RESUMO
As resinas acrílicas são amplamente utilizadas na odontologia, especialmente em ortodontia e prótese. Este artigo relata o caso de um paciente de 33 anos de idade, do gênero masculino que relatava desconforto e dores na região de pré-molar superior esquerdo após a colocação de um provisório, com presença de uma lesão eritomatosa. Após biópsia incisional constatouse a processo inflamatório crônico inespecífico. A causa apresentada para tal patologia foi o provisório confeccionado com resina acrílica autopolimerizável à base de metil-metacrilato. (AU)
Acrylic resins are widely used in dentistry, especially in orthodontics and prosthetics. Patients: this article reports the case of a leukodermic 33-year-old male who reported discomfort and pain due to an erythematous lesion in the upper first left premolar (24) after the placement of an acrylic resin temporary restoration. Discussion: The signs and symptoms presented by the patient and his report of visiting the rural countryside generated concern regarding the possible diagnosis, which led to a more invasive biopsy to differentiate allergic inflammation from a paracoccidioidomycosis. Biopsy revealed a chronic inflammatory process. Conclusion: the pathology was caused by contact with methyl methacrylate-based provisional acrylic resin. After cementation of the final crown, the inflammatory signs and symptoms disappeared .(AU)
Assuntos
Humanos , Masculino , Adulto , Resinas Acrílicas , Hipersensibilidade , MetilmetacrilatoRESUMO
The objective of this study was to evaluate the influence of different speeds using the piston device in the shear bond strength. 48 cylinders of composed resin had been confectioned (Solidex),and were divided randomly in four groups (n=12). The specimens were adapted to the device for the shear bond strenth test and were taken to an universal testing machine with a load cell of 1000 Kg. The test were carried through with four different speeds: group A: 0.5; group B: 1.0; group C: 1.5 and group D: 2.0 mm/min. The mean and standard deviations, in Kgf, were: A - 66,31 (10,24); B - 64,53 (20,40); C - 75,23 (11,84) and D - 66,62 (13,81). The data were submitted to ANOVA (p = 0.13). The results indicated that it did not have statistical significant difference between the groups A, B, C and D concluding that the speed in this type of test, with this device, can be varied without modify results
O objetivo do presente estudo foi avaliar a influência de diferentes velocidades usando o dispositivo pistão para o ensaio de cisalhamento. Foram confeccionados 48 cilindros em resina composta microhíbrida (Solidex), divididos aleatoriamente em quatro grupos (n = 12). As amostras foram adaptadas ao dispositivo para o ensaio de cisalhamento e levadas a uma máquina de ensaios universal com uma célula de carga de 1000 Kg. Os ensaios foram realizados com quatro velocidades diferentes: grupo A: 0,5 mm/min; grupo B 1,0 mm/ min; grupo C: 1,5 mm/min e grupo D 2,0 mm/min. Os valores médios e desvios padrão obtidos, em Kgf, foram: grupo A: 66,31 ± 10,24; grupo B: 64,53 ± 20,40; grupo C: 75,23 ± 11,84 e grupo D: 66,62 ± 13,81. Os dados foram submetidos ao teste ANOVA (p = 0,13). Os resultados indicaram que não houve diferença estatisticamente significante entre os grupos A, B, C e D concluindo que se pode variar a velocidade neste tipo de ensaio, utilizando o dispositivo pistão, sem que os resultados fossem alterados
Assuntos
Resinas Compostas , Teste de Materiais , Resistência ao CisalhamentoRESUMO
Objetivo: avaliar, por meio de extensometria, a infl uência da flange do implante de titânio na deformação superficial do osso. Material e métodos: um bloco de poliuretano simulando um osso tipo I mais corticalizado e menos medular (40 PCF) recebeu um implante de hexágono externo intraoral, sem flange 3,75 mm x 8,5 mm (G1) e um implante de hexágono externo extraoral, com flange 3,75 mm x 8 mm (G2). Em seguida, foram instalados componentes standard com 2 mm de altura de cinta metálica e cilindros metálicos para restauração provisória. Dois extensômetros lineares foram colados na superfície do bloco (mesial e distal de cada implante), e uma carga axial de 100 Ncm em uma máquina de ensaio universal foi aplicada, com cinco medições de microdeformação (µÎµ) para cada implante. Os dados foram submetidos ao teste Shapiro-Wilk para verifi car a homogenidade dos dados e em seguida ao teste t Student. Resultados: as médias e desvios-padrão obtidos foram: G1: 148,2 ± 5,84 e G2: 92,4 ± 11,24 µÆ, com diferença estatística significativa entre os grupos. Conclusão: os implantes extraorais tiveram melhor comportamento mecânico para as cargas axiais do que os implantes intraorais, sendo que a flange melhorou a distribuição da carga na superfície do bloco de poliuretano.
