Comparative Evaluation of Flexural Strength of Nano-zirconia-integrated Pressable Feldspathic and Lithium Disilicate Ceramics.
J Contemp Dent Pract
; 19(3): 339-344, 2018 Mar 01.
Article
em En
| MEDLINE
| ID: mdl-29603709
AIM: The purpose of the study was to evaluate and compare the flexural strength of nano-reinforced zirconia feldspathic porcelain, lithium disilicate ceramics, and zirconia. MATERIALS AND METHODS: Ten bar-shaped specimens of computer-aided design (CAD)/computer-aided manufacturing (CAM) zirconia, reinforced feldspathic porcelain, and reinforced lithium disilicate were fabricated in accordance to International Organization for Standardization (ISO 6872; n = 10). Feldspathic porcelain and lithium disilicate ceramic specimens were reinforced with 5, 10, 15, and 20% of zirconia nanoparticles through a customized technique. The specimens were subjected to three-point flexural strength test using universal testing machine (UTM) and examined for crack propagation using a scanning electron microscope (SEM). Oneway analysis of variance (ANOVA) and Tukey test were used to analyze the data (p < 0.05). RESULTS: The flexural strength of feldsphatic porcelain increased with the increase in the concentration of zirconia particles. The mean flexural strength of 5, 10, 15, and 20% nano-zirconia-incorporated lithium disilicate was 93.8, 97.1, 100.6, and 100.8 MPa respectively, and was lower than the control group (221.7 MPa). A significant difference in the flexural strength was found with the incorporation of nano-zirconia particles. CONCLUSION: The flexural strength of zirconia-integrated feld-spathic porcelain increased and lithium disilicate ceramics decreased with the nano-zirconia reinforcement. CLINICAL SIGNIFICANCE: The simplified approach of reinforcing feldspathic porcelain with zirconia nanoparticles can be adapted in clinical situations of higher masticatory forces.
Palavras-chave
Buscar no Google
Coleções:
01-internacional
Base de dados:
MEDLINE
Assunto principal:
Zircônio
/
Porcelana Dentária
/
Nanoestruturas
Idioma:
En
Ano de publicação:
2018
Tipo de documento:
Article