Influence of the sintering atmosphere on the physico-chemical properties and the osteoclastic resorption of ß-tricalcium phosphate cylinders.

One of the most widely used materials for bone graft substitution is ß-Tricalcium phosphate (ß-TCP; ß-Ca3(PO4)2). ß-TCP is typically produced by sintering in air or vacuum. During this process, evaporation of phosphorus (P) species occurs, leading to the formation of a calcium-rich alkaline layer. It was recently shown that the evaporation of P species could be prevented by co-sintering ß-TCP with dicalcium phosphate (DCPA; CaHPO4; mineral name: monetite). The aim of this study was to see how a change of sintering atmosphere could affect the physico-chemical and biological properties of ß-TCP. For this purpose, three experimental groups were considered: ß-TCP cylinders sintered in air and subsequently polished to remove the surface layer (control group); the same polished cylinders after subsequent annealing at 500 °C in air to generate a calcium-rich alkaline layer (annealed group); and finally, ß-TCP cylinders sintered in a monetite-rich atmosphere and subsequently polished (monetite group). XPS analysis confirmed that cylinders from the annealed group had a significantly higher Ca/P molar ratio at their surface than that of the control group while this ratio was significantly lower for the cylinders from the monetite group. Sintering ß-TCP in the monetite-rich atmosphere significantly reduced the grain size and increased the density. Changes of surface composition affected the activity of osteoclasts seeded onto the surfaces, since annealed ß-TCP cylinders were significantly less resorbed than ß-TCP cylinders sintered in the monetite-rich atmosphere. This suggests that an increase of the surface Ca/P molar ratio leads to a decrease of osteoclastic resorption. STATEMENT OF SIGNIFICANCE: Minimal changes of surface and bulk (< 1%) composition have major effects on the ability of osteoclasts to resorb ß-tricalcium phosphate (ß-TCP), one of the most widely used ceramics for bone substitution. The results presented in this study are thus important for the calcium phosphate community because (i) ß-TCP may have up to 5% impurities according to ISO and ASTM standards and still be considered to be "pure ß-TCP", (ii) ß-TCP surface properties are generally not considered during biocompatibility assessment and (iii) a rationale can be proposed to explain the various inconsistencies reported in the literature on the biological properties of ß-TCP.

The history of the development of the regular straight stem in hip arthroplasty.

Since the middle of the 20th century, total hip arthroplasty has become a very successful treatment for all end-stage diseases of the hip joint. Charnley solved with his low frictional torque arthroplasty the problem of wear and friction with the introduction of a new bearing couple and the reduction of the head size, which set the prerequisite for the further development of stem design. This narrative review presents the major developments of regular straight stems in hip arthroplasty. It does not only provide an overview of the history but also assembles the generally scarce documentation available regarding the rationale of developments and illustrates often-unsuspected links. Charnley's success is based on successfully solving the issue of fixation of the prosthetic components to the bone, using bone cement made of polymethyl-methacrylate. In the field of cemented anchorage of the stem, two principles showing good long-term revision rates emerged over the years: the force-closed and the shape-closed principles. The non-cemented anchorage bases on prosthesis models ensure enough primary stability for osteointegration of the implant to occur. For bone to grow onto the surface, not only sufficient primary stability is required but also a suitable surface structure together with a biocompatible prosthetic material is also necessary.

Reduced thrombogenicity of surface-treated Nitinol implants steered by altered protein adsorption.

Blood-contacting medical implants made of Nitinol and other titanium alloys, such as neurovascular flow diverters and peripheral stents, have the disadvantage of being highly thrombogenic. This makes the use of systemic (dual) anti-platelet/anticoagulant therapies inevitable with related risks of device thrombosis, bleeding and other complications. Meeting the urgent clinical demand for a less thrombogenic Nitinol surface, we describe here a simple treatment of standard, commercially available Nitinol that renders its surface ultra-hydrophilic and functionalized with phosphate ions. The efficacy of this treatment was assessed by comparing standard and surface-treated Nitinol disks and braids, equivalent to flow diverters. Static and dynamic (Chandler loop) blood incubation tests showed a drastic reduction of thrombus formation on treated devices. Surface chemistry and proteomic analysis indicated a key role of phosphate and calcium ions in steering blood protein adsorption and avoiding coagulation cascade activation and platelet adhesion. A good endothelialization of the surface confirmed the biocompatibility of the treated surface. STATEMENT OF SIGNIFICANCE: Titanium alloys such as Nitinol are biocompatible and show favorable mechanical properties, which led to their widespread use in medical implants. However, in contact with blood their surface triggers the activation of the intrinsic coagulation cascade, which may result in catastrophic thrombotic events. The presented results showed that a phosphate functionalization of the titanium oxide surface suppresses the activation of both coagulation cascade and platelets, avoiding the subsequent formation of a blood clot. This novel approach has therefore a great potential for mitigating the risks associated to either thrombosis or bleeding complications (due to systemic anticoagulation) in patients with cardiovascular implants.