Objectives: to evaluate, by means of extensometry, the influence of the titanium implant flange on the superficial deformation of the bone. Material and methods: a polyurethane block simulating a more corticalized and less spinal type I bone (40 PCF) received an external intraoral hexagon implant with a 3.75 mm x 8.5 mm fl ange (G1) and an extraoral external hexagon implant, with flange 3.75 mm x 8 mm (G2). Subsequently, standard components with 2 mm high of metal strap and metal cylinders were installed for temporary restoration. Two linear strain gauges were glued to the surface of the block (mesial and distal of each implant), and an axial load of 100N in a universal test machine was applied with five microdemorphometric measurements (µÎµ) for each implant. The data were submitted to the Shapiro-Wilks test to verify the homogeneity of the data and then to the t-student test. Results: the means and standard deviations obtained were: G1: 148.2 ± 5.84 and G2: 92.4 ± 11.24 µÎµ, with signifi cant statistical difference between the groups. Conclusion: extraoral implants had better mechanical behavior for axial loads than intraoral implants, and the flange improved the load distribution on the surface of the polyurethane block.
Assuntos
Humanos , Estudo Comparativo , Prótese Maxilofacial , Implante de Prótese Maxilofacial , Osseointegração , Próteses e ImplantesRESUMO
Objetivo: avaliar, por meio de extensometria, a transmissão da carga mastigatória axial ao osso de suporte em próteses unitárias implantossuportadas por implantes de diferentes comprimentos. Material e métodos: em um bloco de poliuretano que simula 2 mm de osso cortical e o restante de medular, segundo a norma ASTMF1839, com 22 mm x 16 mm x 150 mm, foram instalados quatro implantes cone-morse infraósseos 2 mm: G1) 4 mm x 7 mm; G2) 4 mm x 9 mm; G3) 4 mm x 11 mm; G4) 4 mm x 13 mm. Sobre os mesmos, foram instalados pilares do tipo esteticone e cilindros metálicos. Dois extensômetros lineares foram colados na superfície do bloco, tangenciando a plataforma de cada implante (mesial e distal). Em uma máquina de ensaio universal, foi aplicada uma carga de 100 N sobre a superfície oclusal de cada cilindro. Para cada grupo, foram realizados cinco medições e os dados obtidos em microdeformacão (µÆ). Foi verificada a normalidade dos dados pelo teste de Shapiro-Wilk e realizada a análise de variância 1 critério (p < 0,05), e o teste Tukey (p ï³ 0,5). Resultados: as médias e os desvios-padrão das amostras foram, respectivamente, G1: 346.16,3 ± 10,28 µÆ; G2: 216.91 ± 15,47 µÆ; G3: 114,41 ± 2,33 µÆ; e G4: 76.83,3 ± 7,13 µÆ. O teste de Shapiro-Wilk constatou a normalidade dos dados, e os testes Anova e Turkey a diferença estatística significante entre todos os grupos. Conclusão: para cargas axiais, implantes com menor comprimento produziram maior deformação no osso superfi cial.
Purpose: the aim of this study was to evaluate, by extensometry, the transmission of the axial masticatory load to supporting bone around implants of different lengths. Material and methods: in a block of polyurethane that simulates 2 mm of cortical bone and the remaing of medullary bone, according to the ASTM-F1839 standard, with 22 mm x 16 mm x 150 mm, were installed 4 morse tappered dental implants, 2 mm subcrestal: G1) 4 mm x 7 mm; G2) 4 mm x 9 mm; G3) 4 mm x 11 mm; G4) 4 mm x 13 mm. Estheticone-like abutments and metallic cylinders were placed. Two linear strain gauges were bonded on block surface, tangential to the platform of each implant (mesial and distal). A 100 N load on the occlusal surface of each cylinder was applied to a universal test machine. For each group, five measurements and the data obtained in microdeformation (µÆ) were performed. The normality of the data was verified by the Shapiro-Wilk test and (p < 0.05) and Tukey's test (p ï³ 0.5). Results: the means and standard deviation of the samples were respectively G1: 346.16.3 ± 10.28 µÆ; G2: 216.91 ± 15.47 µÆ; G3: 114.41 ± 2.33 µÆ; G4: 76.83.3 ± 7.13 µÆ. The Shapiro-Wilk test exhibit the normality of the data, and the Anova and Turkey tests exhibit statistically significant difference between all groups. Conclusion: axial load produced more tension for short implants on the superficial bone.
Assuntos
Humanos , Análise de Variância , Fenômenos Biomecânicos , Força de Mordida , Implantação Dentária , Análise de Elementos Finitos , Equipamentos de Medição de Riscos , Técnicas In VitroRESUMO
Atualmente, a estética periodontal ou estética vermelha tem sido muito discutida e valorizada na busca pela harmonia do sorriso. Em situações de erupção passiva alterada, ou seja, existência de grande exposição de gengiva acompanhada de coroas clínicas curtas, há uma indicação precisa para a execução de aumento de coroa clínica. A Odontologia estética reabilitadora exerce um papel fundamental no tratamento multidisciplinar. Este trabalho teve como objetivo relatar um caso clínico de sorriso gengival causado pela erupção passiva alterada, associando reabilitação estética com facetas dentárias. Após a conclusão do tratamento, foi possível afirmar que a interação Prótese/Periodontia foi de fundamental importância para a obtenção do resultado final esperado pela paciente.
