Na Storage Activity or Inertness of P-Configurations in N, P Dual-Doped Carbon Nanofibers: Bulk vs Surface.
ACS Appl Mater Interfaces
; 14(51): 56836-56846, 2022 Dec 28.
Article
em En
| MEDLINE
| ID: mdl-36511695
ABSTRACT
Heteroatom doping is an effective method to improve the electrochemical properties of hard carbon anodes for sodium-ion batteries. However, the different roles of surface and bulk heteroatoms in Na storage have not been explored much. Herein, N, P dual-doped carbon nanofibers (NP-CNFs) with high doping contents and low surface area are designed to clarify the above issue. It is confirmed that P plays a more crucial role in Na storage compared with N. In addition, surface and bulk P not only possess different configurations but also show distinct Na storage activity. There are only oxidized POx groups on the surface, which are inactive for Na storage but promote the stability of electrochemistry interphase, while in the bulk phase, unoxidized P-C bonds also emerge except POx, which shows preeminently reversible Na storage activity, and the POx groups are activated simultaneously. Furthermore, P-doping changes the reactivity of N-configurations with Na both on the surface and in the bulk phase, exhibiting interesting synergism. As expected, the surface stability, bulk activity, and synergism enable NP-CNFs to achieve superior performance. It could deliver a prominent capacity of 105.6 mAh g-1 at 10 A g-1 after 3000 cycles in half cells and 164.3 mAh g-1 at 1 A g-1 after 200 cycles in full cells.
Texto completo:
1
Coleções:
01-internacional
Base de dados:
MEDLINE
Idioma:
En
Ano de publicação:
2022
Tipo de documento:
Article