Use of cyanoacrylate-based surgical adhesives associated to the macroporous tape in skin synthesis in rats

Purpose: To compare the use of new cyanoacrylate surgical adhesive associated with macroporous tapes in cutaneous synthesis. Methods: Male Wistar rats with a longitudinal incision of 4cm were used on the back, divided into four groups: GI used octyl-cyanoacrylate (Dermabond®), GII used N-2-butylcyanoacrylate, GIII used octyl-cyanoacrylate and macroporous tape and GIV used N-2-butyl cyanoacrylate and macroporous tape. On the fourteenth day, the rats were submitted to euthanasia, were divided in two parts, and a layer of skin subcutaneous tissue through an area of operative healing was removed. One part was submitted to the study of rupture strength with the use of tensiometer, and in the other part histological examination was performed. Results: No force test was similar between groups I and II, being different from groups III and IV (P <0.001), which were identical to each other (P> 0.05). The units were compared among the studied groups, and they were different with the use of macroporous tapes (P> 0.05). Conclusions: The purpose of macroporous tapes is associated with CA adhesives in cutaneous tissues that provide more resistant scars. The use of a combination of macroporous tapes leads to complete re-epithelialization, without provoking foreign body reaction, has hemostatic properties and does not cause an absorptive reaction.(AU)

The aplication of cyanoacrilate surgical glue on skin suture in rats

Purpose: To compare the use of a new cyanoacrylate-based surgical glue and suture with sepa-rate points in skin wounds closure. Methods: Thirty-six rats were subjected to a 4cm dorsal longitudinal incision. Twelve were sub-jected to simple suture with polyamide 6-0, 12 rats underwent wall synthesis using Dermabond(r) and 12 was performed cutaneous synthesis with N-2-Butyl-Cyanoacrylate. Twelve of each group was euthanized on the seventh postoperative day, their blood was taken to biochemical tests and a layer of skin and subcutaneous tissue surrounding the surgical scar was randomly divided in two segments, to the submission of tension tests and to histological study. Results: There were no significant difference between groups (p>0.05). In the soft dermis there was more type I collagen production in group I (p 0.05), group II and III was similar re-sults (p>0.05). In the compact dermis, all 3 groups showed similar results (p>0.05). The biomechanical study was similarity between the glue groups (p>0.05) but the group III proved to be different from the others having a higher resistance (p>0.05) . Conclusion: This glue does not cause any inflammation or kidney and hepatic toxicity. Polyamide sutures are more resistant and the glue should be used alone only in less tension are-as.(AU)