Thermal expansion and corrosion resistance of cobalt-chromium alloys fabricated by contemporary manufacturing processes: an in vitro study / Expansión térmica y resistencia a la corrosión de aleaciones de cobalto-cromo fabricadas mediante procesos de abricación contemporáneos: un estudio in vitro

In Purpose: The fabrication technique can influence the mechanical properties of Cobalt-Chromium (Co-Cr) dental alloys. Hence, the present study aims to determine the corrosion resistance and thermal expansion of alloys manufactured using three contemporary techniques. Material and Methods: A total of nine specimens of Co-Cr alloy were prepared according to ISO 22674 by each one of the three manufacturing processes (three in each process); conventional casting, direct metal laser sintering (DMLS) and milling (MIL). All these specimens were tested for coefficient of thermal expansion and corrosion resistance. The data was tabulated and analyzed statistically. Results: The difference in the thermal expansion of alloys fabricated using three techniques was non-significant at almost all the temperatures from 50 ºC to 950 ºC (p>0.05), except 450 ºC and 600 °C. The polarization resistance of specimens manufactured using the conventional method was more compared to DMLS and MIL at pH 5 (Conventional>MIL>DMLS) (p<0.001). Conclusion: The thermal expansion behavior of alloys manufactured using the three selected techniques were similar, whereas, at acidic pH, the corrosion resistance of conventional and MIL were better than the DMLS.

Antecedentes: La técnica de fabricación puede influir en las propiedades mecánicas de las aleaciones dentales de cobalto-cromo (Co-Cr). Por lo tanto, el presente estudio tiene como objetivo determinar la resistencia a la corrosión y la expansión térmica de aleaciones fabricadas con tres técnicas contemporáneas. Material y Métodos: Se prepararon un total de nueve probetas de aleación de Co-Cr según ISO 22674 por cada uno de los tres procesos de fabricación (tres en cada proceso); fundición convencional, sinterización directa de metal por láser (DMLS) y fresado (MIL). Todos estos especímenes fueron probados para determinar el coeficiente de expansión térmica y la resistencia a la corrosión. Los datos fueron tabulados y analizados estadísticamente. Resultados: La diferencia en la dilatación térmica de las aleaciones fabricadas con las tres técnicas no fue significativa en casi todas las temperaturas desde 50ºC hasta 950ºC (p>0,05), excepto 450ºC y 600ºC. La resistencia a la polarización de las muestras fabricadas con el método convencional fue mayor en comparación con DMLS y MIL a pH 5 (Convencional>MIL>DMLS) (p<0, 0 01). Conclusión: El comportamiento de expansión térmica de las aleaciones fabricadas con las tres técnicas seleccionadas fue similar, mientras que, a pH ácido, la resistencia a la corrosión de la convencional y la MIL fue mejor que la de la DMLS.

Influência do hipoclorito de sódio na resistência à fadiga cíclica em instrumentos rotatórios endodônticos de memória controlada de NiTi: uma avaliação experimental / Influence of sodium hypochlorite on cyclic fatigue resistance in niti controlled memory endodontics rotary instruments: an experimental evaluation

Introdução: É importante saber se o hipoclorito de sódio (NaOCl) influencia a resistência à fadiga cíclica das limas de níquel-titânio (NiTi). Objetivo: Avaliar a influência de NaOCl 2,5% na resistência à fadiga cíclica de dois sistemas de NiTi. Material e método: 40 instrumentos rotatórios - 20 TruNatomy® (TRU, Dentsply Sirona, Maillefer, Ballaigues, Suíça) e 20 Prodesing Logic2® (PDL2, Bassi, Belo Horizonte, Minas Gerais, Brasil) - foram aleatoriamente distribuídos em 4 grupos experimentais (n = 10) imersos em água destilada (H2O) e NaOCl 2,5% em temperatura a 37°C. Foram submetidos a testes de fadiga cíclica mensurando o número de ciclos para fratura (NCF) e análise dessas superfícies pós-teste em microscópio eletrônico por varredura. Para a análise estatística entre os grupos, foi aplicada a análise de variância (ANOVA), complementada com o pós-teste de Tukey. Resultado: Houve diferença estatística em todos os grupos (P<0.05). Os instrumentos PDL2 obtiveram maior resistência à fratura nas condições em H2O e em NaOCl 2,5% comparados aos instrumentos TRU. Na análise de grupos de instrumentos nas soluções de NaOCl e H2O, foi observado que o NaOCl 2,5% diminuiu o NCF. Conclusão: A resistência à fadiga cíclica dos instrumentos TRU e PDL2 diminuiu com NaOCl 2,5%. Os instrumentos PDL2 foram mais resistentes à fratura em relação aos instrumentos TRU.

Introduction: It is important to know whether sodium hypochlorite (NaOCl) influences the cyclic fatigue resistance of nickel-titanium (NiTi) files. Objective: To evaluate the influence of NaOCl 2.5% on the cyclic fatigue resistance of two NiTi systems. Material and method: Forty rotary instruments - 20 TruNatomy® (TRU, Dentsply Sirona, Maillefer, Ballaigues, Switzerland) and 20 Prodesign Logic2® (PDL2, Bassi, Belo Horizonte, Minas Gerais, Brazil) - were distributed randomly across four experimental groups (n=10) and submerged in distilled water (H2O) or 2.5% NaOCl at 37°C according to allocation. Cyclic fatigue testing was then performed, measuring the number of cycles to fracture (NCF), and post-test surfaces were analysed by scanning electron microscopy (SEM). Statistical Analysis: Analysis of variance (ANOVA) was applied for between-group analysis, followed by Tukey's post-hoc test. Result: A significant difference was observed in all groups (P<0.05). PDL2 instruments showed higher fracture resistance under H2O and 2.5% NaOCl conditions compared to TRU. Analysis of all instrument groups showed that exposure to 2.5% NaOCl decreased the NCF compared to H2O. Conclusion: Cyclic fatigue resistance of the TRU and PDL2 instruments was decreased by exposure to 2.5% NaOCl. PDL2 instruments were more resistant to fracture than TRU instruments.

