RESUMEN
Silicon germanium (SiGe) is a multifunctional material considered for quantum computing, neuromorphic devices, and CMOS transistors. However, implementation of SiGe in nanoscale electronic devices necessitates suppression of surface states dominating the electronic properties. The absence of a stable and passive surface oxide for SiGe results in the formation of charge traps at the SiGe-oxide interface induced by GeOx. In an ideal ALD process in which oxide is grown layer by layer, the GeOx formation should be prevented with selective surface oxidation (i.e., formation of an SiOx interface) by controlling the oxidant dose in the first few ALD cycles of the oxide deposition on SiGe. However, in a real ALD process, the interface evolves during the entire ALD oxide deposition due to diffusion of reactant species through the gate oxide. In this work, this diffusion process in nonideal ALD is investigated and exploited: the diffusion through the oxide during ALD is utilized to passivate the interfacial defects by employing ozone as a secondary oxidant. Periodic ozone exposure during gate oxide ALD on SiGe is shown to reduce the integrated trap density (Dit) across the band gap by nearly 1 order of magnitude in Al2O3 (<6 × 1010 cm-2) and in HfO2 (<3.9 × 1011 cm-2) by forming a SiOx-rich interface on SiGe. Depletion of Ge from the interfacial layer (IL) by enhancement of volatile GeOx formation and consequent desorption from the SiGe with ozone insertion during the ALD growth process is confirmed by electron energy loss spectroscopy (STEM-EELS) and hypothesized to be the mechanism for reduction of the interfacial defects. In this work, the nanoscale mechanism for defect suppression at the SiGe-oxide interface is demonstrated, which is engineering of diffusion species in the ALD process due to facile diffusion of reactant species in nonideal ALD.
RESUMEN
Marking colon tumors for surgery is normally done with the use of India ink. However, non-fluorescent dyes such as India ink cannot be imaged below the tissue surface and there is evidence for physiological complications such as abscess, intestinal perforation and inconsistency of dye injection. A novel infrared marker was developed using FDA approved indocyanine green (ICG) dye and ultrathin hollow silica nanoshells (ICG/HSS). Using a positively charged amine linker, ICG was non-covalently adsorbed onto the nanoparticle surface. For ultra-thin wall 100 nm diameter silica shells, a bimodal ICG layer of < 3 nm is was formed. Conversely, for thicker walls on 2 µm diameter silica shells, the ICG layer was only bound to the outer surface and was 6 nm thick. In vitro testing of fluorescent emission showed the particles with the thinner coating were considerably more efficient, which is consistent with self-quenching reducing emission shown in the thicker ICG coatings. Ex-vivo testing showed that ICG bound to the 100 nm hollow silica shells was visible even under 1.5 cm of tissue. In vivo experiments showed that there was no diffusion of the ICG/nanoparticle marker in tissue and it remained imageable for as long as 12 days.
RESUMEN
Silica particles are convenient ultrasound imaging contrast agents because of their long imaging time and ease of modification; however, they require a relatively high insonation power for imaging and have low biodegradability. In this study, 2 µm ultrathin asymmetric hollow silica particles doped with iron (III) (Fe(III)-SiO2) are synthesized to produce biodegradable hard shelled particles with a low acoustic power threshold comparable with commercial soft microbubble contrast agents (Definity) yet with much longer in vivo ultrasound imaging time. Furthermore, high intensity focused ultrasound ablation enhancement with these particles shows a 2.5-fold higher temperature elevation than with Definity at the same applied power. The low power visualization improves utilization of the silica shells as an adjuvant in localized immunotherapy. The data are consistent with asymmetric engineering of hard particle properties that improve functionality of hard versus soft particles.
