RESUMEN
BACKGROUND: Bioglass materials have gained significant attention in the field of tissue engineering due to their osteoinductive and biocompatible properties that promote bone cell differentiation. In this study, a novel composite scaffold was developed using a sol-gel technique to combine bioglass (BG) 58 S with a poly L-lactic acid (PLLA). METHODS AND RESULTS: The physiochemical properties, morphology, and osteoinductive potential of the scaffolds were investigated by X-ray diffraction analysis, scanning electron microscopy, and Fourier-transform infrared spectroscopy. The results showed that the SiO2-CaO-P2O5 system was successfully synthesized by the sol-gel method. The PLLA scaffolds containing BG was found to be osteoinductive and promoted mineralization, as demonstrated by calcium deposition assay, upregulation of alkaline phosphatase enzyme activity, and Alizarin red staining data. CONCLUSIONS: These in vitro studies suggest that composite scaffolds incorporating hBMSCs are a promising substitute material to be implemented in bone tissue engineering. The PLLA/BG scaffolds promote osteogenesis and support the differentiation of bone cells, such as osteoblasts, due to their osteoinductive properties.
Asunto(s)
Materiales Biocompatibles , Diferenciación Celular , Cerámica , Osteogénesis , Poliésteres , Ingeniería de Tejidos , Andamios del Tejido , Poliésteres/química , Andamios del Tejido/química , Cerámica/química , Cerámica/farmacología , Ingeniería de Tejidos/métodos , Materiales Biocompatibles/farmacología , Materiales Biocompatibles/química , Osteogénesis/efectos de los fármacos , Humanos , Diferenciación Celular/efectos de los fármacos , Regeneración Ósea/efectos de los fármacos , Osteoblastos/efectos de los fármacos , Osteoblastos/metabolismo , Espectroscopía Infrarroja por Transformada de Fourier , Células Madre Mesenquimatosas/efectos de los fármacos , Células Madre Mesenquimatosas/metabolismo , Difracción de Rayos X , Huesos/efectos de los fármacos , Huesos/metabolismo , Fosfatasa Alcalina/metabolismo , Microscopía Electrónica de RastreoRESUMEN
In the aging society, slow bone regeneration poses a serious hindrance to the quality of life. To deal with this problem, in this study, we have combined irisin with the bioglass regular beads to enhance the bone regeneration process. For this purpose, highly porous bioglass was obtained as spherical beads by using sodium alginate. The bioglass was evaluated by various analytical techniques such as SEM, EDS, XRD, and pore size distribution. The results depicted that porous bioglass was prepared correctly and SEM analysis showed a highly porous bioglass was formulated. On this bioglass, irisin was loaded with the assistance of polyvinyl alcohol (PVA) in three concentrations (50 ng/ml, 100 ng/ml, and 150 ng/ml per 1 g of bioglass). SEM analysis showed that pores are covered with PVA. The irisin release profile showed a sustained release over the time period of 7 days. In vitro, biocompatibility evaluation by the MC3T3E1 cells showed that prepared bioglass and irisin loaded bioglass (BGI50, BGI100, and BG150) are highly biocompatible. Alizarin Red staining analysis showed that after 2 weeks BGI50 samples showed highest calcium nodule formation. In vivo in the rabbit femur model was conducted for 1 and 2 months. BGI150 samples showed highest BV/TV ratio of 37.1 after 2 months. The histological data showed new bone formation surrounding the beads and with beads loaded with irisin. Immunohistochemistry using markers OPN, RUNX, COL, and ALP supported the osteogenic properties of the irisin-loaded bioglass beads. The results indicated that irisin-loaded bioglass displayed remarkable bone regeneration.