Análise da resistência à fadiga e resistência à corrosão em instrumentos, HyFlex EDM, HyFlex CM e RaCe / Analysis of fatigue resistance and corrosion resistance in instruments, HyFlex EDM, HyFlex CM and RaCe

O objetivo deste trabalho foi avaliar a resistência à fadiga e a resistência à corrosão em instrumentos endodônticos de NiTi dos sistemas HyFlex EDM, Hyflex CM, e RaCe, além de relacionar estes resultados às características físicas, químicas e estruturais destes instrumentos. Para tal, instrumentos 25/.~ do sistema HyFlex EDM (EDM), instrumentos 30/.06 do sistema HyFlex CM (CM) e RaCe (RC) foram utilizados. A composição química foi determinada por espectroscopia dispersiva de raios-X, as fases presentes nos materiais foram determinadas por difratometria de raios-X (DRX) e as temperaturas de transformação de fases por calorimetria exploratória diferencial (DSC). A análise da rugosidade superficial dos instrumentos foi realizada por microscopia de força atômica (AFM) e a caracterização dimensional dos instrumentos foi realizada através da mensuração do diâmetro a 3mm da ponta. Ensaios de fadiga até a ruptura foram realizados nos três grupos (n=10) e o tempo médio até a fratura determinado. Instrumentos novos foram subdivididos em grupos controle e experimental para cada sistema. Os grupos experimentais foram submetidos à ensaios de fadiga, até 3/4 do tempo médio para a ruptura e posteriormente a testes de corrosão (potencial de circuito aberto e polarização). Os grupos controle foram diretamente submetidos aos mesmos testes de corrosão. A análise de Weibull foi aplicada para avaliação da probabilidade de falha em relação ao tempo nos instrumentos testados em fadiga até a ruptura. Análise de variância com índice de significância de 0,05% foi adotada para os resultados de composição química, temperatura de transformação de fases, diâmetro, rugosidade e testes de corrosão. A composição química foi praticamente equiatomica em instrumentos RaCe, com presença de Níquel e Titânio. Já instrumentos EDM e CM apresentaram, além destes elementos, Oxigênio na composição. A caracterização estrutural evidenciou maiores temperaturas de transformação de fase Af (austenite finish) para os grupos tratados termicamente (CM e EDM), este dado foi comprovado pelos resultados da difratometria de raios-X com a presença de fase-R e austenita (fase ß) à temperatura ambiente para ambos. O grupo RC, apresentou menores temperaturas Af (p<.05), além de apenas austenita na análise por DRX. As medidas de diâmetro apresentaram-se sem diferenças estatisticamente significativas entre os grupos CM e RC, ambos significativamente maiores que EDM. Os testes de fadiga flexural apresentaram tempo até a fratura sem diferença entre EDM e CM (p>0,05) e ambos foram superiores em relação à RC (p<0.05). Por outro lado, a análise de Weibull apresentou melhores parâmetros de confiabilidade para RC e CM. Os ensaios de corrosão apresentaram diferenças significativas entre os sistemas analisados, mas não entre instrumentos novos e ciclados. Os grupos CM apresentaram maior resistência à corrosão, seguido de EDM e RC. A rugosidade superficial foi maior em instrumentos CM, seguidos de EDM e RC. De acordo com os resultados a microestrutura dos instrumentos tratados termicamente melhora a resistência à fadiga e resistência à corrosão, independentemente do tipo de usinagem.

The aim of this study was to assess the fatigue and corrosion resistance of NiTi endodontic instruments. HyFlex EDM 25 /. ~, HyFlex CM 30/.06 and RaCe 30/.06 were used. Chemical composition was determined by energy-dispersive X-ray spectroscopy, phase constitution by X-ray diffraction and transformation temperatures by differential scanning calorimetry. Surface roughness was analyzed by atomic microscopic force (AFM) and the geometric characterization of the instruments was performed by measuring the diameter at 3mm from the tip. Initially, 10 instruments from each group were tested until rupture in the flexural fatigue bench to obtain the mean time until fracture. Then, new instruments were subdivided into control and experimental groups for each system. Experimental groups were subjected to fatigue tests, up to 3/4 of the mean time to rupture and subsequently to corrosion tests. Control groups were directly subjected to the same corrosion tests. Weibull analysis was applied to assess the reliability in the tested instruments to failure. Analysis of variance with a significance of 0.05% was adopted for the results of chemical composition, phase transformation temperature, diameter, roughness, and corrosion tests. The chemical composition was near equiatomic in RaCe instruments, with the presence of Nickel and Titanium. On the other hand, EDM and CM instruments presented, in addition to these elements, Oxygen in the composition. The structural characterization showed higher Af phase transformation temperatures (austenite finish) for the heat-treated groups (CM and EDM), this data was confirmed by the results of X-ray diffractometry with the presence of R-phase and austenite (phase ß) at room temperature for both. The RC group had lower temperatures Af (p<.05), in addition to only austenite in the XRD analysis. Diameter measurements showed no statistically significant differences between the CM and RC groups, both significantly larger than EDM. Flexural fatigue tests showed time to fracture with no difference between EDM and CM (p>0.05) and both were superior to RC (p<0.05). However, the Weibull analysis showed better reliability parameters for RC and CM. The corrosion tests showed significant differences between the analyzed systems, but not between new and cycled instruments. The CM groups showed greater resistance to corrosion, followed by EDM and RC. Surface roughness was higher in CM instruments, followed by EDM and RC. According to the results, the microstructure of the thermally treated instruments improves fatigue resistance and corrosion resistance, regardless of the type of machining.

In vitro comparison of peracetic acid and autoclave sterilization in the corrosion of orthodontic pliers: a pilot study

ABSTRACT Introduction: The most currently recommended method for sterilization of orthodontic pliers is the autoclave, while peracetic acid has also been shown to be effective in the chemical sterilization process. Objective: This study sought to compare the corrosive effects of peracetic acid and autoclave sterilization process of orthodontic pliers. Methods: Four active tungsten carbide (WC) stainless steel tie-cutting pliers from the manufacturers Quinelato (Rio Claro, SP, Brazil) and ICE (Cajamar, SP, Brazil) were selected. The active ends of the pliers were sectioned, and six active tips were obtained and distributed into the following groups: 1) control group (no sterilization); 2) AC group (two active pliers tips submitted to 100 autoclave sterilization cycles); and 3) AP group (two active pliers tips submitted to 100 cycles of sterilization by immersion in 2% peracetic acid solution for 30 minutes). Results: Chemical analysis using X-ray dispersive energy spectroscopy showed that after autoclave sterilization, only the ICE pliers presented oxidation corrosion (Δ[O] = +24.5%; Δ[Fe] = +5.8%; Δ[WC] = -1.9%). In comparison, following peracetic acid sterilization, both manufacturers ICE (Δ[O] = +1.8%; Δ[Fe] = +18.0%; Δ[WC] = -1.1%) and Quinelato (Δ[O] = +5.3%; Δ[Fe] = -10.4%; Δ[WC] = -15.2%) showed corrosion. The morphological analysis revealed that peracetic acid caused a pitting and localized corrosion in both brands, while the autoclave caused uniform surface corrosion on the ICE pliers. Conclusion: Autoclave application was the sterilization method that generated less corrosive damage to the orthodontic cutting pliers, when compared to the immersion in 2% peracetic acid.

