RESUMO
The application of titanium as medical implants is limited to a certain extent due to its insufficient corrosion resistance, biological activity, and antibacterial ability. In this work, a gradient nanograined (GNG) layer was fabricated on the titanium surface by surface ultrasonic rolling treatment (SURT). The subsequent copperizing kinetics was greatly enhanced so that a thick copperized layer could be obtained on the surface of GNG Ti at a relatively low diffusion temperature (450 °C). Meanwhile, the GNG structure accelerated the release rate of Cu2+, which endows GNG Cu/Ti with strong antibacterial activity. Moreover, the corrosion resistance and cytocompatibility of GNG Cu/Ti were also evidently improved compared with coarse-grained Ti, indicating a good biomedical application prospect.
Assuntos
Antibacterianos/farmacologia , Materiais Biocompatíveis/farmacologia , Cobre/farmacologia , Temperatura , Titânio/farmacologia , Antibacterianos/química , Materiais Biocompatíveis/química , Cobre/química , Escherichia coli/efeitos dos fármacos , Teste de Materiais , Testes de Sensibilidade Microbiana , Tamanho da Partícula , Staphylococcus aureus/efeitos dos fármacos , Propriedades de Superfície , Titânio/químicaRESUMO
A GPM-30 fatigue machine was used to investigate the influence of surface ultrasonic rolling (SURT) on the rolling contact fatigue (RCF) life of D2 wheel steel. The experimental results present that the RCF life of the grinding processing sample is 4.1 × 105 cycles. During the RCF process, the flaking of the fine grain layer and high surface roughness of the grinding processing sample cause the production of RCF cracks. When the samples are treated by SURT with 0.2 MPa and 0.4 MPa, the RCF life is 9.2 × 105 cycles and 9.6 × 105 cycles, respectively. After SURT, the surface roughness of the samples is reduced, and a certain thickness of gradient-plastic-deformation layer and a residual-compressive-stress layer are produced. These factors lead to the improvement of the RCF property. However, when the static pressure increases to 0.6 MPa during SURT, the RCF life of the sample is reduced during RCF testing. The micro-cracks, which are formed during SURT, become the crack source and cause the formation of RCF cracks, decreasing of the RCF life.