Nowadays, the periodontal or red esthetics has been highlightened in the search of smile harmony. In cases of altered passive eruption, which means the existence of great gum exhibition and short clinical crowns, there is precise indication for crown lengthening. Esthetic dentistry has a fundamental role in the multidisciplinary treatment. This paper reports on a clinical case of gummy smile due to passive eruption receiving an oral rehabilitation with laminate veneers. After treatment delivery, it was possible to recognize that the Prosthodontic/Periodontal relationship is of critical importance for the patient's desired outcome.
Assuntos
Humanos , Feminino , Adulto , Aumento da Coroa Clínica , Facetas Dentárias , Diastema , Estética Dentária , Osteotomia , PeriodontiaRESUMO
Este trabalho relata um caso clínico do uso do sistema CAD/CAM para confecção da infraestrutura metálica. Um paciente de 57 anos de idade apresentava-se com uma prótese total metalocerâmica superior de longa data e próteses mandibulares bilaterais sobre dois implantes cada, afetados pela peri-implantite. O planejamento incluiu a remoção dos implantes afetados e a colocação de quarto novos implantes entre os forâmenes mentonianos, mas sem carregamento imediato em função da atividade parafuncional do paciente. A infraestrutura metálica foi fresada a partir de uma bolacha de CoCr em dez minutos. Cada cantiléver apresentou extensão de 20 mm. A adaptação passiva da prótese mandibular definitiva confirmou as possibilidades e benefícios da tecnologia CAD/CAM para próteses totais fixas implantossuportadas.
This paper reports a clinical case where a CAD/CAM system was used to fabricate a metallic framework. A 57 years-old patient presented with an old tooth-supported fused-to-metal prosthesis in the maxilla and bilateral mandibular implant-supported prostheses (two implants each) affected by peri-implantitis. The treatment planning included removal of infected implants and placement of four new dental implants between mental foramina, but with no immediate loading due to the patient´s parafunctional activities. The metallic infra-structure was milled from a CoCr disk in ten minutes. Each cantilever had a 20 mm-length. The passive fit of the definitive mandibular prosthesis was deemed excellent and confirmed the possibilities and benefi ts of the CAD/CAM technology for complete fixed implant-supported prostheses.
Assuntos
Humanos , Masculino , Pessoa de Meia-Idade , Implantes Dentários , Prótese Total , Peri-Implantite , Ligas Metalo-CerâmicasRESUMO
O objetivo deste estudo foi avaliar a transmissão da carga mastigatória ao osso de suporte em próteses implantossuportadas em função do cantiléver, variando o tipo de pilar (Micro-Unite Ucla). A partir de dois modelos de poliuretano (norma ASTM F 1839), foram inseridos três implantes em cada, a uma distância de 8 mm, que conformaram os grupos: 1) implantes de hexágono externo e pilares Micro-Unit; 2) implantes de hexágono externo e pilares Ucla. Foram confeccionadas estruturas protéticas em resina acrílica ativada quimicamente sob cilindros com base de Co-Cr, que foram fundidas pela técnica convencional à brasagem. Foram fixados extensômetros no poliuretano entre os implantes e um na distal do implante mais próximo ao cantiléver. Em uma máquina de ensaio universal (2000RK Kratos, São Paulo, Brasil), foi realizada a aplicação da carga de 150 N. A carga foi aplicada entre os implantes e no cantiléver nos intervalos de 5, 10, 15, 20 e 25 mm. Os dados obtidos foram analisados estatisticamente para cada extensômetro e levando em consideração a extensão do cantiléver. Quanto maior a extensão do cantiléver, maior a deformação superficial do osso ao redor do implante mais distal. A utilização do componente tipo Micro-Unit apresentou valores de deformação inferiores em relação ao Ucla.
Objectives: to evaluate transmission of masticatory loads according to different prosthetic implant abutment and cantilever lengths. Material and methods: two polyurethane models (ASTM F-1839) received 3 external hex dental implants 8 mm each apart divided into two groups: 1) Micro-Unit and, 2) Ucla. Metallic frameworks were prepared using acrylic resin and cast over CoCr prosthetic cylinders. Strain gauges were attached at the polyurethane-abutment interface and at the distal part of the implant near the cantilever. After, a 150 N load (2000 RK, Kratos, São Paulo, Brazil) was applied at 15, 20, and 25 mm from the most distal implant. Statistical analysis considered abutment type and cantilever lengths. Results: longer cantilevers generate more deformation in the distal implant. Deformation values at Micro-Unit were lower than at Ucla abutment type.