RESUMO Introdução: O método mais recomendado para a esterilização dos alicates ortodônticos é a autoclave; porém, o ácido peracético mostrou-se eficaz no processo de esterilização química. Objetivo: O objetivo do presente estudo foi avaliar o efeito corrosivo do ácido peracético e da autoclave no processo de esterilização de alicates ortodônticos. Métodos: Foram selecionados quatro alicates de corte de amarrilho de aço inoxidável, com ponta ativa de carboneto de tungstênio (WC), das marcas Quinelato (Rio Claro/SP, Brasil) e ICE (Cajamar/SP, Brasil), que foram distribuídos em três grupos: 1) Controle (C), o qual não foi submetido à esterilização; 2) Grupo AC, constituído por duas pontas ativas de alicates submetidas a 100 ciclos de esterilização em autoclave; e 3) Grupo AP, formado por duas pontas ativas de alicates submetidas a 100 ciclos de esterilização por imersão em solução de ácido peracético a 2% durante 30 minutos. Resultados: Por meio da análise química (EDS, energia dispersiva de raios X), constatou-se que, após esterilização em autoclave, somente o alicate ICE apresentou corrosão por oxidação (Δ[O] = +24,5%; Δ[Fe] = +5,8% e Δ[WC] = -1,9%), enquanto na esterilização em ácido peracético, ambas as marcas, ICE (Δ[O] = +1,8%; Δ[Fe] = +18,0% e Δ[WC] = -1,1%) e Quinelato (Δ[O] = +5,3%; Δ[Fe] = -10,4% e Δ[WC] = -15,2%), apresentaram corrosão. A análise morfológica demonstrou que o ácido peracético causou uma corrosão localizada em pite em ambas as marcas, enquanto a autoclave ocasionou uma corrosão superficial uniforme no alicate ICE. Conclusão: A autoclave foi o método de esterilização que gerou menor dano corrosivo aos alicates ortodônticos, em comparação à imersão em ácido peracético a 2%.

Avaliação do grau de corrosão de fios ortodônticos submetidos a desafio de pH / Evaluation of the corrosion degree of orthodontic wires subjected to pH challenge

Introdução: a movimentação dentária requer a aplicação de um sistema de forças que é orientado com o uso de acessórios, incluindo fios ortodônticos. Existem diversos materiais e fabricantes disponíveis no mercado, por isso é importante que o profissional conheça a composição deste material, uma vez que estará em contato com a mucosa oral, podendo sofrer corrosão e liberação de íons metálicos. Objetivo: avaliar, in vitro, o grau de corrosão de duas ligas metálicas que compõem fios ortodônticos de três fabricantes diferentes, submetidos à ciclagem de pH. Metodologia: 60 corpos de prova foram confeccionados com dois tipos de ligas metálicas (NiTi e CrNiaço 302) produzidas por três fabricantes diferentes, divididos em 6 Grupos de Testes com 10 unidades cada. Os corpos-de-prova foram submetidos à ciclagem ácida de pH 4,3, diariamente, e mantidos em estufa a 37 ° C por 14 dias. A massa foi pesada antes e após a ciclagem, por meio de balança analítica de precisão. A avaliação das características visuais dos fios foi realizada por um único observador em lupa estereomicroscópica. Resultados: a ciclagem de pH dos fios ortodônticos não promoveu perda significativa de massa ou corrosão, apesar da análise das características visuais terem mudado após a ciclagem. Conclusão: com base nos resultados do protocolo experimental estabelecido no presente estudo, a análise do comportamento das ligas de aço NiTi e CrNi ­ 302 que compõem os fios ortodônticos, frente ao desafio ácido de pH 4,3, por duas semanas, concluiu-se que esses materiais não apresentaram perdas de massa, opacidade, brilho e lisura consideradas significativas. Outros estudos são recomendados para fornecer maiores esclarecimentos sobre o tema.

Introduction: the tooth movement requires the application of a force system that is guided with the use of accessories, including orthodontic wires. There are several materials and manufacturers available on the market, so it is important that the professional knows the composition of this material, since it will be in contact with the oral mucosa, and may suffer corrosion and release metal ions. Objective: to evaluate, in vitro, the degree of corrosion of two metal alloys that make up orthodontic wires from three different manufacturers, submitted to pH cycling. Methodology: 60 specimens were made from two types of metal alloys (NiTi and CrNi ­ steel 302) produced by three different manufacturers, divided into 6 Test Groups with 10 units each. The specimens were subjected to acid pH 4.3 cycling, daily, and kept in an oven at 37 ° C for 14 days. The mass was obtained before and after cycling, using a precision analytical balance. The evaluation of the visual characteristics of the wires was performed by a single observer using a stereomicroscopic loupe. Results: the pH cycling of orthodontic wires did not promote significant loss of mass or corrosion, despite the analysis of visual characteristics having changed after cycling. Conclusion: based on the results of the experimental protocol established in the present study, the analysis of the behavior of the NiTi and CrNi ­ 302 steel alloys that make up the orthodontic wires, facing the acid challenge of pH 4.3, for two weeks, it was concluded that these materials did not present loss of mass, opacity, brightness and smoothness considered significant. Other studies are recommended to provide further clarification on the topic.

Sports supplement induces dental structure corrosion: an in vitro pilot study / El suplemento deportivo induce corrosión en la estructura dental: un estudio piloto in vitro

Dietary supplements are being consumed with an increasingly high frequency among sports practitioners, whether at professional and/or amateur level. The supplements contain some nutritional properties in their composition, so they can dissolute the hydroxyapatite crystals of the enamel and favor the process of dental corrosion. The objective was to measure the corrosive power of protein-based supplementation (Whey Protein), under conditions that resemble the use of the supplement by the athletes, increasing the ecological validity of the study. The teeth of the test group (TG) were placed in contact with the Whey protein solution and then exposed to artificial saliva. And the teeth of the control group (CG) were exposed only to artificial saliva. The analysis occurred in natural healthy molar teeth, so that each tooth of the TG was immersed in 50 mL of supplement for 1.5 minutes and then placed in contact with the artificial saliva for 30 seconds. The same procedure was performed 5 times a day for 30, 60, 90, 120, 150 and 180 days. Each group, in its time (TG0 to TG180), underwent analysis of superficial roughness with the aid of optical profilometer (Talysurf CCI®, 3D model). The control group (CG) did not change its superficial roughness. Half of the teeth of the test group (TG) suffered loss of enamel surface. The values, in micrometers, of surface loss of the TG samples were 1.21; 2.1; 2.0; 1.04; 0.97; 0.8; 0.53; 1.14; 1.9; 2.0; 1.66; 1.80. The dietary supplement (Whey protein®) may be a potential cause of the dental corrosion process, considering the demineralization of hydroxyapatite that occurs along with the surface enamel loss.