Asunto(s)
Osteogénesis , Andamios del Tejido , Animales , Conejos , Andamios del Tejido/química , Fibronectinas , Calidad de Vida , Cerámica/química , Alcohol PolivinílicoRESUMEN
Hybrid scaffolds that are based on PLA and PLA/PMMA with 75/25, 50/50, and 25/75 weight ratios and functionalized with 10 wt.% of bioglass nanoparticles (n-BG) were developed using an electrospinning technique with a chloroform/dimethylformamide mixture in a 9:1 ratio for bone tissue engineering applications. Neat PLA and PLA/PMMA hybrid scaffolds were developed successfully through a (CF/DMF) solvent system, obtaining a random fiber deposition that generated a porous structure with pore interconnectivity. However, with the solvent system used, it was not possible to generate fibers in the case of the neat PMMA sample. With the increase in the amount of PMMA in PLA/PMMA ratios, the fiber diameter of hybrid scaffolds decreases, and the defects (beads) in the fiber structure increase; these beads are associated with a nanoparticle agglomeration, that could be related to a low interaction between n-BG and the polymer matrix. The Young's modulus of PLA/PMMA/n-BG decreases by 34 and 80%, indicating more flexible behavior compared to neat PLA. The PLA/PMMA/n-BG scaffolds showed a bioactive property related to the presence of hydroxyapatite crystals in the fiber surface after 28 days of immersion in a Simulated Body Fluids solution (SBF). In addition, the hydrolytic degradation process of PLA/PMMA/n-BG, analyzed after 35 days of immersion in a phosphate-buffered saline solution (PBS), was less than that of the pure PLA. The in vitro analysis using an HBOF-1.19 cell line indicated that the PLA/PMMA/n-BG scaffold showed good cell viability and was able to promote cell proliferation after 7 days. On the other hand, the in vivo biocompatibility evaluated via a subdermal model in BALC male mice corroborated the good behavior of the scaffolds in avoiding the generation of a cytotoxic effect and being able to enhance the healing process, suggesting that the materials are suitable for potential applications in tissue engineering.
Asunto(s)
Cerámica , Nanopartículas , Poliésteres , Polimetil Metacrilato , Ingeniería de Tejidos , Andamios del Tejido , Ingeniería de Tejidos/métodos , Poliésteres/química , Polimetil Metacrilato/química , Andamios del Tejido/química , Cerámica/química , Cerámica/farmacología , Nanopartículas/química , Animales , Ratones , Huesos/efectos de los fármacos , Materiales Biocompatibles/química , Materiales Biocompatibles/farmacología , Humanos , Línea CelularRESUMEN
Injectable hydrogels find extensive application in the treatment of diabetic wound healing. However, traditional bulk hydrogels are significantly limited due to their nano-porous structure, which obstructs cell migration and tissue infiltration. Moreover, regulating inflammation and matrix metalloproteinase -9 (MMP-9) expression in diabetic wounds is crucial for enhancing wound healing. This study marks the first instance of introducing an efficient, scalable, and simple method for producing microfiber-gel granules encapsulating bioceramics powders. Utilizing this method, an injectable microporous granular microgel-fiber hydrogel (MFgel) is successfully developed by assembling microgel-fibers made from hyaluronic acid (HA) and sodium alginate (SA) loaded with small interfering RNA (siRNA) and bioglass (BG) particles. Compared to traditional hydrogels (Tgel), MFgel possesses a highly interconnected network with micron-sized pores, demonstrating favorable properties for cell adhesion and penetration in in vitro experiments. Additionally, MFgel exhibits a higher compressive modulus and superior mechanical stability. When implanted subcutaneously in mice, MFgel promotes cellular and tissue infiltration, facilitating cell proliferation. Furthermore, when applied to skin defects in diabetic rats, MFgel not only effectively regulates inflammation and suppresses MMP-9 expression but also enhances angiogenesis and collagen deposition, thereby significantly accelerating diabetic wound healing. Taken together, this hydrogel possesses great potential in diabetic wound healing applications.
RESUMEN
This study aimed to evaluate the maximum compressive strength, the modulus of elasticity, pH variation, ionic release, radiopacity and biological response of an experimental endodontic repair cement based on 45S5 Bioglass®. An in vitro and in vivo study with an experimental endodontic repair cement containing 45S5 bioactive glass was conducted. There were three endodontic repair cement groups: 45S5 bioactive glass-based (BioG), zinc oxide-based (ZnO), and mineral trioxide aggregate (MTA). In vitro tests were used to evaluate their physicochemical properties: compressive strength, modulus of elasticity, radiopacity, pH variation, and the ionic release of Ca+ and PO4. An animal model was used to evaluate the bone tissue response to endodontic repair cement. Statistical analysis included the unpaired t-test, one-way ANOVA and Tukey's test. BioG showed the lowest compressive strength and ZnO showed the highest radiopacity among the groups, respectively (p < 0.05). There were no significant differences in the modulus of elasticity among the groups. BioG and MTA maintained an alkaline pH during the 7 days of evaluation, both at pH 4 and in a pH 7 buffered solutions. PO4 was elevated in BioG, peaking at 7 days (p < 0.05). Histological analysis showed less intense inflammatory reactions and new bone formation in MTA. BioG showed inflammatory reactions that decreased over time. These findings suggest that the BioG experimental cement had good physicochemical characteristics and biocompatibility required for bioactive endodontic repair cement.