Grafting of calcium chelating functionalities onto PLA monofilament fiber surfaces.

Polymer surface grafting is widely used in the field of bone regeneration to increase calcium phosphate (CaP) adhesion, with the intent of improving mechanical properties of CaP-polymer composite cements. Reinforcement can be achieved using multiple combined functional groups and/or complex surface geometries that, however, concurrently influence multiple effects such as wetting, roughness, and interfacial strengthening. This study focused on the influence of a chelating group, namely aspartic acid, on the adsorption of divalent ions such as Ba2+ or Ca2+ onto poly-l-lactic acid (PLA) films. The films were analyzed using contact angle measurements and X-ray photoelectron spectroscopy. The adsorption of CaP and its interfacial mechanical properties were investigated using functionalized PLA monofilaments whose surface roughness was analyzed using white light interferometry. Mechanical analysis was conducted by performing pull-out tests. The surfaces were analyzed using scanning electron microscopy and energy dispersive X-ray spectroscopy. Using aspartic acid as a chelating group resulted in a 50 % increased adsorption of barium, an almost threefold increase in calcium coverage of the fiber compared to the control group and a twofold increase in interfacial stiffness. No significant increase in interfacial strength was determined, most likely due to the weakness of the CaP matrix, which was partially visible as residues on the monofilaments in the postfracture imaging. This study shows the potential of surfaces functionalized with aspartic acid as a simple alternative to complex polypeptide based functional groups for the adsorption of divalent ions such as calcium on poly-lactic acid in bone regenerating applications.

Influence of UV Irradiation and Cold Atmospheric Pressure Plasma on Zirconia Surfaces: An In Vitro Study

PURPOSE: To compare the influence of ultraviolet (UV) irradiation and cold atmospheric pressure plasma (CAP) treatment on surface structure, surface chemistry, cytocompatibility, and cell behavior on zirconia in vitro. MATERIALS AND METHODS: Zirconia samples (TZ-3YSBE) were treated by UV irradiation, oxygen plasma, or argon plasma for 12 minutes each and compared with the nontreated samples. Surface analysis was conducted using scanning electron microscopy, roughness analysis, and x-ray photoelectron spectroscopy. Cell proliferation, viability, and cell attachment as well as cytotoxicity were evaluated using MC3T3-E1 murine osteoblasts cultivated directly on the zirconia samples. RESULTS: Surface structure and roughness were not affected by the surface treatments. CAP and UV irradiation significantly reduced organic material and increased the surface oxidation on the zirconia samples. Furthermore, CAP and UV treatment significantly decreased the contact angle on the zirconia samples, indicating superhydrophilicity. Cell attachment was significantly increased on oxygen plasma-treated zirconia samples compared with the nontreated samples at all times (P < .001). After 24 and 48 hours, cell proliferation and viability (P < .001) were significantly increased on oxygen plasma-treated samples in comparison with the nontreated, UV-treated, and argon plasma-treated samples. Neither UV nor CAP treatment led to cytotoxicity. CONCLUSION: In vitro, surface treatment by UV irradiation or CAP causes a significant reduction of organic material, increases the hydrophilicity of zirconia, and improves the conditions for osteoblasts. Results stipulate that treatment of zirconia surfaces with oxygen plasma may favor cell proliferation.

Changes in surface characteristics of titanium and zirconia after surface treatment with ultraviolet light or non-thermal plasma.

Positive effects of irradiation with ultraviolet (UV) light or treatment with non-thermal plasma on titanium and zirconia surfaces have been described in various studies. The aim of this study was to assess and compare the changes in the physicochemical surface conditions of titanium and zirconia surfaces after a short treatment with UV light or with non-thermal plasmas of argon or oxygen. Titanium and zirconia samples with moderately rough surfaces were treated for 12 min either in a UV-light oven or in a non-thermal plasma reactor that generates non-thermal plasmas of oxygen or argon. Changes in surface conditions were assessed by confocal microscopy, dynamic contact angle measurement, and X-ray photoelectron spectroscopy (XPS). No changes in roughness occurred. Ultraviolet irradiation and non-thermal plasma significantly increased the wettability of the titanium and zirconia surfaces. X-ray photoelectron spectroscopy showed an increase of oxygen and a significant decrease of carbon after treatment with either method. Thus, ultraviolet light and non-thermal plasma were found to be able to improve the chemical surface conditions of titanium and zirconia following a short exposure time. However, further in vitro and in vivo studies are needed to determine the relevance of the results.

Photofunctionalization and non-thermal plasma activation of titanium surfaces.

