Surgical application of fascia lata as a pericardial substitute in rabbits / Aplicação cirúrgica de fascia lata como substituto do pericárdio em coelhos

PURPOSE: To use fascia lata instead of pericardium and observe the presence of adhesions. METHODS: Twenty rabbits were divided into two group of ten. In group A, a 1×1 cm segment of pericardium was excised and resutured. In group B excised pericardium was substituted for autologous fascia lata. RESULTS: In the comparison of microscopic adhesion rate between two groups A, B after eight weeks, there was no significant statistical difference. CONCLUSION: Fascia lata is safe and it can be substituted for pericardium especially in repeat sternotomy in repairing congenital heart defects to avoid heart injury.

OBJETIVO: Utilizar fascia lata em vez de pericárdio e observar a presencça de aderências. MÉTODOS: Vinte coelhos foram distribuidos em dois grupos de dez. No grupo A, um 1×1 cm de segmento de pericárdio foi retirado e resuturado. No grupo B pericárdio retirado foi substituído por fáscia lata autóloga. RESULTADOS: Na comparação da taxa de aderência microscópica entre dois grupos A, B, após oito semanas, não houve diferença estatisticamente significante. CONCLUSÃO: A fascia lata é segura e pode ser substituta do pericárdio, especialmente em nova esternotomia na reparação de defeitos cardíacos congênitos para evitar lesão cardíaca.

Mechanical properties of radial bone defects treated with autogenous graft covered with hydroxyapatite in rabbit / Propriedades mecânicas de defeito de osso radial tratado com enxerto autógeno coberto com nano-hydroxyapatite em coelho

PURPOSE: To determine biomechanical property of autogenous bone graft covered with hydroxyapatite in the defect of radial bone in rabbit. METHODS: Eighteen adult male New Zealand white rabbits were used which were divided into three groups (I, II, III) of six rabbits each. A segmental bone defect of 10 mm in length was created in the middle of the right radial shaft under general effective anesthesia in all rabbits and were stabilized using mini-plate with four screws. The defects In group I were left as such without filler, whereas in group II the defect were filled up with harvested 10 mm rib bone and in group III the defect were packed with rib bone covered with nano-hydroxyapatite. All rabbits in three groups were divided into two subgroups (one month and three months duration with three rabbits in each one). RESULTS: The mechanical property and the mean load for fracturing normal radial bone was recorded 388.2±6 N whereas it was 72.4±12.8 N for group I in 1 month duration which was recorded 182.4±14.2 N for group II and 211.6±10.4 N for group III at the end of 1 month. These values were 97.6±10.2 N for group I and 324.6±8.2 N for group II and 372.6±17.4 N for group III at the end of three months after implantation. CONCLUSION: Implantation of autologous graft covered with hydroxyapatite indicated to have positive effect in integral formation of qualitative callus at the site of fracture and early re-organization of callus to regain mechanical strength too.

OBJETIVO: Determinar as propriedades biomecânicas de enxerto ósseo autógeno coberto com hidroxiapatita em defeito do osso radial em coelhos. MÉTODOS: Foram utilizados 18 coelhos adultos, machos, brancos, Nova Zelândia, distribuídos em três grupos (I, II, III) de seis coelhos cada. Um defeito segmentar de 10 mm de comprimento foi criado no meio do eixo radial direito sob anestesia geral efetiva em todos os coelhos e foram fixados usando mini-placa com quatro parafusos. Os defeitos no grupo I foram deixados sem preenchimento, enquanto no grupo II o defeito foi preenchido com 10 mm de costela recoberta com nano-hidroxiapatita. Os coelhos nos três grupos foram distribuídos em dois subgrupos (Um e três meses, com três coelhos cada um). RESULTADOS: A propriedade mecânica e a média do peso para fraturar o osso radial normal foi 388,2±6 N, enquanto para o Grupo I, com um mês foi 72,4±12,8 N, para o grupo II 182,4±14,2 N e para o Grupo III 211,6±10,4 N. Após três meses de implantação, os valores foram 97,6±10,2 N para o Grupo I, 324,6±8,2 N para o Grupo II e 372,6±17,4 N para o Grupo III. CONCLUSÃO: A implantação de enxerto autólogo recoberto com hidroxiapatita indicou ter um efeito positivo na formação integral qualitativa do calo ósseo no local da fratura e precoce reorganização do calo com recuperação da força mecânica.