Push-Out Bond Strength of Glass Fiber Endodontic Posts with Different Diameters.

(1) Background: The retention of intraradicular posts is an important factor for the prognosis of endodontically treated teeth. The purpose of this study was to evaluate the push-out bond strength (PBS) of the posts relating to their diameter and region of the root. (2) Methods: A total of 40 premolar teeth (decoronated and root canal-filled) were divided into four groups (n = 10). After post-space preparation, different sizes (1.0, 1.2, 1.5, and 2.0 mm) of glass fiber posts were luted with resin cement into the root canals. After placement, 2 mm thick slices were cut from the roots according to their apical, middle, and coronal regions (n = 116). Push-out tests were carried out in a universal testing machine on each slice. A statistical evaluation of the data was applied. (3) Results: When comparing the diameter, the 2.0 mm posts had the highest PBS (111.99 ± 10.40 N), while the 1.0 mm posts had the lowest PBS (99.98 ± 8.05 N). Divided by the surface of the bonded area, the average PBS value was the highest for the 1.0 mm posts (18.20 ± 1.67 MPa) and the lowest for the 2.0 mm posts (12.08 ± 1.05 MPa). (4) Conclusions: Within the limitations of the study, when comparing the regions of the roots, no significant differences were found among the PBS values of the three regions (p = 0.219). When comparing the diameters, significant differences were shown between the PBS values of the four groups (p = 0.023 and p = 0.003, respectively).

Push-Out Bond Strength of Endodontic Posts Cemented to Extracted Teeth: An In-Vitro Evaluation.

(1) Background: An ideal bond strength between endodontic posts and root canal dentin is essential for optimal retention and good prognosis. This study aimed to evaluate the push-out bond strength (PBS) of prefabricated fiber and metal posts, luted with resin cement to natural dentin. (2) Methods: Extracted premolars with similar root dimensions were assigned into two groups of 30 each for the metal and fiber posts. Teeth were mounted in acrylic blocks exposing 2 mm of the coronal root. Teeth were subjected to endodontic treatment and post-space preparations. Two groups were further subdivided into three sub-groups (n = 10) according to the size of the posts (# 4, 5 and 6). Posts were cemented with resin cement. Specimens were sectioned into 4 mm slices and subjected to the PBS test. (3) Results: The mean PBS was similar for the metal and fiber posts bonded with resin cement, showing a statistically significant result. An increase in post size increased the bond strength initially, but a further increase in size did not show any marked difference. A total of 71.66% of tested specimens failed with the adhesive failure mode. (4) Conclusions: Metal posts showed slightly higher retention compared to the fiber posts, although the p-value was similar for both types. An increase in the size of posts showed increased retention. The most common mode of failure was adhesive failure between cement and dentin.

Cement layer thickness and shear stress resistance in cylindrical dowel spaces: pull-out test.

PURPOSE: This study evaluated the effects of different dowel space (DS) diameters on pull-out bond strength of a cylindrical post, of threaded steel, to dentin. MATERIALS AND METHODS: Forty-five extracted human teeth were divided in 3 groups with DSs, with the same depth (6 mm), differing for the diameter (i.e. 1.5 mm, Group 1; 1.75 mm, Group 2; 2.00 mm, Group 3). Both the diameter of the post (1.3 mm) and the composite resin cement (Panavia 21) were the same for all the samples. The samples were submitted to pull-out test by means an Universal Testing Machine (Mod. 1193, Instron) (1KN load cell, crosshead speed 0.5 mm/min). RESULTS: The mean values of the bond strength (BS) were: Group 1, 442±128.3N; Group 2, 411.3±111N; Group 3, 448.7±142.29N. While the calculated average shear bond strengths (SBSs) were: Group 1, 14.7±4.27MPa; Group 2, 11.6±3.14MPa; Group 3, 11±3.5MPa. ANOVA test showed not significative differences, among the groups, concerning the BS: Group 1 vs Group 2 (p = 0.490); Group 1 vs Group 3 (p = 0.894); Group 2 vs Group 3 (p = 0.431). Significative differences were observed, among the groups, concerning the SBS for Group 1 vs Group 2 (p = 0.032) and Group 1 vs Group 3 (p = 0.014). While a not significative difference was found, concerning this parameter, for Group 2 vs Group 3 (p = 0.641). CONCLUSION: The cement thickness can influence the SBS of the adhesively luted posts, in our setting, the best values were obtained with a thickness of 100 µm.