wenzhou 325035, People's Republic of China. xiangweidong001@126.com.
  • Shen L; College of Chemistry and Materials Engineering, Wenzhou University, Wenzhou 325035, People's Republic of China. xiangweidong001@126.com.
  • Shen C; College of Chemistry and Materials Engineering, Wenzhou University, Wenzhou 325035, People's Republic of China. xiangweidong001@126.com.
  • Liu J; College of Chemistry and Materials Engineering, Wenzhou University, Wenzhou 325035, People's Republic of China. xiangweidong001@126.com.
  • Zhou L; College of Chemistry and Materials Engineering, Wenzhou University, Wenzhou 325035, People's Republic of China. xiangweidong001@126.com.
  • Xiang W; College of Chemistry and Materials Engineering, Wenzhou University, Wenzhou 325035, People's Republic of China. xiangweidong001@126.com.
  • Liang X; College of Chemistry and Materials Engineering, Wenzhou University, Wenzhou 325035, People's Republic of China. xiangweidong001@126.com.
Chem Commun (Camb) ; 54(27): 3395-3398, 2018 Mar 29.
Article em En | MEDLINE | ID: mdl-29553148
ABSTRACT
Eu3+ ions were introduced into the lattices of CsPbBr3 perovskite QDs and a tunable multicolour emission from CsPbBr3xEu3+ perovskite QD glass was successfully obtained. Multicolour LEDs that were fabricated by combining the as-prepared CsPbBr3xEu3+ QD glasses with a UV chip were also researched in this study.
Texto completo
Imprimir
XML
PubMed Links
Buscar no Google

Texto completo: 1 Coleções: 01-internacional Base de dados: MEDLINE Idioma: En Ano de publicação: 2018 Tipo de documento: Article
Texto completo
Imprimir
XML
PubMed Links
Buscar no Google

Texto completo: 1 Coleções: 01-internacional Base de dados: MEDLINE Idioma: En Ano de publicação: 2018 Tipo de documento: Article