RESUMEN
Purpose To assess the performance of computer-aided diagnosis (CAD) systems and to determine the dominant ultrasonographic (US) features when classifying benign versus malignant focal liver lesions (FLLs) by using contrast material-enhanced US cine clips. Materials and Methods One hundred six US data sets in all subjects enrolled by three centers from a multicenter trial that included 54 malignant, 51 benign, and one indeterminate FLL were retrospectively analyzed. The 105 benign or malignant lesions were confirmed at histologic examination, contrast-enhanced computed tomography (CT), dynamic contrast-enhanced magnetic resonance (MR) imaging, and/or 6 or more months of clinical follow-up. Data sets included 3-minute cine clips that were automatically corrected for in-plane motion and automatically filtered out frames acquired off plane. B-mode and contrast-specific features were automatically extracted on a pixel-by-pixel basis and analyzed by using an artificial neural network (ANN) and a support vector machine (SVM). Areas under the receiver operating characteristic curve (AUCs) for CAD were compared with those for one experienced and one inexperienced blinded reader. A third observer graded cine quality to assess its effects on CAD performance. Results CAD, the inexperienced observer, and the experienced observer were able to analyze 95, 100, and 102 cine clips, respectively. The AUCs for the SVM, ANN, and experienced and inexperienced observers were 0.883 (95% confidence interval [CI]: 0.793, 0.940), 0.829 (95% CI: 0.724, 0.901), 0.843 (95% CI: 0.756, 0.903), and 0.702 (95% CI: 0.586, 0.782), respectively; only the difference between SVM and the inexperienced observer was statistically significant. Accuracy improved from 71.3% (67 of 94; 95% CI: 60.6%, 79.8%) to 87.7% (57 of 65; 95% CI: 78.5%, 93.8%) and from 80.9% (76 of 94; 95% CI: 72.3%, 88.3%) to 90.3% (65 of 72; 95% CI: 80.6%, 95.8%) when CAD was in agreement with the inexperienced reader and when it was in agreement with the experienced reader, respectively. B-mode heterogeneity and contrast material washout were the most discriminating features selected by CAD for all iterations. CAD selected time-based time-intensity curve (TIC) features 99.0% (207 of 209) of the time to classify FLLs, versus 1.0% (two of 209) of the time for intensity-based features. None of the 15 video-quality criteria had a statistically significant effect on CAD accuracy-all P values were greater than the Holm-Sidak α-level correction for multiple comparisons. Conclusion CAD systems classified benign and malignant FLLs with an accuracy similar to that of an expert reader. CAD improved the accuracy of both readers. Time-based features of TIC were more discriminating than intensity-based features. © RSNA, 2017 Online supplemental material is available for this article.
Asunto(s)
Medios de Contraste/uso terapéutico , Interpretación de Imagen Asistida por Computador/métodos , Neoplasias Hepáticas/diagnóstico por imagen , Ultrasonografía/métodos , Humanos , Curva ROC , Estudios RetrospectivosRESUMEN
Thin film processing technologies that promise atomic and molecular scale control have received increasing interest in the past several years, as traditional methods for fabrication begin to reach their fundamental limits. Many of these technologies involve at their heart phenomena occurring at or near surfaces, including adsorption, gas-surface reactions, diffusion, desorption, and re-organization of near-surface layers. Moreover many of these phenomena involve not just reactions occurring under conditions of local thermodynamic equilibrium but also the action of energetic species including electrons, ions, and hyperthermal neutrals. There is a rich landscape of atomic and molecular scale interactions occurring in these systems that is still not well understood. In this Special Topic Issue of The Journal of Chemical Physics, we have collected recent representative examples of work that is directed at unraveling the mechanistic details concerning atomic and molecular layer processing, which will provide an important framework from which these fields can continue to develop. These studies range from the application of theory and computation to these systems to the use of powerful experimental probes, such as X-ray synchrotron radiation, probe microscopies, and photoelectron and infrared spectroscopies. The work presented here helps in identifying some of the major challenges and direct future activities in this exciting area of research involving atomic and molecular layer manipulation and fabrication.
RESUMEN
Si0.5Ge0.5(110) surfaces were passivated and functionalized using atomic H, hydrogen peroxide (H2O2), and either tetrakis(dimethylamino)titanium (TDMAT) or titanium tetrachloride (TiCl4) and studied in situ with multiple spectroscopic techniques. To passivate the dangling bonds, atomic H and H2O2(g) were utilized and scanning tunneling spectroscopy (STS) demonstrated unpinning of the surface Fermi level. The H2O2(g) could also be used to functionalize the surface for metal atomic layer deposition. After subsequent TDMAT or TiCl4 dosing followed by a post-deposition annealing, scanning tunneling microscopy demonstrated that a thermally stable and well-ordered monolayer of TiOx was deposited on Si0.5Ge0.5(110), and X-ray photoelectron spectroscopy verified that the interfaces only contained Si-O-Ti bonds and a complete absence of GeOx. STS measurements confirmed a TiOx monolayer without mid-gap and conduction band edge states, which should be an ideal ultrathin insulating layer in a metal-insulator-semiconductor structure. Regardless of the Ti precursors, the final Ti density and electronic structure were identical since the Ti bonding is limited by the high coordination of Ti to O.