Assuntos
Força de Mordida , Implantes Dentários , Prótese Dentária Fixada por ImplanteRESUMO
Objetivo: Avaliar a resistência de união ao cisalhamento entre um material de revestimento estético e um metal submetido a três tratamentos de superfície. Método: Foram confeccionados trinta cilindros metálicos, com 5 mm de comprimento e 4mm de diâmetro cada, obtidos por meio de usinagem de barras de titânio comercialmente puro (Ticp). Os cilindros foram divididos em três grupos conforme o tratamento superficial (n=10): Grupo 1 - jateamento com óxido de alumínio (150 micrometros); Grupo 2 - Sistema Rocatec (3M/ESPE): jateamento com óxido de alumínio (Al2O3) 110 micrometros (Rocatec-pre powder) e com sílica (Rocatec-plus powder) + silano (Rocatec-Sil) e Grupo 3 - Sistema CoJet (3M/ESPE): jateamento com partículas de sílica 30 micrometros + Silano (ESPE Sil). Para confecção dos espécimes, foi aplicado sobre cada base metálica o sistema opaco (Sinfony Opaco, 3M ESPE/EUA) e posteriormente a resina composta para restauração indireta (Sinfony, 3M ESPE/EUA). Os espécimes foram armazenados em água destilada (37 graus Celsius / 24 horas) e submetidos ao ensaio de cisalhamento em máquina de ensaio universal (EMIC, modelo DL- 1000), com célula de carga de 500 Kgf, a uma velocidade constante de 0,5mm/min. Os dados obtidos (MPa) foram submetidos ao teste ANOVA (1 fator) e teste de Tukey (5%). Resultados: Observou-se que o grupo 1 (20,01 - 3,12) diferiu estatisticamente do grupo 2 (27,83 - 3,02) e do grupo 3 (26,91 - 3,65) que, entre si, não diferiram estatisticamente. Conclusão: O tratamento da superfície do Ticp com Rocatec ou CoJet gera maior resistência de união entre o Ticp e a resina Sinfony.
Objective: To assess the shear bond strength of an esthetic coatingmaterial and a metal subjected to three surface treatments. Methods: Thirty metallic cylinders (5 mm high x 4 mm diameter) were fabricated from machining of commercially pure titanium (CPTi) bars. The cylinders were assigned to three groups (n=10), according to the surface treatment: Group 1: 150- micrometrics aluminum oxide particle air abrasion; Group 2 - Rocatec system (3M/ESPE):110- micrometrics aluminum oxide particle air abrasion (Rocatec-pre powder) and silica air abrasion (Rocatec-plus powder) + silane (Rocatec- Sil); and Group 3 - CoJet system (3M/ESPE): 30- micrometrics silica particle air abrasion + silane (ESPE Sil). The specimens were fabricated by applying the opaque system (Sinfony Opaco, 3M/ESPE) followed by indirect composite resin (Sinfony, 3M ESPE/USA). After storage in distilled water at 37 degrees celsius for 24 hours, the specimens were tested in shear strength in a universal testing machine (EMIC, model DL- 1000) with a 500 kgf charge cell at 0.5 mm/min crosshead speed. The obtained data (MPa) were subjected to one-way ANOVA and Tukey's test at 5% significance level. Results: Group 1 (20.01 - 3.12) was statistically different from Group 2 (27.83 -3.02) and Group 3 (26.91 - 3.65). Groups 2 and 3 did not differ significantly from each other. Conclusion: The surface treatment of CPTi with Rocatec or CoJet produced greater bond strength between CPTi and Sinfony composite resin.
Assuntos
Propriedades de Superfície , Abrasão Dental por Ar/métodos , Resinas Compostas/química , Resistência ao Cisalhamento , Titânio , Resinas Compostas , Análise de VariânciaRESUMO
O presente estudo in vivo propôs avaliar a precisão de instalação de 23 implantes sem retalhos empregando guias cirúrgicos obtidos por estereolitografia em quatro pacientes com maxilas totalmente desdentadas. Após duplo escaneamento com tomografia computadorizada tipo cone-beam, o planejamento pré-cirúrgico foi realizado com o programa Procera. Depois da cirurgia, realizou-se a comparação entre as posições dos implantes planejados e executados através de tomografia computadorizada pós-operatória. Para comparação da posição e dos longos eixos das imagens dos implantes foram eleitos três pontos em cada implante planejado e executado: no centro do limite coronário (D1), no centro da porção central (D2), no centro do limite apical (D3). Assim, as distâncias e o ângulo (A1) formado entre os longos eixos dos implantes planejados e executados foram numericamente calculados. De acordo com a análise tomográfica, os implantes executados em relação aos implantes planejados apresentaram desvios médios de 0,72 mm para a posição D1; 0,98 mm para a posição D2; 1,45 mm para a posição D3; 1,92 graus para o ângulo A1. Concluiu-se que houve desempenho adequado para a utilização de protocolos de cirurgia guiada baseados no método empregado em associação com guias cirúrgicos produzidos pelo processo de estereolitografia. A transferência do planejamento protético-cirúrgico para o campo operatório foi considerada satisfatória, visto que viabilizou a instalação de implantes dentários nas situações propostas...
