RESUMO
The formation of intrinsic point defects in the N-sublattice of semi-insulating Mg-doped GaN crystals grown by the ammonothermal method (SI AT GaN:Mg) was investigated for the first time. The grown-in defects produced by the displacement of nitrogen atoms were experimentally observed as deep traps revealed by the Laplace transform photoinduced transient spectroscopy in the compensated p-type crystals with the Mg concentrations of 6 × 1018 and 2 × 1019 cm-3 and resistivities of ~1011 Ωcm and ~106 Ωcm, respectively. In both kinds of materials, three closely located traps with activation energies of 430, 450, and 460 meV were revealed. The traps, whose concentrations in the stronger-doped material were found to be significantly higher, are assigned to the (3+/+) and (2+/+) transition levels of nitrogen vacancies as well as to the (2+/+) level of nitrogen split interstitials, respectively. In the material with the lower Mg concentration, a middle-gap trap with the activation energy of 1870 meV was found to be predominant. The results are confirmed and quantitatively described by temperature-dependent Hall effect measurements. The mechanism of nitrogen atom displacement due to the local strain field arising in SI AT GaN:Mg is proposed and the effect of the Mg concentration on the charge compensation is discussed.
RESUMO
A detailed analysis of morphology of gallium nitride crystal growth obtained by ammonothermal and halide vapor phase epitaxy methods was carried out. The work was conducted to determine the source of triangular planar defects visible in X-ray topography as areas with locally different lattice parameters. It is shown that the occurrence of these defects is related to growth hillocks. Particular attention was paid to analyzing the manner and consequences of merging hillocks. In the course of the study, the nature of the mentioned defects and the cause of their formation were determined. It was established that the appearance of the defects depends on the angle formed between the steps located on the sides of two adjacent hillocks. A universal growth model is presented to explain the cause of heterogeneity during the merging of growth hillocks.
RESUMO
In this paper, a detailed investigation of the basic ammonothermal growth process of GaN is presented. By analyzing the crystallization on a native seed with a lenticular shape, thus with an intentionally varying off-cut, we wanted to answer some basic questions: (i) Which crystallographic planes play the most important role during growth (which planes are formed and which disappear)? (ii) What is the relationship between the growth rates in different crystallographic directions? (iii) What is the influence of the off-cut of the seed on the growth process? Two non-polar slices, namely, 12¯10 and 1¯100, as well as a 0001 basal plane slice of an ammonothermal crystal were analyzed. The examined planes were selectively etched in order to reveal the characteristic features of the growth process. The applied characterization methods included: optical microscopy with Nomarski contrast and ultraviolet illumination, X-ray topography and high-resolution X-ray diffraction, and secondary ion mass spectrometry. The obtained results allowed for creating a growth model of an ammonothermal GaN crystal on a lenticular seed. These findings are of great importance for the general understanding of the basic ammonothermal crystal growth process of GaN.
RESUMO
In this paper, we investigate, using X-ray Bragg diffraction imaging and defect selective etching, a new type of extended defect that occurs in ammonothermally grown gallium nitride (GaN) single crystals. This hexagonal "honeycomb" shaped defect is composed of bundles of parallel threading edge dislocations located in the corners of the hexagon. The observed size of the honeycomb ranges from 0.05 mm to 2 mm and is clearly correlated with the number of dislocations located in each of the hexagon's corners: typically ~5 to 200, respectively. These dislocations are either grouped in areas that exhibit "diameters" of 100-250 µm, or they show up as straight long chain alignments of the same size that behave like limited subgrain boundaries. The lattice distortions associated with these hexagonally arranged dislocation bundles are extensively measured on one of these honeycombs using rocking curve imaging, and the ensemble of the results is discussed with the aim of providing clues about the origin of these "honeycombs".
RESUMO
X-ray topography defect analysis of entire 1.8-inch GaN substrates, using the Borrmann effect, is presented in this paper. The GaN wafers were grown by the ammonothermal method. Borrmann effect topography of anomalous transmission could be applied due to the low defect density of the substrates. It was possible to trace the process and growth history of the GaN crystals in detail from their defect pattern imaged. Microscopic defects such as threading dislocations, but also macroscopic defects, for example dislocation clusters due to preparation insufficiency, traces of facet formation, growth bands, dislocation walls and dislocation bundles, were detected. Influences of seed crystal preparation and process parameters of crystal growth on the formation of the defects are discussed.