Asunto(s)
Óxido de Zinc , Animales , Vidrio , Resinas Acrílicas , Óxidos , Ensayo de MaterialesRESUMEN
The current study reports on the fabrication of composite scaffolds based on polycaprolactone (PCL) and cerium (Ce)-containing powders, followed by their characterization from compositional, structural, morphological, optical and biological points of view. First, CeO2, Ce-doped calcium phosphates and Ce-substituted bioglass were synthesized by wet-chemistry methods (precipitation/coprecipitation and sol-gel) and subsequently loaded on PCL fibres processed by electrospinning. The powders were proven to be nanometric or micrometric, while the investigation of their phase composition showed that Ce was present as a dopant within the crystal lattice of the obtained calcium phosphates or as crystalline domains inside the glassy matrix. The best bioactivity was attained in the case of Ce-containing bioglass, while the most pronounced antibacterial effect was visible for Ce-doped calcium phosphates calcined at a lower temperature. The scaffolds were composed of either dimensionally homogeneous fibres or mixtures of fibres with a wide size distribution and beads of different shapes. In most cases, the increase in polymer concentration in the precursor solution ensured the achievement of more ordered fibre mats. The immersion in SBF for 28 days triggered an incipient degradation of PCL, evidenced mostly through cracks and gaps. In terms of biological properties, the composite scaffolds displayed a very good biocompatibility when tested with human osteoblast cells, with a superior response for the samples consisting of the polymer and Ce-doped calcium phosphates.
Asunto(s)
Cerio , Poliésteres , Humanos , Polímeros , Antibacterianos , PolvosRESUMEN
Implantology is crucial for restoring aesthetics and masticatory function in oral rehabilitation. Despite its advantages, certain issues, such as bacterial infection, may still arise that hinder osseointegration and result in implant rejection. This work aims to address these challenges by developing a biomaterial for dental implant coating based on 45S5 Bioglass® modified by zirconium insertion. The structural characterization of the glasses, by XRD, showed that the introduction of zirconium in the Bioglass network at a concentration higher than 2 mol% promotes phase separation, with crystal phase formation. Impedance spectroscopy was used, in the frequency range of 102-106 Hz and the temperature range of 200-400 K, to investigate the electrical properties of these Bioglasses, due to their ability to store electrical charges and therefore enhance the osseointegration capacity. The electrical study showed that the presence of crystal phases, in the glass ceramic with 8 mol% of zirconium, led to a significant increase in conductivity. In terms of biological properties, the Bioglasses exhibited an antibacterial effect against Gram-positive and Gram-negative bacteria and did not show cytotoxicity for the Saos-2 cell line at extract concentrations up to 25 mg/mL. Furthermore, the results of the bioactivity test revealed that within 24 h, a CaP-rich layer began to form on the surface of all the samples. According to our results, the incorporation of 2 mol% of ZrO2 into the Bioglass significantly improves its potential as a coating material for dental implants, enhancing both its antibacterial and osteointegration properties.
Asunto(s)
Implantes Dentales , Circonio/farmacología , Circonio/química , Antibacterianos , Bacterias Gramnegativas , Bacterias Grampositivas , Cerámica/farmacología , Cerámica/química , Vidrio/química , Propiedades de SuperficieRESUMEN
Dental implants have emerged as one of the most consistent and predictable treatments in the oral surgery field. However, the placement of the implant is sometimes associated with bacterial infection leading to its loss. In this work, we intend to solve this problem through the development of a biomaterial for implant coatings based on 45S5 Bioglass® modified with different amounts of niobium pentoxide (Nb2O5). The structural feature of the glasses, assessed by XRD and FTIR, did not change in spite of Nb2O5 incorporation. The Raman spectra reveal the Nb2O5 incorporation related to the appearance of NbO4 and NbO6 structural units. Since the electrical characteristics of these biomaterials influence their osseointegration ability, AC and DC electrical conductivity were studied by impedance spectroscopy, in the frequency range of 102-106 Hz and temperature range of 200-400 K. The cytotoxicity of glasses was evaluated using the osteosarcoma Saos-2 cells line. The in vitro bioactivity studies and the antibacterial tests against Gram-positive and Gram-negative bacteria revealed that the samples loaded with 2 mol% Nb2O5 had the highest bioactivity and greatest antibacterial effect. Overall, the results showed that the modified 45S5 bioactive glasses can be used as an antibacterial coating material for implants, with high bioactivity, being also non-cytotoxic to mammalian cells.