Los suplementos dietéticos se consumen con una frecuencia cada vez más alta entre los practicantes de deportes, sea a nivel profesional y / o aficionado. Los suplementos contienen algunas propiedades nutricionales en su composición, por lo que pueden disolver los cristales de hidroxiapatita del esmalte y favorecer el proceso de corrosión dental. El objetivo fue medir el poder corrosivo de la suplementación a base de proteínas (proteína de suero), en condiciones que se asemejan al uso del suplemento por parte de los atletas, aumentando la validez ecológica del estudio. Los dientes del grupo de prueba (TG) se pusieron en contacto con la solución de proteína de suero y luego se expusieron a saliva artificial. Y los dientes del grupo de control (CG) estuvieron expuestos solo a saliva artificial. El análisis se realizó en dientes molares sanos naturales, cada diente del TG se sumergió en 50 ml de suplemento durante 1,5 minutos y luego se puso en contacto con la saliva artificial durante 30 segundos. El mismo procedimiento se realizó 5 veces al día durante 30, 60, 90, 120, 150 y 180 días. Cada grupo, en su momento (TG0 a TG180), se sometió a un análisis de rugosidad superficial con la ayuda de un perfilómetro óptico (Talysurf CCI®, modelo 3D). El grupo de control (CG) no cambió su rugosidad superficial. La mitad de los dientes del grupo de prueba (TG) sufrieron pérdida de la superficie del esmalte. Los valores, en micrómetros, de pérdida de superficie de las muestras de TG fueron 1.21; 2.1; 2,0; 1.04; 0,97; 0.8; 0,53; 1.14; 1.9; 2,0; 1,66; 1.80. El suplemento dietético (Whey protein®) puede ser una causa potencial del proceso de corrosión dental, considerando la desmineralización de la hidroxiapatita que ocurre junto con la pérdida de esmalte superficial.

Análise de limas endodônticas submetidas a biocorrosão por bactérias redutoras de sulfato in vitro / Analysis of endodontic files submitted to biocorrosion by sulfate reducing bacteria in vitro

Objetivo: Avaliar as alterações químicas presentes na superfície metálica de limas endodônticas fraturadas em canais radiculares, in vitro, após a inoculação intrarradicular de culturas de BRS de três cepas microbianas, Desulfovibrio desulfuricans (uma cepa oral e outra ambiental) e Desulfovibrio fairfieldensis. Métodos: foram analisadas 5 limas kerr #90, sendo uma Lima Kerr nova, sem tratamento, e as outras 4 limas fraturadas dentro de canais radiculares in vitro, com posterior inoculação de Desulfovibrio desulfuricans, cepa oral e ambiental, e Desulfovibrio fairfieldensis e um grupo controle sem inoculação bacteriana, por 477 dias. Os grupos foram analisados no modo EDS (Espectrometria de Energia Dispersiva de Raios-x) do microscópio eletrônico de varredura (FEI-Inspect-S50). Resultados:A presença do S, Cl e O foram relacionados ao processo biocorrosivo, assim como a redução dos elementos de liga nesta área. Conclusão:As análises no modo EDS demonstraram biocorrosão ao longo da superfície metálica das limas quando empregado o biofármaco BACCOR, nas três diferentes cepas empregadas, indicada pela redução dos elementos formadores da liga metálica, Fe, Ni e Cr, com a associação da presença de elementos indicadores de biocorrosão como O, Cl e S. (AU)

Aim:To evaluate the chemical alterations present on the metallic surface of root canal fractured endodontic files in vitro after the intraradicular inoculation of BRS cultures of three microbial strains, Desulfovibrio desulfuricans (one oral and one environmental strain), and Desulfovibrio fairfieldensis. Methods: Five kerr #90 files were analyzed, one new untreated Kerr file and the other 4 files fractured within root canals in vitro, with a subsequent inoculation of Desulfovibrio desulfuricans (oral and environmental strains), and Desulfovibrio fairfieldensis, as well as a control group without bacterial inoculation for 477 days. The groups were analyzed using the scanning electron microscope (FEI-Inspect-S50) EDS (X-ray Dispersive Energy Spectrometry) mode. Results:The presence of S, Cl, and O were related to the biocorrosive process, as well as the reduction of alloying elements in this area. Conclusion: The EDS mode analysis showed biocorrosion along the metallic surface of the files when the BACCOR biopharmaceutical was used in the three different strains employed in this study, indicated by the reduction of the alloying elements ­ Fe, Ni, and Cr ­ with the association of the presence of indicator elements of biocorrosion, such as O, Cl, and S. (AU)

The importance of corrosion resistance test of cannulas in the quality control of hypodermic needles

According to Anvisa risk rating, hypodermic needles offer medium risk to the user's health. This study discussed the importance of the corrosion resistance test in tubes of hypodermic needles, in the product quality control. A review of cannulas of hypodermic needles was carried out according to ISO 9626:2003 and 9259:1997 ABNT NBR. For the results evaluation, a scale which classifies the extent of corrosion was adjusted. 174 samples of PNI needles from 17 States and 9 different record holders were analyzed. According to the methodology of ISO 9626:2003, 100% of the samples were considered satisfactory. However, in accordance with the methodology of ISO 9259:1997, 97.1% of the samples were rejected. Irregularities can lead to impairment of product quality, resulting in risks to the consumer's health. Since 2011 the product has undergone certification, so it is necessary to reflect on the importance of corrosion resistance testing and mandatory certification for health monitoring.

