Study of a SiGeSn/GeSn/SiGeSn structure toward direct bandgap type-I quantum well for all group-IV optoelectronics.

A SiGeSn/GeSn/SiGeSn single quantum well structure was grown using an industry standard chemical vapor deposition reactor with low-cost commercially available precursors. The material characterization revealed the precisely controlled material growth process. Temperature-dependent photoluminescence spectra were correlated with band structure calculation for a structure accurately determined by high-resolution x-ray diffraction and transmission electron microscopy. Based on the result, a systematic study of SiGeSn and GeSn bandgap energy separation and barrier heights versus material compositions and strain was conducted, leading to a practical design of a type-I direct bandgap quantum well.

Temperature dependent spectral response and detectivity of GeSn photoconductors on silicon for short wave infrared detection.

The GeSn direct gap material system, with Si complementary-metal-oxide semiconductor (CMOS) compatibility, presents a promising solution for direct incorporation of focal plane arrays with short wave infrared detection on Si. A temperature dependence study of GeSn photoconductors with 0.9, 3.2, and 7.0% Sn was conducted using both electrical and optical characterizations from 300 to 77 K. The GeSn layers were grown on Si substrates using a commercially available chemical vapor deposition reactor in a Si CMOS compatible process. Carrier activation energies due to ionization and trap states are extracted from the temperature dependent dark I-V characteristics. The temperature dependent spectral response of each photoconductor was measured, and a maximum long wavelength response to 2.1 µm was observed for the 7.0% Sn sample. The DC responsivity measured at 1.55 µm showed around two orders of magnitude improvement at reduced temperatures for all samples compared to room temperature measurements. The noise current and temperature dependent specific detectivity (D*) were also measured for each sample at 1.55 µm, and a maximum D* value of 1 × 10(9) cm·âˆšHz/W was observed at 77 K.

Investigation of GeSn Strain Relaxation and Spontaneous Composition Gradient for Low-Defect and High-Sn Alloy Growth.

Recent development of group-IV alloy GeSn indicates its bright future for the application of mid-infrared Si photonics. Relaxed GeSn with high material quality and high Sn composition is highly desirable to cover mid-infrared wavelength. However, its crystal growth remains a great challenge. In this work, a systematic study of GeSn strain relaxation mechanism and its effects on Sn incorporation during the material growth via chemical vapor deposition was conducted. It was discovered that Sn incorporation into Ge lattice sites is limited by high compressive strain rather than historically acknowledged chemical reaction dynamics, which was also confirmed by Gibbs free energy calculation. In-depth material characterizations revealed that: (i) the generation of dislocations at Ge/GeSn interface eases the compressive strain, which offers a favorably increased Sn incorporation; (ii) the formation of dislocation loop near Ge/GeSn interface effectively localizes defects, leading to the subsequent low-defect grown GeSn. Following the discovered growth mechanism, a world-record Sn content of 22.3% was achieved. The experiment result shows that even higher Sn content could be obtained if further continuous growth with the same recipe is conducted. This report offers an essential guidance for the growth of high quality high Sn composition GeSn for future GeSn based optoelectronics.