RESUMEN
Atomic layer deposition of a silicon rich SiNx layer on Si0.7Ge0.3(001), Si0.5Ge0.5(001), and Si0.5Ge0.5(110) surfaces has been achieved by sequential pulsing of Si2Cl6 and N2H4 precursors at a substrate temperature of 285 °C. XPS spectra show a higher binding energy shoulder peak on Si 2p indicative of SiOxNyClz bonding while Ge 2p and Ge 3d peaks show only a small amount of higher binding energy components consistent with only interfacial bonds, indicating the growth of SiOxNy on the SiGe surface with negligible subsurface reactions. Scanning tunneling spectroscopy measurements confirm that the SiNx interfacial layer forms an electrically passive surface on p-type Si0.70Ge0.30(001), Si0.50Ge0.50(110), and Si0.50Ge0.50(001) substrates as the surface Fermi level is unpinned and the electronic structure is free of states in the band gap. DFT calculations show that a Si rich a-SiO0.4N0,4 interlayer can produce lower interfacial defect density than stoichiometric a-SiO0.8N0.8, substoichiometric a-Si3N2, or stoichiometric a-Si3N4 interlayers by minimizing strain and bond breaking in the SiGe by the interlayer. Metal-oxide-semiconductor capacitors devices were fabricated on p-type Si0.7Ge0.3(001) and Si0.5Ge0.5(001) substrates with and without the insertion of an ALD SiOxNy interfacial layer, and the SiOxNy layer resulted in a decrease in interface state density near midgap with a comparable Cmax value.
RESUMEN
Silica nanoparticles are an emerging class of biomaterials which may be used as diagnostic and therapeutic tools for biomedical applications. In particular, hollow silica nanoshells are attractive due to their hollow core. Approximately 70% of a 500 nm nanoshell is hollow, therefore more particles can be administered on a mg/kg basis compared to solid nanoparticles. Additionally, their nanoporous shell permits influx/efflux of gases and small molecules. Since the size, shape, and composition of a nanoparticle can dramatically alter its toxicity and biodistribution, the toxicology of these nanomaterials was assessed. A single dose toxicity study was performed in vivo to assess the toxicity of 500 nm iron-doped silica nanoshells at clinically relevant doses of 10-20 mg/kg. This study showed that only a trace amount of silica was detected in the body 10 weeks post-administration. The hematology, biochemistry and pathological results show that the nanoshells exhibit no acute or chronic toxicity in mice.
Asunto(s)
Hierro/farmacocinética , Hierro/toxicidad , Nanocáscaras/análisis , Nanocáscaras/toxicidad , Dióxido de Silicio/farmacocinética , Dióxido de Silicio/toxicidad , Animales , Materiales Biocompatibles/administración & dosificación , Materiales Biocompatibles/análisis , Materiales Biocompatibles/farmacocinética , Materiales Biocompatibles/toxicidad , Femenino , Hierro/administración & dosificación , Hierro/análisis , Ratones , Nanocáscaras/administración & dosificación , Nanocáscaras/ultraestructura , Tamaño de la Partícula , Dióxido de Silicio/administración & dosificación , Dióxido de Silicio/análisis , Distribución TisularRESUMEN
The growth in efficiency of earth-abundant kesterite Cu2ZnSn(S,Se)4 (CZTSSe) solar cells has slowed, due in part to the intrinsic limitations imposed by the band tailing attributed primarily to I-II antisite exchange. In this study, density functional theory simulations show that when Ag is substituted for Cu to form kesterite Ag2ZnSnSe4 (AZTSe), the I-II isolated antisite formation energy becomes 3.7 times greater than in CZTSSe, resulting in at least an order of magnitude reduction in I-II antisite density. Experimental evidence of an optoelectronically improved material is also provided. Comparison of the low-temperature photoluminescence (PL) structure of Cu(In,Ga)Se2 (CIGSe), CZTSSe, and AZTSe shows that AZTSe has a shallow defect structure with emission significantly closer to the band edge than CZTSe. Existence of suppressed band tailing is found in the proximity of the room-temperature PL peak of AZTSe to its measured band gap. The results are consistent with AZTSe being a promising alternative to CZTSSe and CIGSe for thin film photovoltaics.