O efeito de diferentes níveis de PH em soluções de flúor a 1, 1% na corrosão de arcos NITI / The effect of different PH levels on fluoride solutions at 1. 1% on corrosion of NITI archs

Objetivo: Determinar o pH crítico para ocorrer a corrosão de arcos NiTi em soluções de flúor a 1,1%, variando o pH de 3,5 a 7,0. Materiais e Métodos: Doze amostras com 10mm de comprimento de fio superelástico NiTi 0017 x 0025 (Abzil), obtidas do segmento distal dos arcos. As amostras foram aleatoriamente separadas e imersas dentro de recipientes contendo 40ml de seis soluções (água, soluções fluoretadas com pH: 3,5; 4,0; 4,5; 5,0; 5,5; 6,0; 6,5 e 7,0), sob uma mesa agitadora durante 90 minutos. Todas as amostras foram, então, levadas ao MEV. As imagens das amostras imersas em água e soluções fluoretadas com pH 7,0, 6,5 e 6,0 não se apresentaram diferentes, no entanto a partir da solução fluoretada com pH 5,5, as imagens superficiais apresentaram características diferentes dos grupos anteriores. Conclusão: Com base nos resultados obtidos neste estudo, o pH crítico para corrosão de arcos NiTi em soluções de flúor a 1,1% parece estar entre 6,0 e 5,5

Objective: To determine the critical pH to occur corrosion of NiTi arches in 1.1% fluoride solutions by varying the pH between 3.5 and 7.0. Materials and Methods: Twelve samples of 10 mm length superelastic NiTi wire 0017 x 0025 (Abzil) obtained in the distal segment of the arcs. The samples were randomly separated and immersed in 40 ml of six solutions (water, fluoride solutions with pH: 3.5; 4.0; 4.5; 5.0; 5.5; 6.0; 6.5 and 7.0) under a shaker table for 90 minutes. All samples were observed under SEM. The images of the samples immersed in water and fluoride solutions at pH 7.0, 6.5 and 6.0 did not show differences, however from the fluoride solution at pH 5.5, the surface characteristics of images presented differences from above groups. Conclusion: Based on the results obtained in this study the critical pH for corrosion of NiTi arches in fluoride solutions to 1.1% appears to be between 6.0 and 5.5

Evaluation of cytotoxicity and corrosion resistance of orthodontic mini-implants

ABSTRACT Objective: To evaluate and compare in vitro cytotoxicity and corrosion resistance of mini-implants from three different commercial brands used for orthodontic anchorage. Methods: Six mini-implants (Conexão(tm), Neodent(tm) and SIN(tm)) were separately immersed in artificial saliva (pH 6.76) for 30 and 60 days. The cytotoxicity of the corrosion extracts was assessed in L929 cell cultures using the violet crystal and MTT assays, as well as cell morphology under light microscopy. Metal surface characteristics before and after immersion in artificial saliva were assessed by means of scanning electron microscopy (SEM). The samples underwent atomic absorption spectrophotometry to determine the concentrations of aluminum and vanadium ions, constituent elements of the alloy that present potential toxicity. For statistical analysis, one-way ANOVA/Bonferroni tests were used for comparisons among groups with p < 0.05 considered significant. Statistical analysis was carried out with Graph Pad PRISM software Version 4.0. Results: No changes in cell viability or morphology were observed. Mini-implants SEM images revealed smooth surfaces with no obvious traces of corrosion. The extracts assessed by means of atomic absorption spectrophotometry presented concentrations of aluminum and vanadium ions below 1.0 µg/mL and 0.5 µg/mL, respectively. Conclusion: Orthodontic mini-implants manufactured by Conexão(tm), Neodent(tm) and SIN(tm) present high corrosion resistance and are not cytotoxic.

RESUMO Objetivo: avaliar, in vitro, e comparar a citotoxicidade e a resistência à corrosão de mini-implantes de três marcas comerciais diferentes, utilizados para ancoragem ortodôntica. Métodos: seis mini-implantes fabricados pelas empresas Conexão(r), Neodent(r) e SIN(r) foram imersos, separadamente, em saliva artificial (pH = 6,76), por 30 e 60 dias, de forma a obter os extratos da corrosão. A citotoxicidade dos extratos foi avaliada em cultura de células L929, empregando-se a análise de ensaios do cristal violeta e MTT, bem como da morfologia celular sob microscopia óptica. As características da superfície do metal antes e após a imersão em saliva artificial foram avaliadas usando microscopia eletrônica de varredura. Os extratos foram submetidos a espectrofotometria de absorção atômica, para determinar as concentrações dos íons alumínio e vanádio, elementos constituintes da liga e que apresentam toxicidade em potencial. Para análise estatística, os testes one-way ANOVA/Bonferroni foram usados para comparação entre os grupos, com p < 0,05 sendo considerado significativo. A análise estatística foi realizada com o programa Graph Pad PRISM v. 4.0. Resultados: não foi observada alteração na viabilidade ou morfologia celular após a exposição dos mini-implantes aos extratos. A análise dos mini-implantes por microscopia eletrônica de varredura revelou superfícies lisas e sem traços evidentes de corrosão. Os extratos analisados usando espectrofotometria de absorção atômica apresentaram concentrações de íons alumínio e vanádio inferiores a 1,0 µg/ml e 0,5 µg/ml, respectivamente. Conclusão: os mini-implantes fabricados pelas empresas Conexão(r), Neodent(r) e SIN(r) apresentam alta resistência à corrosão e não são citotóxicos.

Lobulación pulmonar de la rata blanca (Rattus norvegicus albinus) / Pulmonary lobulation of the white rat (Rattus norvegicus albinus)

La rata de laboratorio (Rattus norvegicus albinus), ha sido usada como modelo biológico para investigación, desde hace mucho tiempo. Por lo cual conocer su anatomía, en particular lo que dice relación con la lobulación pulmonar, resulta de utilidad para eventuales aplicaciones en las ciencias biomédicas. Para tal propósito, se utilizaron 10 ratas machos de la cepa Wistar, las que luego de ser sacrificadas por sobredosis de tiopental sódico intraperitoneal y antes de ser extraídos los pulmones de la cavidad torácica, a 7 de ellas, se les inyectó formalina al 10 % intratraqueal y a las otras 3, acrílico dental autocurable, para posteriormente, colocar el tejido en una solución KOH, para su corrosión. Es así como, de acuerdo a la arborización bronquial observada, se evidenció en el pulmón derecho 4 lóbulos (craneal, medio, caudal y accesorio) y 1 sólo lóbulo no dividido en el pulmón izquierdo.

The laboratory rat (Rattus norvegicus albinus) laboratory rat has long been used as a biological model for research. Therefore knowledge of its anatomy, particularly as related to pulmonary lobulation is useful for any applications in the biomedical sciences. For this reason, 10 male rats of the Wistar strain were used. After being sacrificed by overdose of intraperitoneal thiopental and before extracting the lungs from the thoracic cavity, 7 of them were injected 10 % formalin intratracheal and the other 3, self-curing dental acrylic, subsequently placing the tissue in a KOH solution for corrosion. Thus, according to the observed bronchial tree, 4 lobes were observed in the right lung (cranial, middle, caudal and accessory) and only one lobe not divided in the left lung.