Asunto(s)
Implantes Dentales , Animales , Niobio/química , Antibacterianos/química , Bacterias Gramnegativas , Bacterias Grampositivas , Materiales Biocompatibles/farmacología , Materiales Biocompatibles/química , Vidrio/química , Cerámica/química , MamíferosRESUMEN
Polyetheretherketone (PEEK) is a biocompatible, chemically and physically stable radiolucent polymer that exhibits a similar elastic modulus to the normal human bone, making it an attractive orthopedic implant material. However, PEEK is biologically inert, preventing strong enough bonding with the surrounding bone tissue when implanted in vivo. Surface modification and composite preparation are the two main strategies for the improvement of the bioactivity of PEEK. In this study, the plasma activated PEEK surfaces with the embedded bioglass, chitosan, and bioglass-chitosan mixed layers applying from the solution dip-coating technique were investigated. The most prominent factors affecting the coating biocompatibility are strictly connected with the composition of its outer surface (its charge and functional groups), hydrophilic-hydrophobic character, wettability and surface free energy, and topography (size of pores/substructures, roughness, stiffness), as well as the personal characteristics of the patient. The obtained surfaces were examined in terms of wettability and surface-free energy changes. Additionally, FTIR (Fourier Transformation Infrared Spectrometry) and SIMS (Secondary Ion Mass Spectrometry) were applied to establish and control the coating composition. Simultaneously the structure of coatings was visualized with the aid of SEM (Scanning Electron Microscopy). Finally, the obtained systems were incubated in SBF (Simulated Body Fluid) to verify the modifications' influence on the bioactivity/biocompatibility of the PEEK surface. Different structures with variable compositions, as well as changes of the wettability, were observed depending on the applied modification. In addition, the incubation in SBF suggested that the bioglass-chitosan ratio influenced the formation of apatite-like structures on the modified PEEK surfaces.
Asunto(s)
Quitosano , Humanos , Polímeros/química , Polietilenglicoles/química , Benzofenonas , Cetonas/química , Propiedades de SuperficieRESUMEN
Guttapercha (GP, trans-1,4-polyisoprene) is the most used tooth root filling material, and it must be used with an appropriate cement (typically a polydimethylsiloxane (PDMS)-based sealer) to ensure an adequate canal obturation. This study aimed to assess the bioactivity and dentin remineralization ability of a bioglass containing PDMS commercial endodontic sealer, BG-PDMS (GuttaFlow Bioseal), and to evaluate the possible influence of a GP cone (Roeko GP point) on the mineralization process. To this end, BG-PDMS disks were aged alone or in the presence of a GP cone in Hank's Balanced Salt Solution (28 d, 37 °C). Dentin remineralization experiments were carried out under the same conditions. Micro-Raman and IR analyses demonstrated that BG-PDMS is bioactive, thanks to the formation of a silica-rich layer with nucleation sites for B-type carbonated apatite deposition. This phase was thicker when BG-PDMS was aged in the presence of GP. The two materials influenced each other because GP, which alone did not show any bioactivity, nucleated a calcium phosphate phase under these conditions. Analogously, dentin remineralization experiments showed that BG-PDMS is able to remineralize dentin, especially in the presence of GP. Under the experimental conditions, GP acted as a templating agent for calcium phosphate deposition.