RESUMEN
Several proposed beyond-CMOS devices based on two-dimensional (2D) heterostructures require the deposition of thin dielectrics between 2D layers. However, the direct deposition of dielectrics on 2D materials is challenging due to their inert surface chemistry. To deposit high-quality, thin dielectrics on 2D materials, a flat lying titanyl phthalocyanine (TiOPc) monolayer, deposited via the molecular beam epitaxy, was employed to create a seed layer for atomic layer deposition (ALD) on 2D materials, and the initial stage of growth was probed using in situ STM. ALD pulses of trimethyl aluminum (TMA) and H2O resulted in the uniform deposition of AlOx on the TiOPc/HOPG. The uniformity of the dielectric is consistent with DFT calculations showing multiple reaction sites are available on the TiOPc molecule for reaction with TMA. Capacitors prepared with 50 cycles of AlOx on TiOPc/graphene display a capacitance greater than 1000 nF/cm(2), and dual-gated devices have current densities of 10(-7)A/cm(2) with 40 cycles.
RESUMEN
A saturated Si-Hx seed layer for gate oxide or contact conductor ALD has been deposited via two separate self-limiting and saturating CVD processes on InGaAs(001)-(2 × 4) at substrate temperatures of 250 and 350 °C. For the first self-limiting process, a single silicon precursor, Si3H8, was dosed at a substrate temperature of 250 °C, and XPS results show the deposited silicon hydride layer saturated at about 4 monolayers of silicon coverage with hydrogen termination. STS results show the surface Fermi level remains unpinned following the deposition of the saturated silicon hydride layer, indicating the InGaAs surface dangling bonds are electrically passivated by Si-Hx. For the second self-limiting process, Si2Cl6 was dosed at a substrate temperature of 350 °C, and XPS results show the deposited silicon chloride layer saturated at about 2.5 monolayers of silicon coverage with chlorine termination. Atomic hydrogen produced by a thermal gas cracker was subsequently dosed at 350 °C to remove the Si-Cl termination by replacing with Si-H termination as confirmed by XPS, and STS results confirm the saturated Si-Hx bilayer leaves the InGaAs(001)-(2 × 4) surface Fermi level unpinned. Density function theory modeling of silicon hydride surface passivation shows an Si-Hx monolayer can remove all the dangling bonds and leave a charge balanced surface on InGaAs.
RESUMEN
Current logic devices rely on 3D architectures, such as the tri-gate field effect transistor (finFET), which utilize the (001) and (110) crystal faces simultaneously thus requiring passivation methods for the (110) face in order to ensure a pristine 3D surface prior to further processing. Scanning tunneling microscopy (STM), x-ray photoelectron spectroscopy (XPS), and correlated electrical measurement on MOSCAPs were utilized to compare the effects of a previously developed in situ pre-atomic layer deposition (ALD) surface clean on the InGaAs (001) and (110) surfaces. Ex situ wet cleans are very effective on the (001) surface but not the (110) surface. Capacitance voltage indicated the (001) surface with no buffered oxide etch had a higher C(max) hypothesized to be a result of poor nucleation of HfO2 on the native oxide. An in situ pre-ALD surface clean employing both atomic H and trimethylaluminum (TMA) pre-pulsing, developed by Chobpattana et al. and Carter et al. for the (001) surface, was demonstrated to be effective on the (110) surface for producing low D(it) high C(ox) MOSCAPs. Including TMA in the pre-ALD surface clean resulted in reduction of the magnitude of the interface state capacitance. The XPS studies show the role of atomic H pre-pulsing is to remove both carbon and oxygen while STM shows the role of TMA pre-pulsing is to eliminate H induced etching. Devices fabricated at 120 °C and 300 °C were compared.
RESUMEN
There are a wide variety of silica nanoformulations being investigated for biomedical applications. Silica nanoparticles can be produced using a wide variety of synthetic techniques with precise control over their physical and chemical characteristics. Inorganic nanoformulations are often criticized or neglected for their poor tolerance; however, extensive studies into silica nanoparticle biodistributions and toxicology have shown that silica nanoparticles may be well tolerated, and in some case are excreted or are biodegradable. Robust synthetic techniques have allowed silica nanoparticles to be developed for applications such as biomedical imaging contrast agents, ablative therapy sensitizers, and drug delivery vehicles. This review explores the synthetic techniques used to create and modify an assortment of silica nanoformulations, as well as several of the diagnostic and therapeutic applications.