Corrosion behavior of zirconia in acidulated phosphate fluoride

ABSTRACT Objective The corrosion behavior of zirconia in acidulated phosphate fluoride (APF) representing acidic environments and fluoride treatments was studied. Material and Methods Zirconia rods were immersed in 1.23% and 0.123% APF solutions and maintained at 37°C for determined periods of time. Surfaces of all specimens were imaged using digital microscopy and scanning electron microscopy (SEM). Sample mass and dimensions were measured for mass loss determination. Samples were characterized by powder X-ray diffraction (XRD) to detect changes in crystallinity. A biosensor based on electrochemical impedance spectroscopy (EIS) was used to detect ion dissolution of material into the immersion media. Results Digital microscopy revealed diminishing luster of the materials and SEM showed increased superficial corrosion of zirconia submerged in 1.23% APF. Although no structural change was found, the absorption of salts (sodium phosphate) onto the surface of the materials bathed in 0.123% APF was significant. EIS indicated a greater change of impedance for the immersion solutions with increasing bathing time. Conclusion Immersion of zirconia in APF solutions showed deterioration limited to the surface, not extending to the bulk of the material. Inferences on zirconia performance in acidic oral environment can be elucidated from the study.

Effects of Peracetic Acid on the Corrosion Resistance of Commercially Pure Titanium (grade 4)

The aim of this study was to evaluate the corrosion resistance of pure titanium grade 4 (cp-Ti-4), subjected to disinfection with 0.2% and 2% peracetic acid during different immersion periods using anodic potentiodynamic polarization test in acid and neutral artificial saliva. Cylindrical samples of cp-Ti-4 (5 mm x 5 mm) were used to fabricate 24 working electrodes, which were mechanically polished and divided into eight groups (n=3) for disinfection in 2% and 0.2% peracetic acid for 30 and 120 min. After disinfection, anodic polarization was performed in artificial saliva with pH 4.8 and 6.8 to assess the electrochemical behavior of the electrodes. A conventional electrochemical cell, constituting a reference electrode, a platinum counter electrode, and the working electrode (cp-Ti specimens) were used with a scanning rate of 1 mV/s. Three curves were obtained for each working electrode, and corrosion was characterized by using scanning electron microscopy (SEM) and energy dispersive x-ray spectrometry (EDS). Data of corrosion potential (Ecorr) and passive current (Ipass) obtained by the polarization curves were analyzed statistically by Student's t-test (a=0.05). The statistical analysis showed no significant differences (p>0.05) between artificial saliva types at different concentrations and periods of disinfection, as well as between control and experimental groups. No surface changes were observed in all groups evaluated. In conclusion, disinfection with 0.2% and 2% peracetic acid concentrations did not cause corrosion in samples manufactured with cp-Ti-4.

Resumo O objetivo deste estudo foi avaliar a resistência à corrosão de titânio puro grau 4 (cp-Ti-4) submetido à desinfecção com ácido peracético a 0,2% e 2% durante diferentes períodos de imersão por meio do teste de polarização potenciodinâmica anódica em saliva artificial ácida e neutra. Amostras cilíndricas de cp-Ti-4 (5 mm x 5 mm) foram usadas para confeccionar 24 eletrodos de trabalho, os quais foram polidos mecanicamente e divididos em oito grupos (n=3) para desinfecção com ácido peracético a 2% e 0,2% por 30 e 120 minutos. Após a desinfecção, foi realizado o teste de a polarização anódica em saliva artificial com pH 4,8 e 6,8 para avaliar o comportamento eletroquímico dos eletrodos. Uma célula electroquímica convencional, composta por eletrodo de referência, contra-eletrodo de platina, e eletrodo de trabalho (amostras de cp-Ti) foi usada com taxa de varredura de 1 mV/s. Foram obtidas três curvas para cada eletrodo de trabalho e a corrosão foi analisada por microscopia eletrônica de varredura (MEV) e espectrometria de energia dispersiva de raios-X (EEDX). Os dados de potencial de corrosão (Ecorr) e corrente passiva (Ipass) obtidos com as curvas de polarização foram analisados estatisticamente pelo teste t de Student (=0,05). A análise estatística não mostrou diferenças significantes (p>0,05) entre os tipos de saliva artificial nas diferentes concentrações e períodos de desinfecção, bem como entre os grupos controle e experimental. Não foram observadas alterações nas superfícies das amostras de todos os grupos avaliados. Conclui-se que a desinfecção com ácido peracético nas concentrações de 0,2% e 2% não provocou corrosão nas amostras confeccionadas com cp-Ti-4.

Streptococcus mutans adhesion and releasing of metallic ions in dental alloys

To evaluate the adherence of Streptococcus mutans to the surface of the amalgam and copper/aluminum alloy samples and also evaluate the release of metallic ions. METHODS: The prepared medium was changed every 72 h and analyzed by atomic absorption spectrophotometer. Samples were removed from the prepared medium at 15, 30, 48 and 60 days. RESULTS: The result shows that ions released were statistically different among all groups, and so were both biofilm and pits formation and the corrosion induced by the S. mutans in both types of samples. SEM observation of the samples immersed in the prepared medium with S. mutans showed adherence of microorganisms on the whole surface, in all groups. CONCLUSIONS: The S. mutans adhere to both amalgam and copper/aluminum alloy causing corrosion of those restorations. S. mutans produced a greater ions release in Cu/Al alloy; in amalgam, the ions release was not influenced by exposure to S. mutans...

Comparison surface characteristics and chemical composition of conventional metallic and Nickel-Free brackets

This study aims at comparing conventional and nickel-free metal bracket surface characteristics with elemental composition by scanning electron microscopy (SEM), using energy dispersive spectroscopy (EDS). The sample consisted of 40 lower incisor brackets divided into four groups: ABZ = conventional brackets, Kirium Abzil 3M® (n = 10); RL = conventional brackets, Roth Light Morelli® (n = 10); NF = nickel-free brackets, Nickel-Free Morelli® (n = 10); and RM = nickel-free brackets, Roth Max Morelli® (n = 10). Qualitative evaluation of the bracket surface was performed using SEM, whereby surface features were described and compared. The elemental composition was analyzed by EDS. According to surface analysis,groups ABZ and RL showed a homogeneous surface, with better finishing, whereas the surfaces in groups NF and RM were rougher. The chemical components with the highest percentage were Fe, Cr and C. Groups NF and MR showed no nickel in their composition. In conclusion, the bracket surface of the ABZ and RL groups was more homogeneous, with grooves and pores, whereas the surfaces in groups NF and RM showed numerous flaws, cracks, pores and grooves. The chemical composition analysis confirmed that the nickel-free brackets had no Ni in their composition, as confirmed by the manufacturer’s specifications, and were therefore safe to use in patients with a medical history of allergy to this metal.