Asunto(s)
Compuestos de Calcio , Gutapercha , Cavidad Pulpar , Silicatos , Dimetilpolisiloxanos/farmacología , Dentina , Ensayo de MaterialesRESUMEN
Recently some borate bioactive glasses have been discovered to have an antibacterial effect when interacting with pathogenic bacteria. In this study, borate bioactive glasses (BG) doped with metal oxide (MO) ZnO, TiO2, TeO2, and CeO2 (encoded BG-Zn, BG-Ti, BG-Te, and BG-Ce, respectively) were prepared using the melt-quench method and have been characterized before and after gamma irradiation at 25.0 kGy. X-ray diffraction was performed to recognize the amorphous phases of all samples. Infrared absorption of glasses confirms vibrational bands in their wave number according to mixed main triangular and tetrahedral borate groups. After immersion in the simulated body fluid (SBF) solution, two characteristic peaks are generated indicating the bioactivity of the studied glasses through the formation of hydroxyapatite. SEM micrographs of glass after immersion display that the crystalline phases are identified to be more distinct in different shapes because of the multi-composition involved. The antibacterial activity of borate glasses was assessed against methicillin-resistant Staphylococcus aureus (MRSA) ATCC 6538. The antibacterial results showed that BG-Te was the most efficient against S. aureus ATCC 6538. Furthermore, BG-Te reduced biofilm production (79.23%) at the concentration of 20.0 mg/mL. (BG-Te) at 20.0 mg/mL significantly decreased the viability percent, cell count, protein content, and protease activity of S. aureus cells. BG-Te presents powerful activity against bacterial infections. It was necessary to equilibrate the antibacterial efficiency with the biocompatibility, so the MTT assay confirmed that BG-Te has low cytotoxicity on the human fibroblast cells (WI-38). It is expected that borate bioglass contained TeO2 could be a promising biomaterial for bone tissue engineering.
Asunto(s)
Staphylococcus aureus Resistente a Meticilina , Antibacterianos/química , Antibacterianos/farmacología , Boratos/química , Boratos/farmacología , Vidrio/química , Humanos , Staphylococcus aureusRESUMEN
OBJECTIVES: To evaluate the effect of strontium-containing titanium- and/or magnesium-doped phosphate bioactive glass on the control of dental erosion. MATERIALS AND METHODS: Fifty fragments of human enamel were divided into five groups: negative control, 45S5 bioglass, strontium-containing Ti-doped phosphate bioactive glass (PBG-Ti), strontium-containing Mg-doped phosphate bioactive glass (PBG-Mg), and strontium-containing Ti- and Mg-doped phosphate bioactive glass (PBG-TiMg). The specimens underwent cycles of erosive challenge twice daily for 5 days with 1 mL of citric acid for 2 min followed by 1 mL of the suspension with bioactive substances for 3 min. After the cycles, profilometry, roughness and microhardness testing, and scanning electron microscopy (SEM) were performed. The following statistical tests were used: one-way ANOVA (profile, roughness, and surface microhardness (%VMS) data variation), Tukey's HSD (%VMS), Games-Howell test (profilometry), Student's t test (roughness), and Pearson's correlation between the variables. RESULTS: The lower loss of enamel surface and lower %VMS was observed in the PBG-Mg and PBG-TiMg groups, and only the PBG-Mg group showed similar roughness between baseline and eroded areas (p > 0.05). On SEM micrographs, PBG-Ti and PBG-Mg groups showed lower apparent demineralization. CONCLUSION: All bioactive materials protected the enamel against erosion. However, strontium-containing phosphate bioactive glasses showed lower enamel loss, and the presence of Mg in these bioactive glasses provided a greater protective effect. CLINICAL RELEVANCE: Experimental strontium-containing phosphate bioactive glasses are effective in controlling enamel erosion. The results obtained in this study will guide the development of new dental products.
Asunto(s)
Óxido de Magnesio , Erosión de los Dientes , Esmalte Dental , Vidrio , Humanos , Fosfatos , Estroncio , Titanio , Erosión de los Dientes/prevención & controlRESUMEN
Well-diffracting protein crystals are indispensable for X-ray diffraction analysis, which is still the most powerful method for structure-function studies of biomolecules. A promising approach to growing such crystals is the use of porous nucleation-inducing materials. However, while protein crystal nucleation in pores has been thoroughly considered, little attention has been paid to the subsequent growth of crystals. Although the nucleation stage is decisive, it is the subsequent growth of crystals outside the pore that determines their diffraction quality. The molecular-scale mechanism of growth of protein crystals in and outside pores is theoretically considered. Due to the low degree of metastability, the crystals that emerge from the pores grow slowly, which is a prerequisite for better diffraction. This expectation has been corroborated by experiments carried out with several types of porous material, such as bioglass ("Naomi's Nucleant"), buckypaper, porous gold and porous silicon. Protein crystals grown with the aid of bioglass and buckypaper yield significantly better diffraction quality compared with crystals grown conventionally. In all cases, visually superior crystals are usually obtained. Our theoretical conclusion is that heterogeneous nucleation of a crystal outside the pore is an exceptional case. Rather, the protein crystals nucleating inside the pores continue growing outside them.