RESUMEN
BACKGROUND: High intensity-focused ultrasound (HIFU) is an alterative ablative technique currently being investigated for local treatment of breast cancer and fibroadenomas. Current HIFU therapies require concurrent magnetic resonance imaging monitoring. Biodegradable 500 nm perfluoropentane-filled iron-silica nanoshells have been synthesized as a sensitizing agent for HIFU therapies, which aid both mechanical and thermal ablation of tissues. In low duty cycle high-intensity applications, rapid tissue damage occurs from mechanical rather than thermal effects, which can be monitored closely by ultrasound obviating the need for concurrent magnetic resonance imaging. MATERIALS AND METHODS: Iron-silica nanoshells were synthesized by a sol-gel method on polystyrene templates and calcined to yield hollow nanoshells. The nanoshells were filled with perfluoropentane and injected directly into excised human breast tumor, and intravenously (IV) into healthy rabbits and Py8119 tumor-bearing athymic nude mice. HIFU was applied at 1.1 MHz and 3.5 MPa at a 2% duty cycle to achieve mechanical ablation. RESULTS: Ex vivo in excised rabbit livers, the time to visually observable damage with HIFU was 20 s without nanoshells and only 2 s with nanoshells administered IV before sacrifice. Nanoshells administered IV into nude mice with xenograft tumors were activated in vivo by HIFU 24 h after administration. In this xenograft model, applied HIFU resulted in a 13.6 ± 6.1 mm(3) bubble cloud with the IV injected particles and no bubble cloud without particles. CONCLUSIONS: Iron-silica nanoshells can reduce the power and time to perform HIFU ablative therapy and can be monitored by ultrasound during low duty cycle operation.
Asunto(s)
Neoplasias de la Mama/terapia , Ultrasonido Enfocado de Alta Intensidad de Ablación/instrumentación , Nanocáscaras/uso terapéutico , Animales , Femenino , Fibroadenoma/terapia , Fluorocarburos , Humanos , Hierro , Ratones , Ratones Desnudos , Conejos , Dióxido de SilicioRESUMEN
Passivation, functionalization, and atomic layer deposition nucleation via H2O2(g) and trimethylaluminum (TMA) dosing was studied on the clean Ge(100) surface at the atomic level using scanning tunneling microscopy (STM) and scanning tunneling spectroscopy (STS). Chemical analysis of the surface was performed using x-ray photoelectron spectroscopy, while the bonding of the precursors to the substrate was modeled with density functional theory (DFT). At room temperature, a saturation dose of H2O2(g) produces a monolayer of a mixture of -OH or -O species bonded to the surface. STS confirms that H2O2(g) dosing eliminates half-filled dangling bonds on the clean Ge(100) surface. Saturation of the H2O2(g) dosed Ge(100) surface with TMA followed by a 200 °C anneal produces an ordered monolayer of thermally stable Ge-O-Al bonds. DFT models and STM simulations provide a consistent model of the bonding configuration of the H2O2(g) and TMA dosed surfaces. STS verifies the TMA/H2O2/Ge surface has an unpinned Fermi level with no states in the bandgap demonstrating the ability of a Ge-O-Al monolayer to serve as an ideal template for further high-k deposition.
RESUMEN
Titanium (Ti) is widely used as anode current collectors in proton exchange membrane (PEM)-based water electrolyzers due to its self-passivated oxide layer, which protects it from corrosion in acidic solutions. However, the cost of the material and machining process for Ti is high. A wider utilization of water electrolyzers to produce hydrogen could be favored by the use of less expensive coated aluminum (Al) substrates, which could potentially replace high-cost Ti-based components. It is shown here by depositing a pinhole-free oxygen vacancy-rich titanium oxide (TiOx) protection layer by atomic layer deposition (ALD), the corrosion resistance of Al substrates in acidic environments at oxygen evolution potentials can be enhanced. The optimization of the oxygen vacancy concentration is accomplished by tuning the ALD parameters to achieve ideal stoichiometry and conformal coating on rough substrates. The robustness of the coatings was evaluated at high potentials (2.4 V vs NHE = normal hydrogen electrode) in low pH conditions. A low TiOx dissolution rate of the order of â¼6 nm year-1 was observed. By testing under industrially relevant conditions, i.e., high applied voltages (2.4 V) and low pH, an Al loss at around the zero ppb level was achieved using optimized ALD parameters. It is proposed that a 40 nm TiOx coating on Al may be adequate to provide 60,000 h of durability in a PEM water electrolyzer anode current collector.
