RESUMO
Objective: The aim of the study was to fabricate and morphologically characterize ultrafine Polyetherimide fibers (PEI) associated with Polymethylmethacrylate (PMMA) PP (group formed by the association of PEI with PMMA), produced by the electrospinning process. Material and Methods: A solution of PEI (0.562 g) + PMMA (0.377 g) dissolved in 2.5 mL of chloroform, 0.85 mL of Dimethylformamide (DMF) and 0.85 mL of 1.1.2.2 Tetrachloroethane (TCE) was prepared. For the electrospinning process, different continuous voltages (10 to 18 kV) and two different distances (8 and 12 cm) between the needle tip and the collecting apparatus were used, giving rise to 6 distinct groups of ultrafine fibers (PP 1 to 6) that were observed in Scanning Electron Microscopy to check for defects and calculate the average diameter of the fibers. Results: The best parameter, the parameter that was most effective for the production of fibers, observed was subjected to Energy Dispersion X-ray Spectroscopy (EDS), X-ray Diffraction (XRD) and Contact Angle Analysis tests. The data were analyzed using the ANOVA and Tukey test (p <0.05). From the comparative analysis of the pre-established parameters, the pattern of PP4 ultrafine fibers was shown to be more effective. Conclusion: The PP4 standard (13 kV 12 cm) had an average diameter of 0.37 µm. An adequate parameter to electrospinning was able to produce ultrafine fibers of PMMA/PEI (AU)
Introdução: O objetivo do estudo foi sintetizar e caracterizar morfologicamente fibras ultrafinas de Polieterimida (PEI) associadas ao Polimetilmetacrilato (PMMA) - PP (grupo formado pela associação de PEI com PMMA), produzidas pelo processo de eletrofiação. Material e Métodos: Foi preparada uma solução de PEI (0,562 g) + PMMA (0,377 g) dissolvido em 2,5 mL de clorofórmio, 0,85 mL de Dimetilformamida (DMF) e 0,85 mL de 1.1.2.2 Tetracloroetano (TCE). Para o processo de eletrofiação, foram utilizadas diferentes tensões contínuas (10 a 18 kV) e duas distâncias diferentes (8 e 12 cm) entre a ponta da agulha e o aparelho coletor, dando origem a 6 grupos distintos de fibras ultrafinas (PP 1 a 6) que foram observados em Microscopia Eletrônica de Varredura para verificar defeitos e calcular o diâmetro médio das fibras. Resultados: O melhor parâmetro, o parâmetro mais eficaz para a produção de fibras, observado foi submetido aos testes de Espectroscopia de Dispersão de Energia (EDS), Difração de Raios X (DRX) e Análise do Ângulo de Contato. Os dados foram analisados pela ANOVA e teste de Tukey (p <0,05). A partir da análise comparativa dos parâmetros pré-estabelecidos, o padrão das fibras ultrafinas PP4 mostrou-se mais eficaz. Conclusão: O padrão PP4 (13 kV - 12 cm) apresentou diâmetro médio de 0,37 µm. Um parâmetro adequado para eletrofiação foi capaz de produzir fibras ultrafinas de PMMA / PEI. (AU)
Assuntos
Microscopia Eletrônica de Varredura , Polimetil Metacrilato , Espectroscopia de Perda de Energia de ElétronsRESUMO
Portland cement has been analyzed and compared to mineral trioxide aggregate (MTA) because of their chemical similarity. The possibility of using this material as a less expensive alternative to MTA in dental practice should be considered. In view of this, the present study compared the components of a Portland cement (Votoran®) to two commercial brands of MTA (Pro-Root and MTA-Angelus®). Twelve specimens of each material were fabricated and examined by scanning electron microscopy (SEM) with energy dispersive spectroscopy (EDS) to obtain their percentage of chemical elements. The means of the chemical elements found in each material was compared by descriptive statistics. Bismuth was present only in MTA cements to provide radiopacity. In conclusion, the tested cements have similar components, which supports, as far as composition is concerned, the possible clinical use of Portland as an option to MTA.
O cimento Portland tem sido analisado e comparado com o agregado trióxido mineral (MTA) devido a sua similaridade química. Dada à possibilidade de uso na Odontologia como uma alternativa menos onerosa ao MTA, realizou-se uma análise comparativa dos componentes do cimento Portland (Votoran®) com os constituintes de dois cimentos MTA (Pro-Root-MTA e Angelus®-MTA). Para tanto, foram confeccionados 12 corpos-de-prova de cada um dos materiais (n=36), e estes foram analisados em microscopia eletrônica de varredura (MEV) pela técnica de espectroscopia por dispersão de energia (EDS), que fornece o percentual dos componentes químicos encontrados nos corpos-de-prova. As médias dos elementos químicos encontrados nos três cimentos foram comparadas por meio de análise estatística descritiva. O bismuto estava presente somente nos cimentos MTA. Concluiu-se que os cimentos testados apresentaram similaridade em seus constituintes, o que indica, considerando-se a composição, a possibilidade de futura utilização clínica do cimento Portland como alternativa ao MTA.