Asunto(s)
Proteínas , Silicio , Cristalización/métodos , Cristalografía por Rayos X , Oro , Porosidad , Proteínas/química , Silicio/química , Difracción de Rayos XRESUMEN
Bio-based and patient-specific three-dimensional (3D) scaffolds can present next generation strategies for bone tissue engineering (BTE) to treat critical bone size defects. In the present study, a composite filament of poly lactic acid (PLA) and 45S5 bioglass (BG) were used to 3D print scaffolds intended for bone tissue regeneration. The thermally induced phase separation (TIPS) technique was used to produce composite spheres that were extruded into a continuous filament to 3D print a variety of composite scaffolds. These scaffolds were analyzed for their macro- and microstructures, mechanical properties, in vitro cytotoxicity and in vivo biocompatibility. The results show that the BG particles were homogeneously distributed within the PLA matrix and contributed to an 80% increase in the mechanical strength of the scaffolds. The in vitro cytotoxicity analysis of PLA-BG scaffolds using L929 mouse fibroblast cells confirmed their biocompatibility. During the in vivo studies, the population of the cells showed an elevated level of macrophages and active fibroblasts that are involved in collagen extracellular matrix synthesis. This study demonstrates successful processing of PLA-BG 3D-printed composite scaffolds and their potential as an implant material with a tunable pore structure and mechanical properties for regenerative bone tissue engineering.
Asunto(s)
Ingeniería de Tejidos , Andamios del Tejido , Ratones , Animales , Ingeniería de Tejidos/métodos , Andamios del Tejido/química , Poliésteres/farmacología , Poliésteres/química , Regeneración Ósea , Impresión TridimensionalRESUMEN
This study aimed to characterize the chemical properties and bioactivity of an endodontic sealer (GuttaFlow Bioseal) based on polydimethylsiloxane (PDMS) and containing a calcium bioglass as a doping agent. Commercial PDMS-based cement free from calcium bioglass (GuttaFlow 2 and RoekoSeal) were characterized for comparison as well as GuttaFlow 2 doped with dicalcium phosphate dihydrate, hydroxyapatite, or a tricalcium silicate-based cement. IR and Raman analyses were performed on fresh materials as well as after aging tests in Hank's Balanced Salt Solution (28 d, 37 °C). Under these conditions, the strengthening of the 970 cm−1 Raman band and the appearance of the IR components at 1455−1414, 1015, 868, and 600−559 cm−1 revealed the deposition of B-type carbonated apatite. The Raman I970/I638 and IR A1010/A1258 ratios (markers of apatite-forming ability) showed that bioactivity decreased along with the series: GuttaFlow Bioseal > GuttaFlow 2 > RoekoSeal. The PDMS matrix played a relevant role in bioactivity; in GuttaFlow 2, the crosslinking degree was favorable for Ca2+ adsorption/complexation and the formation of a thin calcium phosphate layer. In the less crosslinked RoekoSeal, such processes did not occur. The doped cements showed bioactivity higher than GuttaFlow 2, suggesting that the particles of the mineralizing agents are spontaneously exposed on the cement surface, although the hydrophobicity of the PDMS matrix slowed down apatite deposition. Relevant properties in the endodontic practice (i.e., setting time, radiopacity, apatite-forming ability) were related to material composition and the crosslinking degree.