The aim of this in vivo study was to evaluate the placement accuracy of 23 dental implants with fl apless surgery using stereolithographic guides in four completely edentulous maxillary patients. After double scanning with cone beam computerized tomography (CBCT), the presurgical planning was performed using appropriate software (Procera). After surgery, executed and planned implant positions were compared using CBCT superimposing. Measurements were made at the center of three pre-selected points: coronal (D1), central (D2), and apical (D3) portions. Thus, the distances among points and the angle (A1) formed between the long axes of the planned/executed implants were calculated. Mean deviations were as the following: 0.72 mm at D1, 0.98 mm at D2, and 1.45 mm at D3 positions. The mean angular deviaton (A1) was 1.92 degrees. It was concluded that there was adequate performance with surgical guides produced by stereolithographic process. The transfer of prosthetic-surgical planning for the surgical area was considered satisfactory, since it allowed for implant placement in proposed situations...
Assuntos
Humanos , Tomografia Computadorizada de Feixe Cônico , Implantes Dentários , Estereotipagem , Cirurgia Assistida por ComputadorRESUMO
OBJECTIVES: This study assessed the effect of cast rectifiers on the marginal misfit of cast UCLA abutments compared to premachined UCLA abutments. The influence of casting and porcelain baking on the marginal misfit of these components was also investigated. METHODS: Two groups were analyzed: test group - 10 cast UCLA abutments, finished with cast rectifier and submitted to ceramic application; control group - 10 premachined UCLA abutments, cast with noble metal alloy and submitted to ceramic application. Vertical misfit measurements were performed under light microscopy. In the test group, measurements were performed before and after the use of cast rectifiers, and after ceramic application. In the control group, measurements were performed before and after casting, and after ceramic application. Data were submitted to statistical analysis by ANOVA and Tukey's test (a= 5 percent). RESULTS: The use of cast rectifiers significantly reduced the marginal misfit of cast UCLA abutments (from 25.68mm to 14.83mm; p<0.05). After ceramic application, the rectified cylinders presented misfit values (16.18mm) similar to those of premachined components (14.3 mm). Casting of the premachined UCLA abutments altered the marginal misfit of these components (from 9.63 mm to 14.6 mm; p<0.05). There were no significant changes after porcelain baking, in both groups. CONCLUSION: The use of cast rectifiers reduced the vertical misfit of cast UCLA abutments. Even with carefully performed laboratory steps, changes at the implant interface of premachined UCLA abutments occurred. Ceramic application did not alter the marginal misfit values of UCLA abutments.
RESUMO
O objetivo neste trabalho foi avaliar, por meio da extensometria, a distribuição de tensões ao redor de implantes em função dos diferentes locais para carregamento e configuração (linear e compensada). Para tanto, em um bloco de poliuretano, foram posicionados paralelos entre si e com uma configuração linear, implantes autorrosqueáveis de hexágono externo, com dimensões de 3,75 mm x 13 mm, a uma distância de 7 mm, de centro a centro. Em outro bloco, a fixação do meio foi deslocada em 2 mm para gerar uma configuração compensada (offset). Pilares protéticos Micro-unit, com 3 mm de cinta, foram instalados sobre as fixações. Com duas matrizes em aço inoxidável foram confeccionados dez enceramentos para cada bloco (n = 10). A seguir, esses padrões foram fundidos com uma liga de Co-Cr. Quatro extensômetros (strain gauges) foram colados na superfície superior de cada bloco, tangenciando a plataforma de cada fixação. Um carregamento de 30 kg durante dez segundos foi feito em cinco posições (A, B, C, D, E), sendo repetido três vezes para aquisição dos dados (em µɛ) pelo aparelho condicionador de sinais. Os dados obtidos foram submetidos a análise de variância (RM Anova) e teste de Tukey (p < 0,05). Como conclusão da análise dos resultados obtidos, pudemos observar que não houve diferença entre as configurações linear e compensada; havendo diferença estatisticamente significante para os locais de carregamento.
The aim of this study was to evaluate through strain gauge methods the load distribution around dental implants regarding different sites and configurations (linear and offset). Three cylindrical implants with external hexagon (3.75 mm x 13mm) connection were fixed parallel in a polyurethane model with 7 mm between their centers in a linear configuration. In another block, the middle implant was positioned 2 mm offset. After, micro-unit abutments (3 mm of metallic collar height) were tightened. Ten wax patterns were created for each block (n = 10) and cast in Cobalt-Chromium alloy. Four strain gauges were positioned on the upper surface of each polyurethane model around the implants. A 30 kg axial load was applied for 10 seconds in five positions (A, B, C, D, and E), with three repeated measurements for data aquisition (in µɛ) by the multichannel bridge machine. Data were submitted to Anova and Tukey´s test (p < 0.05). It was concluded that: 1) no difference was seen between the linear and offset configurations and 2) there was statistical significance for different loading sites
Assuntos
Implantes Dentários , Prótese DentáriaRESUMO
Este estudo comparou a resistência de união da interface metal/resina compostacom diferentes tratamentos de superfície metálica. Material e Método: Trinta e trêspadrões de acrílico foram fundidos em CoCrMo com 25 X 3 X 0,5mm (ISO 9693).As amostras foram divididas em três grupos de acordo com os tratamentos de superfície:Grupo A microesferas retentivas (150μm) + jateamento com partículasde 110μm de óxido de alumínio + primer para metal + três camadas de opaco pararesina composta; Grupo B (controle) jateamento com partículas de 110μm de óxidode alumínio + primer para metal + três camadas de opaco para resina compostae o Grupo C jateamento com partículas de 110μm de óxido de alumínio + duascamadas de opaco para porcelana + condicionamento ácido (10% ácido hidrofluorídrico)+ silano + agente de união, e após, usando uma matriz, uma camada deresina composta (8 x 3 x 1mm) foi aplicada. O ensaio de flexão de três pontos foiusado a uma velocidade constante de 0,5mm/min. Os dados foram submetidos àanálise estatística one way ANOVA e o teste Tukey (a = 5%). Resultados: A análisedescritiva dos dados estatísticos (kgf) para os Grupos A, B e C foram (3.167±0.483),(0.858±0.157) e (1.602±0.262) respectivamente. Os resultados mostraram que osvalores de resistência à flexão para todos os grupos diferiram estatisticamente(p<0.001) entre eles. Conclusão: Os resultados mostraram que os maiores valores deresistência de união foram obtidos com o tratamento de superfície usado no Grupo A.
