RESUMO
In response to the environmental impacts of conventional polyurethane adhesives derived from fossil fuels, this study introduces a sustainable alternative utilizing lignin-based polyols extracted from rice straw through a process developed at INESCOP. This research explores the partial substitution of traditional polyols with lignin-based equivalents in the synthesis of reactive hot melt polyurethane adhesives (HMPUR) for the footwear industry. The performance of these eco-friendly adhesives was rigorously assessed through Thermogravimetric Analysis (TGA), Differential Scanning Calorimetry (DSC), rheological analysis, and T-peel tests to ensure their compliance with relevant industry standards. Preliminary results demonstrate that lignin-based polyols can effectively replace a significant portion of fossil-derived polyols, maintaining essential adhesive properties and marking a significant step towards more sustainable adhesive solutions. This study not only highlights the potential of lignin in the realm of sustainable adhesive production but also emphasises the valorisation of agricultural by-products, thus aligning with the principles of green chemistry and sustainability objectives in the polymer industry.
RESUMO
This study focuses on circular bioeconomy and how to reduce the management of solid by-products in tannery facilities. To achieve this, double enzymatic hydrolysis has been developed, which allows the integrated management of both limed and fresh fleshing that are classified as category 3 animal by-products (ABPs). Fleshing has an average content of 15% fat, 20% protein and 65% water. To process these components independently, the fat fraction is separated from the protein and liquid protein fractions. This bioprocess has been developed from fleshing, yielding up to 78% mass recovery as biostimulants that are suitable for formulation and use in the fertiliser market. The efficacy of the protein fraction as a biostimulant was validated through laboratory tests, specifically by cabbage germination, which exhibited a notable improvement by 25%.
Assuntos
Indústrias , Curtume , Animais , Hidrólise , Proteínas , Resíduos IndustriaisRESUMO
This paper briefly discusses the utilization of pruning wastes as a lignocellulosic source of cellulose fibers, which could be of potential use in the development of valuable materials such as sustainable textiles and fillers for footwear components including uppers and soles. Phoenix canariensis palm leaves, one of the most common plants found in the local environment of the Alicante region (Spain), was used as a biomass raw material. Determining appropriate processing parameters and their desired range of maximum cellulose extraction states is key to improving yields. Therefore, this study aimed at determining the effect of processing conditions on cellulose extraction by optimizing the hydrothermal process, as a part of overall combined processes involving several steps. Specifically, the time of the steam-explosion stage was varied between 15 and 33 min in order to maximize the cellulose extraction yield. The composition of both the extracted fibers and the resulting by-product solutions generated during the different steps were determined by FTIR and TGA in order to analyze the effectiveness of removing hemicellulose, lignin and extractives as well as the removed substances at each stage for their further valorization. Additionally, the morphology of cellulosic fibers was evaluated by SEM and their crystallinity by XRD. Crystalline cellulose fibers were successfully extracted from pruning biomass wastes, achieving more efficient removal of hemicellulose and lignin when the hydrothermal process was assessed over 25-33 min. This resulted in finer and smoother fibers, but the crystallinity of α-cellulose decreased as the time of steam-explosion increased to 33 min. The characterization of waste solutions generated after the different extraction steps confirmed that the most effective treatments to remove lignin and hemicellulose from the cell wall are alkaline pretreatment and a hydrothermal process.
RESUMO
In this paper, the effects of ultraviolet (UV) treatments on the aloin content of Aloe vera L. gel have been analyzed. UV-A treatment to A. vera plants for 36 days led to an increase in the aloin concentration in gel, rind tissue, and latex, while a decrease in chlorophylls a and b occurred in the photosynthetic tissue as a consequence of UV treatment. The growth of Penicillium digitatum and Botrytis cinerea (artificially inoculated on the leaf surface) was drastically decreased in UV-A-treated leaves, which could be attributed to the increase in the aloin concentration by the UV-A treatment. In addition, UV-C treatment to detached leaves also led to an increase in the gel aloin concentration, at higher levels than occurred with UV-A treatment, although leaves showed severe lesions after 48 h of treatment.