Asunto(s)
Calcio , Materiales de Obturación del Conducto Radicular , Apatitas/química , Calcio/química , Compuestos de Calcio/química , Fosfatos de Calcio/química , Dimetilpolisiloxanos/química , Hidroxiapatitas , Ensayo de Materiales , Materiales de Obturación del Conducto Radicular/química , Silicatos/químicaRESUMEN
BACKGROUD: Root caries in aging population was prevalent worldwide. Due to the absence of enamel and specific structure of dentine, bacteria are able to penetrate further into dentine at an earlier stage of lesion development. The aim of this study was to investigate the effect of adding of a strontium-doped bioactive glass-ceramic (HX-BGC) to a fluoride-free toothpaste on prevention of formation of artificial dentine caries. METHODS: Thirty-six human tooth specimens were allocated to three groups (n = 12 per group). Group 1 treated with slurry containing a fluoride-free toothpaste and 5% HX-BGC, Group 2 was treated with fluoride-free toothpaste slurry, and Group 3 received deionized water as a negative control. The specimens were subjected to four cycles (15 h demineralization and 8 h remineralization for one cycle) of biochemical cycling. A mixed suspension of five bacteria species (Streptococcus mutans, Streptococcus sobrinus, Lactobacillus acidophilus, Lactobacillus rhamnosus, and Actinomyces naeslundii) were prepared in brain heart infusion broth with 5% sucrose and used as acidic challenge in biochemical cycling. Subsequently, surface morphology of the dentine lesion was assessed by scanning electron microscopy, while the lesion depths and mineral loss were assessed by micro-computed tomography. RESULTS: The mean lesion depths in dentine in Groups 1 to 3 were 87.79 ± 16.99 µm, 101.06 ± 10.04 µm and 113.60 ± 16.36 µm, respectively (p = 0.002). The mean amounts of mineral loss in Groups 1 to 3 were 0.82 ± 0.10 g/cm3, 0.89 ± 0.09 g/cm3 and 0.96 ± 0.11 g/cm3, respectively (p = 0.016). No obvious differences in the surface morphology were seen among the groups. CONCLUSION: Addition of strontium-doped bioactive glass-ceramic to fluoride-free toothpaste has potential to reduce formation of dentine lesions.
Asunto(s)
Caries Dental , Pastas de Dientes , Anciano , Cariostáticos/farmacología , Cerámica/uso terapéutico , Caries Dental/prevención & control , Susceptibilidad a Caries Dentarias , Dentina , Fluoruros/farmacología , Humanos , Minerales/farmacología , Estroncio/farmacología , Estroncio/uso terapéutico , Remineralización Dental/métodos , Pastas de Dientes/uso terapéutico , Microtomografía por Rayos XRESUMEN
This aim of this study was to investigate the effects of three types of air-abrasion particles on dual-species biofilms of Fusobacterium nucleatum and Porphyromonas gingivalis, both of which were cultured on sandblasted and acid-etched (SA) titanium discs. Out of 24 SA discs with biofilm, 18 were exposed to either air-abrasion using Bioglass 45S5 (45S5 BG; n = 6), novel zinc (Zn)-containing bioactive glass (Zn4 BG; n = 6), or inert glass (n = 6). The efficiency of biofilm removal was evaluated using scanning electron microscopy (SEM) imaging and culturing techniques. Air-abrasion using 45S5 BG or Zn4 BG demonstrated a significant decrease in the total number of viable bacteria compared to discs air-abraded with inert glass or intact biofilm without abrasion. Moreover, P. gingivalis could not be detected from SEM images nor culture plates after air-abrasion with 45S5 BG or Zn4 BG. The present study showed that air-abrasion with 45S5 or Zn4 bioactive glasses can successfully eradicate dual-biofilm of F. nucleatum and P. gingivalis from sandblasted and acid-etched titanium discs.
Asunto(s)
Fusobacterium nucleatum , Porphyromonas gingivalis , Biopelículas , Microscopía Electrónica de Rastreo , TitanioRESUMEN
Recently, composite scaffolding has found many applications in hard tissue engineering due to a number of desirable features. In this present study, hydroxyapatite/bioglass (HAp/BG) nanocomposite scaffolds were prepared in different ratios using a hydrothermal approach. The aim of this research was to evaluate the adhesion, growth, viability, and osteoblast differentiation behavior of human Wharton's-jelly-derived mesenchymal stem cells (hWJMSCs) on HAp/BG in vitro as a scaffold for application in bone tissue engineering. Particle size and morphology were investigated by TEM and bioactivity was assessed and proven using SEM analysis with hWJMSCs in contact with the HAp/BG nanocomposite. Viability was evaluated using PrestoBlueTM assay and early osteoblast differentiation and mineralization behaviors were investigated by ALP activity and EDX analysis simultaneously. TEM results showed that the prepared HAp/BG nanocomposite had dimensions of less than 40 nm. The morphology of hWJMSCs showed a fibroblast-like shape, with a clear filopodia structure. The viability of hWJMSCs was highest for the HAp/BG nanocomposite with a 70:30 ratio of HAp to BG (HAp70/BG30). The in vitro biological results confirmed that HAp/BG composite was not cytotoxic. It was also observed that the biological performance of HAp70/BG30 was higher than HAp scaffold alone. In summary, HAp/BG scaffold combined with mesenchymal stem cells showed significant potential for bone repair applications in tissue engineering.