OBJECTIVE: The aim of this study was to compare UV light and non-thermal plasma (NTP) treatment regarding the improvement of physical material characteristics and cell reaction on titanium surfaces in vitro after short-term functionalization. MATERIALS AND METHODS: Moderately rough (Ra 1.8-2.0 µm) sandblasted and acid-etched titanium disks were treated by UV light (0.05 mW/cm2 at λ = 360 nm and 2 mW/cm2 at λ = 250 nm) or by NTP (24 W, -0.5 mbar) of argon or oxygen for 12 min each. Surface structure was investigated by scanning electron microscopy, confocal microscopy and X-ray photoelectron spectroscopy (XPS). Hydrophilicity was assessed by dynamic contact angle measurement. Cell attachment, viability, cell proliferation and cytotoxicity were assessed in vitro using murine osteoblast-like cells. RESULTS: UV irradiation or NTP treatment of titanium surfaces did not alter the surface structure. XPS analysis revealed a significantly increased oxidation of the surface and a decrease of carbon after the use of either method. NTP and UV light led to a significant better cell attachment of murine osteoblasts; significantly more osteoblasts grew on the treated surfaces at each time point (p < 0.001). CONCLUSIONS: UV light as well as NTP modified the surface of titanium and significantly improved the conditions for murine osteoblast cells in vitro. However, results indicate a slight advantage for NTP of argon and oxygen in a short time interval of surface functionalization compared to UV. CLINICAL RELEVANCE: UV light and NTP are able to improve surface conditions of dental implants made of titanium.

Effect of oxide layer modification of CoCr stent alloys on blood activation and endothelial behavior.

CoCr alloys, in particular MP35N and L605, are extensively used in biomedical implants, for example for coronary stents. In practice, these alloys present a moderately hydrophobic surface which leads to significant platelet adhesion and consequently to risk of early thrombosis or in-stent restenosis. Surface modification of biomedical implants is known to alter their biological performances. In this study we focused on the alteration of in vitro biological responses of human cells contacting CoCr surfaces with engineered oxide layers. XPS analysis was performed to determine the composition of the oxide layer of differently treated CoCr while the bulk properties were not modified. An extensive characterization of the surfaces was performed looking at surface roughness, wettability and charge. After static exposure to blood, strongly reduced platelet and increased polymorphonuclear neutrophil adhesion were observed on treated versus untreated surfaces. Comparisons of treated and untreated samples provide evidence for wettability being an important player for platelet adhesion, although multiple factors including surface oxide chemistry and charge might control polymorphonuclear neutrophil adhesion. The differently treated surfaces were shown to be equally suitable for endothelial cell proliferation. We herein present a novel approach to steer biological properties of CoCr alloys. By adjusting their oxide layer composition, substrates were generated which are suitable for endothelial cell growth and at the same time show an altered (reduced) blood contact activation. Such treatments are expected to lead to stents of highly reproducible quality with minimal thrombogenicity and in-stent restenosis, while maintaining rapid re-endothelialization after coronary angioplasty.

Acid and alkali etching of grit blasted zirconia: Impact on adhesion and osteogenic differentiation of MG63 cells in vitro.

There is a need for evaluating zirconia surface modifications and their potential impact on the biological response of osteogenic cells. Grit blasted zirconia discs were either left untreated or underwent acid or alkaline etching. Adhesion and osteogenic differentiation of MG63 cells was determined after one week of culture. The macro-scaled roughness of the grit blasted zirconia discs, independent of the surface treatment, was within a narrow range and only slightly smoother than titanium discs. However, the alkaline- and acid-etching led to an increase of the micro-roughness of the surface. The surface modifications had no effect on cell spreading and did not cause significant change in the expression of differentiation markers. Thus, in this respective setting, morphologic changes observed upon treatment of grit blasted zirconia discs with acid or alkaline do not translate into changes in MG63 cell adhesion or differentiation and are comparable to findings with anodized titanium discs.

Chemical functionalization of bioceramics to enhance endothelial cells adhesion for tissue engineering.

To control the selective adhesion of human endothelial cells and human serum proteins to bioceramics of different compositions, a multifunctional ligand containing a cyclic arginine-glycine-aspartate (RGD) peptide, a tetraethylene glycol spacer, and a gallate moiety was designed, synthesized, and characterized. The binding of this ligand to alumina-based, hydroxyapatite-based, and calcium phosphate-based bioceramics was demonstrated. The conjugation of this ligand to the bioceramics induced a decrease in the nonselective and integrin-selective binding of human serum proteins, whereas the binding and adhesion of human endothelial cells was enhanced, dependent on the particular bioceramics.

Printability of calcium phosphate powders for three-dimensional printing of tissue engineering scaffolds.

Three-dimensional printing (3DP) is a versatile method to produce scaffolds for tissue engineering. In 3DP the solid is created by the reaction of a liquid selectively sprayed onto a powder bed. Despite the importance of the powder properties, there has to date been a relatively poor understanding of the relation between the powder properties and the printing outcome. This article aims at improving this understanding by looking at the link between key powder parameters (particle size, flowability, roughness, wettability) and printing accuracy. These powder parameters are determined as key factors with a predictive value for the final 3DP outcome. Promising results can be expected for mean particle size in the range of 20-35 µm, compaction rate in the range of 1.3-1.4, flowability in the range of 5-7 and powder bed surface roughness of 10-25 µm. Finally, possible steps and strategies in pushing the physical limits concerning improved quality in 3DP are addressed and discussed.