The structure of molten calcium ferrite under various redox conditions.
Philos Trans A Math Phys Eng Sci
; 381(2258): 20220352, 2023 Oct 16.
Article
em En
| MEDLINE
| ID: mdl-37634540
ABSTRACT
Laser-heated melts based on the 43CaO-57Fe2O3-x eutectic, close to the calcium ferrite (CF) composition, were measured with high-energy X-ray diffraction using aerodynamic levitation over a range of redox states controlled by CO/CO2 gas atmospheres. The iron-oxygen coordination number was found to rise from 4.4 ± 0.3 at 15% Fe3+ to 5.3 ± 0.3 at 87% Fe3+. Empirical potential structure refinement modelling was used to obtain the ferric and ferrous partial pair distribution functions. It was found that the Fe2+ iron-oxygen coordination number is consistently approximately 10% higher in CF than in pure iron oxide, while Fe3+ is essentially identical in all but the most oxygen-rich environments (where it is higher in CF compared with FeOx). The model also shows calcium octahedra to be the dominant species across all redox environments, although the population of CaO7 increases with the availability of oxygen at the expense of CaO4 and CaO5. This article is part of the theme issue 'Exploring the length scales, timescales and chemistry of challenging materials (Part 1)'.
Texto completo:
1
Coleções:
01-internacional
Base de dados:
MEDLINE
Idioma:
En
Ano de publicação:
2023
Tipo de documento:
Article