The present study compared the bond strength of the composite resin-metal interfacewith different treatments on the metal. Material and Method: Thirty three acrylicpatterns were casted in CoCrMo with 25 X 3 X 0,5mm (ISO 9693). All metallicspecimens were divided in three groups according to the surfaces treatments: GroupA retentive microballs (150μm) + sandblasting with aluminum oxide particles110μm (Al2O3) + metal primer + one layer of opaque resin; Group B (control)- sandblasting with aluminum oxide particles 110μm (Al2O3) + metal primer +three layers of opaque resin and Group C sandblasting with aluminum oxide particles110μm (Al2O3) + two layers of opaque porcelain + acid conditioning (10%hydrofluoric acid gel for 4min) + silane + bonding agent. After, using a matrix,one layer of composite resin (8 x 3 x 1mm) was applied. The three-point flexuraltest was used at a cross-head speed of 0,5mm/min. These data were submitted toone way ANOVA and Tukey´s test (a = 5%). Results: Descriptive statistics data(kgf) for groups A, B and C were (3.167±0.483), (0.858±0.157) and (1.602±0.262)respectively. The results showed that mean flexural strength values for all groupsdiffer statistically (p <0.001) among them. The values of group A were significantlyhigher than the group B and C. Conclusion: The results showed highestvalues of bond strength were obtained with surface treatment used in A group.
Assuntos
Resinas Compostas , Materiais Dentários , Fenômenos Físicos , Teste de Materiais/métodosRESUMO
A prótese parcial removível (PPR) conjugada a implantes osseointegrados é um desafio na Odontologia restauradora, pois a biomecânica que envolve dois sistemas diferentes é um tanto quanto complexa. Este relato de caso expõe a instalação de uma PPR associada a dois implantes osseointegrados com encaixe do tipo ERA, fixados na região distal. Após minuciosos exames clínico, radiográfico e realização de modelos de estudo fez-se os planejamentos cirúrgico e protético. Restabeleceu-se função e estética associadas a um grande conforto e satisfação relatados pelo paciente, mas vale ressaltar que mais estudos clínicos são necessários para se ter um posicionamento mais definido em relação a esta modalidade terapêutica.
Assuntos
Humanos , Feminino , Adulto , Implantação Dentária Endóssea , Prótese Parcial RemovívelRESUMO
O principal parâmetro para avaliação do sucesso dos implantes osseointegrados é baseado no percentual do contato do tecido ósseo à superfície do implante. Este processo depende de vários fatores que vão desde a inserção do implante no leito cirúrgico e a formação do coágulo sanguíneo a todos os eventos celulares relacionados à biologia óssea peri-implantar. Logo, o objetivo deste estudo foi avaliar, de maneira sistemática, a sequência de eventos celulares assim como os fatores que influenciam a qualidade e a quantidade de contato do tecido ósseo humano a superfície do implante e suas consequências clínicas.
Assuntos
Materiais Biocompatíveis , Implantação Dentária Endóssea , Osseointegração , TitânioRESUMO
O objetivo deste trabalho foi avaliar a resistência à tração entre resinas de uso direto de três diferentes marcas comerciais, simulando reparos, utilizando ou não adesivo nesta interface. Para tanto foram confeccionadas 60 bases cônicas em resina composta (TPH) apresentando as seguintes dimensões: 5mm de comprimento, com uma base maior de 5mm e uma base menor de 3mm de diâmetro. Essas bases foram divididas aleatoriamente em 6 grupos. Sob estas bases foram aplicadas, com auxílio de uma matriz bi-partida de teflon, três resinas: TPH (Dentsply), InTen-S (Ivoclar), Filtek Supreme (3M-ESPE), com ou sem a utilização de um adesivo dentinário (Single Bond û 3M-ESPE), de maneira a obter amostras na forma de ampulheta. Após armazenamento destas amostras durante 7 dias à 37º C, estas foram submetidas ao ensaio de tração em uma máquina de ensaios universal com velocidade de 1,0 mm/ min e célula de carga de 500Kgf a qual carregou a amostra até que ocorresse sua fratura. Os dados obtidos (MPa) foram submetidos à Análise de Variância (ANOVA), e ao o teste de Tukey (5%). As médias e desvios padrão foram obtidos dos grupos sem e com adesivo, respectivamente: G1 - TPH 10,88±2,37, G2 - 17,59±3,42; G3 - Filtek 3,91±3,06, G4 - 14,02±4,34; G5 - Inten-S 5,32±1,30, G6 - 12,54±2,06. O teste estatístico de Tukey demonstrou que a utilização do adesivo levou a valores de tração estatisticamente maiores independentemente da marca comercial de resina composta, assim como a utilização da mesma resina da base, para o reparo.