Asunto(s)
Materiales Biocompatibles/química , Cerámica/química , Hidroxiapatitas/química , Células Madre Mesenquimatosas/fisiología , Nanocompuestos/química , Gelatina de Wharton/citología , Fosfatasa Alcalina/metabolismo , Materiales Biocompatibles/farmacología , Diferenciación Celular/efectos de los fármacos , Supervivencia Celular/efectos de los fármacos , Células Cultivadas , Humanos , Células Madre Mesenquimatosas/efectos de los fármacos , Microscopía Electrónica de Transmisión/métodos , Nanocompuestos/ultraestructura , Osteoblastos/citología , Osteoblastos/efectos de los fármacos , Osteoblastos/metabolismo , Ingeniería de Tejidos/métodos , Andamios del Tejido/químicaRESUMEN
While the infection rate after primary total joint replacements (TJR) sits at 1-2%, for trauma-related surgery, it can be as high as 3.6 to 21.2% based on the type of trauma; the risk of reinfection after revision surgery is even higher. Current treatments with antibiotic-releasing PMMA-based bone cement/ beads and/or systemic antibiotic after surgical debridement do not provide effective treatment due to fluctuating antibiotic levels at the site of infection, leading to insufficient local antibiotic concentration. In addition, non-biodegradable PMMA does not support bone regrowth in the debrided void spaces and often must be removed in an additional surgery. Here, we report a bioactive glass or bioglass (BG) substrate-based biodegradable, easy to fabricate "press fitting" antibiotic-releasing bone void filling (ABVF-BG) putty to provide effective local antibiotic release at the site of infection along with support for bone regeneration. The ABVF-BG putty formulation had homogenously distributed BG particles, a porous structure, and showed putty-like ease of handling. Furthermore, the ABVF-BG putty demonstrated in vitro antibacterial activity for up to 6 weeks. Finally, the ABVF-BG putty was biodegradable in vivo and showed 100% bacterial eradication (as shown by bacterial cell counts) in the treatment group, which received ABVF-BG putty, compared to the infection control group, where all the rats had a high bacterial load (4.63 × 106 ± 7.9 × 105 CFU/gram bone) and sustained osteomyelitis. The ABVF-BG putty also supported bone growth in the void space as indicated by a combination of histology, µCT, and X-ray imaging. The potential for simultaneous infection treatment and bone healing using the developed BG-based ABVF-BG putty is promising as an alternative treatment option for osteomyelitis.
Asunto(s)
Antibacterianos/farmacología , Huesos/efectos de los fármacos , Cerámica/farmacología , Osteomielitis/tratamiento farmacológico , Vancomicina/farmacología , Cicatrización de Heridas/efectos de los fármacos , Animales , Cementos para Huesos/farmacología , Sustitutos de Huesos/farmacología , Portadores de Fármacos/farmacología , Femenino , Vidrio , Masculino , Osteomielitis/microbiología , Ratas , Ratas Sprague-DawleyRESUMEN
Few studies have characterized the clinical outcomes of 45S5 Bioglass® applied as a bone graft to that of allogeneic bone applied in calcaneal open curettage. Therefore, the purpose of the present investigation was to compare the outcomes of patients with calcaneal tumors and tumor-like lesions treated by open curettage with 45S5 Bioglass® or allogeneic bone. Of the 31 patients who underwent open curettage (18 cases of unicameral bone cysts, 7 cases of aneurysmal bone cysts, and 6 cases of intraosseous lipoma), 16 (52%) received grafts with 45S5 Bioglass® and 15 (48%) with allogeneic bone. All the feet achieved bone fusion according to the modified Neer radiographic classification system at the last follow-up examination. The mean bone ingrowth time for the grafts with 45S5 Bioglass® versus allogeneic bone was 3.71 ± 0.86 versus 4.46 ± 1.04 months (p = .038), the mean bone healing time was 4.86 ± 0.93 versus 5.73 ± 1.07 months (p = .021), and the mean incision drying time was 7.2 ± 1.8 versus 8.2 ± 1.5 days (p = .047), respectively. No differences were found in the postoperative American Orthopaedic Foot and Ankle Society ankle-hindfoot scale scores between the 2 groups (p = .213). These results show that 45S5 Bioglass® can better facilitate the formation of new bone with a faster drying time of the incision than allogeneic bone. Although both materials can benefit the clinical outcomes of calcaneal tumors and tumor-like lesions, further studies are needed to observe the long-term complications and lesion recurrence rates.