Stability of antimicrobial activity of peracetic acid solutions used in the final disinfection process

The instruments and materials used in health establishments are frequently exposed to microorganism contamination, and chemical products are used before sterilization to reduce occupational infection. We evaluated the antimicrobial effectiveness, physical stability, and corrosiveness of two commercial formulations of peracetic acid on experimentally contaminated specimens. Stainless steel specimens were contaminated with Staphylococcus aureus, Escherichia coli, Candida albicans, blood, and saliva and then immersed in a ready peracetic acid solution: 2% Sekusept Aktiv (SA) or 0.25% Proxitane Alpha (PA), for different times. Then, washes of these instruments were plated in culture medium and colony-forming units counted. This procedure was repeated six times per day over 24 non-consecutive days. The corrosion capacity was assessed with the mass loss test, and the concentration of peracetic acid and pH of the solutions were measured with indicator tapes. Both SA and PA significantly eliminated microorganisms; however, the SA solution was stable for only 4 days, whereas PA remained stable throughout the experiment. The concentration of peracetic acid in the SA solutions decreased over time until the chemical was undetectable, although the pH remained at 5. The PA solution had a concentration of 500-400 mg/L and a pH of 2-3. Neither formulation induced corrosion and both reduced the number of microorganisms (p = 0.0001). However, the differences observed in the performance of each product highlight the necessity of establishing a protocol for optimizing the use of each one.

Corrosion behavior of self-ligating and conventional metal brackets

Objective: To test the null hypothesis that the aging process in self-ligating brackets is not higher than in conventional brackets. Methods: Twenty-five conventional (GN-3M/Unitek; GE-GAC; VE-Aditek) and 25 self-ligating (SCs-3M/Unitek; INs-GAC; ECs-Aditek) metal brackets from three manufacturers (n = 150) were submitted to aging process in 0.9% NaCl solution at a constant temperature of 37 ± 1ºC for 21 days. The content of nickel, chromium and iron ions in the solution collected at intervals of 7, 14 and 21 days was quantified by atomic absorption spectrophotometry. After the aging process, the brackets were analyzed by scanning electron microscopy (SEM) under 22X and 1,000X magnifications. Results: Comparison of metal release in self-ligating and conventional brackets from the same manufacturer proved that the SCs group released more nickel (p < 0.05) than the GN group after 7 and 14 days, but less chromium (p < 0.05) after 14 days and less iron (p < 0.05) at the three experimental time intervals. The INs group released less iron (p < 0.05) than the GE group after 7 days and less nickel, chromium and iron (p < 0.05) after 14 and 21 days. The ECs group released more nickel, chromium and iron (p < 0.05) than the VE group after 14 days, but released less nickel and chromium (p < 0.05) after 7 days and less chromium and iron (p < 0.05) after 21 days. The SEM analysis revealed alterations on surface topography of conventional and self-ligating brackets. Conclusions: The aging process in self-ligating brackets was not greater than in conventional brackets from the same manufacturer. The null hypothesis was accepted. .

Objetivo: testar a hipótese nula de que o processo de envelhecimento em braquetes autoligáveis não é superior ao de braquetes convencionais. Métodos: Vinte e cinco braquetes metálicos convencionais (GN, 3M/Unitek; GE, GAC; VE, Aditek) e 25 autoligáveis (SCs, 3M/Unitek; INs, GAC; ECs, Aditek) de três fabricantes (n = 150) foram submetidos ao envelhecimento em solução de NaCl à temperatura constante de 37 ± 1ºC, durante 21 dias. O conteúdo de íons níquel, cromo e ferro na solução coletada com 7, 14 e 21 dias foi quantificado por meio de espectrofotometria de absorção atômica. Depois de completado o processo de envelhecimento, os braquetes foram analisados com microscópio eletrônico de varredura (MEV), em magnificações de 22x e de 1.000x. Resultados: comparando-se a liberação de metais por braquetes autoligáveis e convencionais do mesmo fabricante, observou-se que o grupo SCs liberou mais níquel (p < 0,05) que o grupo GN após 7 e 14 dias, mas menos cromo (p < 0,05) após 14 dias e menos ferro (p < 0,05) nos três períodos experimentais. O grupo INs liberou menos ferro (p < 0,05) que o grupo GE após 7 dias, e menos níquel, cromo e ferro (p < 0,05) após 14 e 21 dias. O grupo ECs liberou mais níquel, cromo e ferro (p < 0,05) que o grupo VE após 14 dias; entretanto, liberou menos níquel e cromo (p < 0,05) após 7 dias e menos cromo e ferro (p < 0,05) após 21 dias. A análise no MEV demonstrou alterações na topografia da superfície de braquetes convencionais e autoligáveis. Conclusões: o processo de envelhecimento em braquetes autoligáveis não foi superior ao de braquetes convencionais do mesmo fabricante. A hipótese nula está aceita. .

Mechanical properties of NiTi and CuNiTi wires used in orthodontic treatment. Part 2: Microscopic surface appraisal and metallurgical characteristics

OBJECTIVE: This research aimed at comparing the qualitative chemical compositions and the surface morphology of fracture regions of eight types of Nickel (Ni) Titanium (Ti) conventional wires, superelastic and heat-activated (GAC, TP, Ormco, Masel, Morelli and Unitek), to the wires with addition of copper (CuNiTi 27oC and 35oC, Ormco) after traction test. METHODS: The analyses were performed in a scanning electronic microscope (JEOL, model JSM-5800 LV) with EDS system of microanalysis (energy dispersive spectroscopy). RESULTS : The results showed that NiTi wires presented Ni and Ti as the main elements of the alloy with minimum differences in their composition. The CuNiTi wires, however, presented Ni and Ti with a significant percentage of copper (Cu). As for surface morphology, the wires that presented the lowest wire-surface roughness were the superelastic ones by Masel and Morelli, while those that presented the greatest wire-surface roughness were the CuNiTi 27oC and 35oC ones by Ormco, due to presence of microcavity formed as a result of pulling out some particles, possibly of NiTi. 4 The fracture surfaces presented characteristics of ductile fracture, with presence of microcavities. The superelastic wires by GAC and the CuNiTi 27oC and the heat-activated ones by Unitek presented the smallest microcavities and the lowest wire-surface roughness with regard to fracture, while the CuNiTi 35oC wires presented inadequate wire-surface roughness in the fracture region. CONCLUSION: CuNiTi 35oC wires did not present better morphologic characteristics in comparison to the other wires with regard to surfaces and fracture region. .