This study evaluated the tensile bond strength between direct composite resins of three different brands, simulating repairs with or without utilization of adhesive at this interface. For that purpose, 60 tapered composite resin (TPH) bases were fabricated with the following dimensions: 5mm length, a larger base measuring 5mm in diameter and a smaller base with 3-mm diameter. These bases were randomly divided into 6 groups. Three resins were applied on these bases, with aid of a split Teflon matrix: TPH (Dentsply), InTen-S (Ivoclar), Filtek Supreme (3M-ESPE), with or without utilization of a dentin adhesive (Single Bond û 3M-ESPE), for achievement of hourglass-shaped specimens. After storage of specimens for 7 days at 37ºC, these were submitted to tensile testing in a universal testing machine EMIC û DL1000, at a crosshead speed of 1.0mm/min and a load cell of 500Kgf, which applied load on the specimen until occurrence of fracture. Data achieved (MPa) were submitted to Analysis of Variance (ANOVA) and to the Tukey test (5%). The means and standard deviations for groups with and without adhesive were as follows: G1 û TPH 10.88±2.37, G2 û 17.59±3.42; G3 û Filtek 3.91±3.06, G4 û 14.02±4.34; G5 û Inten-S 5.32±1.30, G6 û 12.54±2.06. The Tukey test demonstrated that utilization of the adhesive provided statistically higher tensile values, regardless of the composite resin brand, as well as repair with the same resin employed for the base.
Assuntos
Resinas Compostas , Materiais Dentários , Restauração Dentária Permanente , Adesivos Dentinários , Resistência à TraçãoRESUMO
Introdução - O propósito deste estudo é avaliar comparativamente a perda de massa resultante da aplicação tópica de flúor fosfato acidulado e de flúor neutro, em três resinas de uso indireto (Artglass - Kulzer; Solidex - Shofu; Targis - Ivoclar), e verificar se esses efeitos se acentUam com o aumento de tempo de contato das resinas com os géis fluoretados. Métodos - Foram confeccionados 12 corpos-de-prova com 5mm de diâmetro por 3mm de espessura, de cada marca comercial, obedecendo às orientações do fabricante. Todas as amostras foram pesadas inicialmente em uma balança analítica (Mettler Toledo, modelo AB204). Cada marca comercial foi dividida em 2 gmpos numericamente iguais, para que metade dos corpos de cada marca comercial fosse acondicionada em gel de flúor fosfato acidulado a 1,23 por cento - NUPRO (Dentsply), com pH de 3,5 - 3,9; e a outra metade permanecesse em NUPRO (Dentsply), pH de 6,5 a 7,5 por cento. Após 4 minutos, as amostras foram pesadas na mesma balança analítica. Depois da obtenção dos resultados, os corpos-de-prova foram colocados novamente em contato com os respectivos géis por 1 hora e as amostras foram lavadas, secas e pesadas novamente. Os valores obtidos foram submetidos ao teste ANOVA, ao nível de significância de 5 por cento e ao teste de Tukey. Conclusão - Não houve perda significativa de massa em todas as sitUações utilizando-se flúor neutro, porém ocorreu quando se utilizou flúor fosfato acidulado, perda essa que só foi estatisticamente significativa com 4 minutos para Artglass. Mas, ao se avaliar por 1 hora, essa perda foi significativa para todas essas resinas.
