Synthesis of 3D flower-like Fe3S4 microspheres and quasi-sphere Fe3S4-RGO hybrid-architectures with enhanced electromagnetic wave absorption.

ABSTRACT

3D flower-like Fe3S4 microspheres and quasi-sphere Fe3S4-RGO hybrid-architectures were successfully fabricated by a facile template-free hydrothermal method. The results of morphology revealed that the single Fe3S4 was composed of many nanoflakes and the Fe3S4-RGO composites mainly distributed together into a ball up and down the RGO sheet. The electromagnetic parameters of the single Fe3S4 and Fe3S4-RGO composites could be controlled by adjusting different filler loading and the addition of different GO to achieve impedance matching. Both the single Fe3S4 and Fe3S4-RGO composites exhibited an excellent EM absorption ability. The minimum reflection loss (RL) of the single Fe3S4 with 50% filler loading could achieve -66.87 dB at 10.57 GHz for the thickness of 2.2 mm, and the absorption bandwidth (RL < -10 dB) could reach 3.49 GHz. For the Fe3S4-RGO composites, the minimum RL of FSR-1 could be -40.25 dB at 9.67 GHz with the thickness of 2.0 mm. In addition, the effective absorption bandwidth of FSR-2 could reach 3.85 GHz at only 1.45 mm and the minimum RL was -29.25 dB at 14.24 GHz. Consequently, the single Fe3S4 and Fe3S4-RGO composites are promising materials as a high performance and adjustable EM wave absorber.