OBJETIVO: objetivou-se nessa pesquisa comparar as composições químicas qualitativas e as morfologias das superfícies e das regiões de fratura, após ensaios de tração, de oito tipos de fios de NiTi superelásticos e termoativados convencionais (GAC, TP, Ormco, Masel, Morelli e Unitek) aos fios com adição de cobre (CuNiTi 27°C e 35°C, da Ormco). MÉTODOS: as análises foram realizadas em microscópio eletrônico de varredura (JEOL, modelo JSM-5800 LV) com sistema de microanálise EDS (energy dispersive spectroscopy). RESULTADOS: os resultados mostraram que os fios de NiTi ensaiados apresentaram Ni e Ti como os principais elementos da liga, com diferenças mínimas em suas composições. Os fios de CuNiTi, por sua vez, apresentaram Ni e Ti, com percentual significativo de cobre (Cu). Em relação às morfologias das superfícies, os fios que apresentaram os melhores acabamentos foram os superelásticos da Masel e Morelli, e os que apresentaram os piores acabamentos foram os de CuNiTi 27°C e 35°C, da Ormco, graças à presença de microcavidades formadas devido ao arrancamento de partículas, possivelmente de NiTi 4 . As superfícies de fratura apresentaram características de fratura dúctil, com a presença de microcavidades. Os fios superelásticos da GAC e de CuNiTi 27°C, bem como os termoativados da Unitek, apresentaram as menores microcavidades e os melhores acabamentos à fratura, enquanto os fios de CuNiTi 35° apresentaram acabamentos inadequados das regiões de fratura. CONCLUSÃO: os fios de CuNiTi 35°C não apresentaram características morfológicas mais adequadas das superfícies e das regiões de fratura em relação aos demais fios. .

Microbiologically induced deterioration of concrete: a review

Microbiologically induced deterioration (MID) causes corrosion of concrete by producing acids (including organic and inorganic acids) that degrade concrete components and thus compromise the integrity of sewer pipelines and other structures, creating significant problems worldwide. Understanding of the fundamental corrosion process and the causal agents will help us develop an appropriate strategy to minimize the costs in repairs. This review presents how microorganisms induce the deterioration of concrete, including the organisms involved and their colonization and succession on concrete, the microbial deterioration mechanism, the approaches of studying MID and safeguards against concrete biodeterioration. In addition, the uninvestigated research area of MID is also proposed.

Evaluation of ionic degradation and slot corrosion of metallic brackets by the action of different dentifrices

OBJECTIVE: To evaluate the in vitro ionic degradation and slot base corrosion of metallic brackets subjected to brushing with dentifrices, through analysis of chemical composition by Energy Dispersive Spectroscopy (EDS) and qualitative analysis by Scanning Electron Microscopy (SEM). METHODS: Thirty eight brackets were selected and randomly divided into four experimental groups (n = 7). Two groups (n = 5) worked as positive and negative controls. Simulated orthodontic braces were assembled using 0.019 x 0.025-in stainless steel wires and elastomeric rings. The groups were divided according to surface treatment: G1 (Máxima Proteção Anticáries®); G2 (Total 12®); G3 (Sensitive®); G4 (Branqueador®); Positive control (artificial saliva) and Negative control (no treatment). Twenty eight brushing cycles were performed and evaluations were made before (T0) and after (T1) experiment. RESULTS: The Wilcoxon test showed no difference in ionic concentrations of titanium (Ti), chromium (Cr), iron (Fe) and nickel (Ni) between groups. G2 presented significant reduction (p < 0.05) in the concentration of aluminium ion (Al). Groups G3 and G4 presented significant increase (p < 0.05) in the concentration of aluminium ion. The SEM analysis showed increased characteristics indicative of corrosion on groups G2, G3 and G4. CONCLUSION: The EDS analysis revealed that control groups and G1 did not suffer alterations on the chemical composition. G2 presented degradation in the amount of Al ion. G3 and G4 suffered increase in the concentration of Al. The immersion in artificial saliva and the dentifrice Máxima Proteção Anticáries® did not alter the surface polishing. The dentifrices Total 12®, Sensitive® and Branqueador® altered the surface polishing.

OBJETIVO: avaliar in vitro a degradação iônica e corrosão do fundo do slot de braquetes metálicos submetidos à escovação com dentifrícios, realizando análises da composição química por Espectroscopia de Energia Dispersiva (EDS) e qualitativa por Microscopia Eletrônica de Varredura (MEV). MÉTODOS: foram selecionados 38 braquetes divididos aleatoriamente em quatro grupos experimentais (n = 7). Dois grupos (n = 5) funcionaram como controles positivo e negativo. Aparelhos ortodônticos simulados foram confeccionados com fios de aço inoxidável 0,019" x 0,025" e anéis elastoméricos. Os grupos foram divididos de acordo com o tratamento de superfície: G1 (Máxima Proteção Anticáries®); G2 (Total 12®); G3 (Sensitive®); G4 (Branqueador®); Controle Positivo (saliva artificial) e Controle Negativo (sem tratamento). Foram realizados 28 ciclos de escovação e avaliações antes (T0) e após (T1) o experimento. RESULTADOS: o teste de Wilcoxon indicou não existir diferença nas concentrações iônicas de titânio (Ti), cromo (Cr), ferro (Fe) e níquel (Ni) entre os grupos. O grupo G2 apresentou redução significativa (p < 0,05) na concentração do íon alumínio (Al) e os grupos G3 e G4 apresentaram aumento significativo (p < 0,05) nas concentrações do íon alumínio. A análise em MEV mostrou aumento nas características indicativas de corrosão dos grupos G2, G3 e G4. CONCLUSÃO: a análise por EDS revelou que os grupos controle e G1 não sofreram alterações na composição química. O grupo G2 apresentou degradação na quantidade de íons Al, e G3 e G4 sofreram aumento na concentração de Al. A imersão em saliva artificial e o dentifrício Máxima Proteção Anticáries® não alteraram o polimento de superfície. Os dentifrícios Total 12®, Sensitive® e Branqueador® alteraram o polimento de superfície.