Assuntos
Resinas Compostas , Desgaste de Restauração Dentária , Flúor , Cimentos de ResinaRESUMO
O objetivo deste estudo foi medir e comparar as forças de uniãoentre uma liga de NiCr e uma resina, usando um adesivodentinário e um cimento resinoso como alternativas parareparar coroas metalocerâmicas. Vinte quatro bases em NiCr(Wironia, Bego) foram confeccionadas, jateadas por 20segundos com óxido de alumínio (250μm com uma pressão de2 bar), lavadas por 5 segundos e secas com jato de ar. As basesforam divididas aleatoriamente em 2 grupos (G1, G2) de 12espécimes cada. O grupo G1 foi tratado com 3M Single BondAdhesive System, e G2 com Panavia F metal primer, Panavia FED primer, e uma fina camada do cimento Panavia F (J.Morita).A resina W3D (Wilcos) foi aplicada nas superfícies de metal epolimerizada. O teste de cisalhamento foi realizado em umamáquina de ensaio universal (modelo DL-1000, EMIC -Equipamentos e Sistemas Ltda., São José dos Pinhais - PR -Brasil) com célula de carga de 50kg e velocidade de0.5mm/min. Após os testes mecânicos, os dados obtidos emMpa foram submetidos ao Mann-Whitney Test (p=0.006), o qualrevelou que os grupos G1 e G2 diferiram estatisticamente entresi, possibilitando concluir que 3M Single Bond Adhesive Systemdemonstrou valores de união significativamente maiores que o Panavia F
Assuntos
Adesivos Dentinários , Cimentos de Resina , Estatísticas não ParamétricasRESUMO
O objetivo deste trabalho foi avaliar a alteração dimensional de um silicone polimerizado por reação de condensação convencional e outro em auto-mistura. Para isso, foi empregado um modelo padrão com quatro pilares angulados, tendo um deles um sulco em forma de ôvõ na região cervical. A técnica de moldagem utilizada foi a do material em consistência densa e fluida em dois estágios, com casquetes metálicos para alívio, o que originou espessura padronizada de 2,0mm para moldagem final. Foram obtidos doze modelos em gesso pedra tipo IV (Durone - Dentsply Indústria e Comércio Ltda., Petrópolis-BRASIL) para cada condição experimental estudada. Os modelos foram mensurados em um projetor de perfil (Jones & Lanson-mod.Epic-30E-Springfield, Vermont-USA), com ampliação de 10x e suas medidas comparadas às do modelo padrão. Os resultados obtidos foram submetidos aos testes estatísticos de Kruskal-Wallis e de Dunn, ao nível de significância de 5%. Verificou-se que houve diferença estatisticamente significante para a largura entre os pilares com angulação de 16o (p3) e com sulco em forma de ôvõ (p4) dos corpos-de-prova obtidos com o silicone de auto-mistura e os pilares cilíndricos (p1) e com angulação de 6o (p2) dos corpos-de-prova obtidos com o silicone convencional. Sendo que os pilares p3 e p4 do grupo auto-mistura apresentaram-se mais largos do que p1 e p2 do grupo convencional. Porém não houve diferença estatisticamente significante para a altura dos corpos-de-prova.
Assuntos
Materiais Dentários/análise , Silicones/química , Elastômeros de SiliconeRESUMO
A combinação de cirurgia e radioterapia é comum para o tratamento de tumores malignos de cabeça e pescoço, determinando alterações teciduais como: mucosa fragilizada, xerostomia, anatomia inadequada e distúrbios miodinâmicos, dificultando a reabilitação oral convencional do paciente. Felizmente, implantes osseointegrados são empregados para a reabilitação protética em pacientes oncológicos, com altas taxas de sucesso, mesmo em tecidos previamente irradiados. Estes pacientes representam um grande desafio aos implantodontistas. Além de possuírem defeitos anatômicos resultantes das cirurgias para remoção dos tumores, possuem suprimento sangüíneo comprometido nas áreas afetadas como resultado da radioterapia. No tratamento desses indivíduos há um alto potencial de complicações, tais como: redução da velocidade de cicatrização, recidiva do tumor, desenvolvimento de necrose dos tecidos duros e moles, aumentando consideravelmente as chances de insucesso da osseointegração. Porém, a cuidadosa seleção dos pacientes e o emprego de técnica cirúrgica e reabilitações protéticas adequadas podem resultar em terapias bem sucedidas
Assuntos
Humanos , Masculino , Feminino , Implantação Dentária Endóssea , Implantes Dentários , Neoplasias Bucais , Osseointegração , Procedimentos de Cirurgia Plástica , Reabilitação Bucal , RadioterapiaRESUMO
O objetivo desta pesquisa foi avaliar a influência do etanol a 50 por cento e do ácido cítrico 0,02M na superfície de resinas compostas para restaurações diretas e indiretas. Foram confeccionados 36 cilindros de resina Esthet X (Dentsply) (D) e 36 de resina Epricord (Kuraray) (I), dividos em 3 grupos de acordo com o meio de estocagem: água destilada (A), etanol a 50 por cento (E) e ácido cítrico 0,02 M (C) e em 3 subgrupos, de acordo com o tempo de estocagem: 1,7 e 14 dias. Os cílindros foram submetidos à leitura de microdureza com carga de 50 gf e tempo de permanência de 10s, utilizando-se o microdurômetro digital (modelo FM 700, Futuretch - Tókio - Japão). Os dados obtidos foram submetdos à análise estatística ANOVA 1 e 2 fatores e ao teste de Tukey (p = 5 por cento). Os resultados foram: DA1(69,38); DA7(68,57); DA14(68,21); DE1(41,67); DE7(50,97); DE14(47,08); DC1(67,12); DC7(52,82); DC14(48,20); IA1(39,42); IA7(40,46); IA14(39,36); IE1(41,67); IE7(33,84); IE14(28,15); IC1(41,88); IC7(37,06); IC14(30,44) e permitiram concluir que o etanol e o ácido cítrico exercem influência significativa na microdureza da resina composta para técnica direta e indireta, sendo influenciada pelo fator tempo, e que houve diferença significativa entre a microdureza da resina composta direta que apresentou-se superior à resina indireta