Filler Mixed Into Adhesives Does Not Necessarily Improve Their Mechanical Properties.
Oper Dent
; 49(3): 311-324, 2024 05 01.
Article
em En
| MEDLINE
| ID: mdl-38632849
ABSTRACT
OBJECTIVES:
To investigate the influence of filler type/loading on the micro-tensile fracture strength (µTFS) of adhesive resins, as measured 'immediately' upon preparation and after 1-week water storage ('water-stored').METHODS:
The morphology and particle-size distribution of three filler particles, referred to as 'Glass-S' (Esschem Europe), 'BioUnion' (GC), and 'CPC_Mont', were correlatively characterized by SEM, TEM, and particle-size analysis. These filler particles were incorporated into an unfilled adhesive resin ('BZF-29unfilled', GC) in different concentrations to measure the 'immediate' µTFS. After 1-week water storage, the 'water-stored' µTFS of the experimental particle-filled adhesive resins with the most optimum filler loading, specific for each filler type, was measured. In addition, the immediate and water-stored µTFS of the adhesive resins of three experimental two-step universal adhesives based on the same resin matrix but varying for filler type/loading, coded as 'BZF-21' (containing silica and bioglass), 'BZF-29' (containing solely silica), and 'BZF-29_hv' (highly viscous with a higher silica loading than BZF-29), and of the adhesive resins of the gold-standard adhesives OptiBond FL ('Opti-FL', Kerr) and Clearfil SE Bond 2 ('C-SE2', Kuraray Noritake) was measured along with that of BZF-29unfilled (GC) serving as control/reference. Statistics involved one-way and two-way ANOVA followed by post-hoc multiple comparisons (α<0.05).RESULTS:
Glass-S, BioUnion, and CPC_Mont represent irregular fillers with an average particle size of 8.5-9.9 µm. Adding filler to BZF-29unfilled decreased µTFS regardless of filler type/loading. One-week water storage reduced µTFS of all adhesive resins except BZF-21, with the largest reduction in µTFS recorded for BZF-29unfilled. Among the three filler types, the µTFS of the 30 wt% Glass-S and 20 wt% BioUnion filled adhesive resin was not significantly different from the µTFS of BZF-29unfilled upon water storage.CONCLUSIONS:
Adding filler particles into adhesive resin did not enhance its micro-tensile fracture strength but appeared to render it less sensitive to water storage as compared to the unfilled adhesive resin investigated.
Texto completo:
1
Coleções:
01-internacional
Base de dados:
MEDLINE
Assunto principal:
Resistência à Tração
/
Teste de Materiais
Limite:
Humans
Idioma:
En
Ano de publicação:
2024
Tipo de documento:
Article