RESUMEN
High-power impulse magnetron sputtering (HiPIMS) plus kick is a physical vapor deposition method that employs bipolar microsecond-scale voltage pulsing to precisely control the ion energy during sputter deposition. HiPIMS plus kick for AlN deposition is difficult since nitride deposition is challenged by low surface diffusion and high susceptibility to ion damage. In this current study, a systematic examination of the process parameters of HiPIMS plus kick was conducted. Under optimized main negative pulsing conditions, this study documented that a 25 V positive kick biasing for AlN deposition is ideal for optimizing a high quality film, as shown by X-ray diffraction and transmission electron microscopy as well as optimal thermal conductivity while increasing high speed deposition (25 nm/min) and obtaining ultrasmooth surfaces (rms roughness = 0.5 nm). HiPIMS plus kick was employed to deposit a single-texture 1 µm AlN film with a 7.4° rocking curve, indicating well oriented grains, which correlated with high thermal conductivity (121 W/m·K). The data are consistent with the optimal kick voltage enabling enhanced surface diffusion due to ion-substrate collisions without damaging the AlN grains.
RESUMEN
Ambient NO2 adsorption onto copper(II) phthalocyanine (CuPc) monolayers is observed using ultrahigh vacuum (UHV) scanning tunneling microscopy (STM) to elucidate the molecular sensing mechanism in CuPc chemical vapor sensors. For low doses (1 ppm for 5 min) of NO2 at ambient temperatures, isolated chemisorption sites on the CuPc metal centers are observed in STM images. These chemisorbates almost completely desorb from the CuPc monolayer after annealing at 100 °C for 30 min. Conversely, for high NO2 doses (10 ppm for 5 min), the NO2 induces a fracture of the CuPc domains. This domain fracture can only be reversed by annealing above 150 °C, which is consistent with dissociative chemisorption into NO and atomic O accompanied by surface restructuring. This high stability implies that the domain fracture results from tightly bound adsorbates, such as atomic O. Existence of atomic O on or under the CuPc layer, which results in domain fracture, is revealed by XPS analysis and ozone-dosing experiments. The observed CuPc domain fracturing is consistent with a mechanism for the dosimetric sensing of NO2 and other reactive gases by CuPc organic thin film transistors (OTFTs).
RESUMEN
The nucleation and passivation of oxide deposition was studied on defect-free GaAs (110) surfaces to understand passivation of surfaces containing only III-V heterobonds. The passivation process on GaAs (110) was studied at the atomic level using scanning tunneling microscopy while the electronic structure was determined by scanning tunneling spectroscopy (STS). The bonding of the oxidant and reductant were modeled with density functional theory. To avoid Fermi level pinning during gate oxide atomic layer deposition, a dual passivation procedure was required using both a reductant, trimethylaluminum (TMA), and an oxidant, O2 or H2O. Dosing GaAs (110) with TMA resulted in the formation of an ordered complete monolayer of dimethylaluminum which passivates the group V dangling bonds but also forms metal-metal bonds with conduction band edge states. These edge states were suppressed by dosing the surface with oxidants O2 or H2O which selectively react with group III-aluminum bonds. The presence of an ordered Al monolayer with a high nucleation density was indirectly confirmed by XPS and STS.
RESUMEN
This study evaluated the in vivo therapeutic efficacy of oncolytic serotype 5 adenovirus TAV255 in CAR-deficient tumors. In vitro experiments were performed with cell lines that expressed different levels of CAR (HEK293, A549, CT26, 4T1, and MCF-7). Low CAR cells, such as CT26, were poorly transduced by Ad in vitro unless the adenovirus was encapsulated in liposomes. However, the CT26 tumor in an immune-competent mouse model responded to the unencapsulated TAV255; 33% of the tumors were induced into complete remission, and mice with complete remission rejected the rechallenge with cancer cell injection. Encapsulation of TAV255 improves its therapeutic efficacy by transducing more CT26 cells, as expected from in vitro results. In a bilateral tumor model, nonencapsulated TAV255 reduced the growth rate of the locally treated tumors but had no effect on the growth rate of the distant tumor site. Conversely, encapsulated TAV255-infected CT26 induced a delayed growth rate of both the primary injected tumor and the distant tumor, consistent with a robust immune response. In vivo, intratumorally injected unencapsulated adenoviruses infect CAR-negative cells with only limited efficiency. However, unencapsulated adenoviruses robustly inhibit the growth of CAR-deficient tumors, an effect that constitutes an 'in situ vaccination' by stimulating cytotoxic T cells.