The effects of TiO2 nanotubes on bond strength and radiopacity of a self-adhesive resin cement in self-curing mode / Os efeitos de nanotubos de TiO2 na resistência de união e radiopacidade de um cimento resinoso auto-adesivo no modo auto-polimerizável

Objective: The aim of this in vitro study w as t o analyze the influence of the titanium dioxide nanotubes i n a self-cure mode polymerization of a dual resin luting agent through push out bond strength and radiopacity tests. Material and Methods: After mixed with a commercial du al self-adhesive resin cement, three concentrations o f tit anium dioxide nanotubes (0.3, 0.6, and 0.9% by weight) we re analyzed in self-curing mode. T he bond strength to bovine root dentin and fi berglass posts was assessed with the push out bond str ength t est and was evaluated in three thirds (cervical, middle and apical) (n=10), followed by failure mode analysis (SEM), and the ISO standard 9917-2 was followed for radiopacity test (n=10). Data were statistically analyzed by one-way ANOVA test, followed by Tukey's test (α=0.05). Results: Reinforced self-adhesive resin cement with 0.6% titanium dioxide nanotubes showed significant difference compared to the control gr oup for push out test (p=0.00158). The modified groups did not s how significant difference among thirds (p=0.782). Radiopacity sh owed higher value for group w ith 0.9% titanium dioxide nanotubes in comparison w ith control group (p<0.001). Conclusion: The addition of titanium dioxide nanotubes to a self-adhesive resin cement increased the bond strength to dentin and radiopacity values in the self-cure polymerization mode (AU)

Objetivo: O objetivo deste estudo in vitro foi analisar a influência de nanotubos de dióxido de titânio na polimerização química de um agente cimentante resinoso dual através de testes de resistência à união e radiopacidade. Material e Métodos: Após misturado com um cimento resinoso auto-adesivo comercial, três concentrações de nanotubos de dióxido de titânio (0,3, 0,6 e 0,9% em peso) foram analisadas. A resistência da união para a dentina da raiz bovina e os pinos de fibra de vidro foi avaliada pelo teste de push-out e avaliada em três terços (cervical, médio e apical) (n = 10), seguido pelo análise de modo de falha (MEV) e a norma ISO 9917-2 foi seguido para teste de radiopacidade (n = 10). Os dados foram analisados estatisticamente pelo teste ANOVA um fator seguido do teste de Tukey (α = 0,05). Resultados: O cimento resinoso auto-adesivo reforçado com nanotubos de dióxido de titânio a 0,6% mostrou diferença significativa em comparação com o grupo controle para teste de push-out (p=0,00158). Os grupos modificados não mostraram diferença significativa entre os terços (p=0,782). A radiopacidade mostrou maior valor para o grupo com nanotubos de dióxido de titânio 0,9% em comparação com o grupo controle (p<0,001). Conclusão: A adição de nanotubos de dióxido de titânio a um cimento resinoso auto-adesivo aumentou a os valores de resistência de união à dentina e radiopacidade no modo de polimerização química do agente cimentante (AU)

Correlation between mechanical properties and stabilization time of chemical bonds in glass-ionomer cements

Abstract The objective was to evaluate the compressive strength (CS), diametral tensile strength (DTS), flexural strength (FS), and Knoop microhardness (KH) of different conventional restorative glass-ionomer cements (GICs) and to correlate these mechanical properties (MP) with the stabilization time (ST) of their chemical bonds. Eighteen GICs were tested: Bioglass [B], Chemfil Rock [CR], Equia Forte [EF], Gold Label 2 [GL2], Gold Label 9 [GL9], Glass Ionomer Cement II [GI], Ionglass [IG], Ion Z[ IZ], Ionomaster [IM], Ionofil Plus [IP], Ionostar Plus [IS], Ketac Molar Easymix [KM], Magic Glass [MG], Maxxion R [Ma], Riva Self Cure [R], Vidrion R [V], Vitro Fil [VF] and Vitro Molar [VM]. The mechanical strength tests were performed in a universal testing machine. KH readings were done with a diamond indenter. STs were examined by Fourier Transform Infrared spectroscopy (FTIR). Data were analyzed with ANOVA and Tukey test (p<0.05). The Spearman rank test was used to evaluate the dependence between the MPs and ST results. The highest MP values were EF, GL2, GL9, GI and KM and the lowest for MG, MA, B, VF and IM. The longest ST was for GL2 and the shortest was for B. ST correlated positively with MP. GICs with longer chemical bonds ST are generally stronger and the ST value obtained from FTIR was useful in predicting the strength of GICs tested.

Understanding the interaction of resin composite with light for predictable aesthetic results in anterior teeth: A case report / Compreensão da interação das resinas compostas com a luz para resultados estéticos previsíveis em dentes anteriores: Relato de caso

This case report illustrates a conservative technique for reintervention on anterior composite restorations in a young patient with composite veneers. The treatment incorporated the use of photos and digital planning to establish a harmonious smile design. In order to conserve the dental tissues, existing resin composites restorations in maxillary anterior teeth were carefully removed to minimize enamel reduction, followed by a study of color and shade of teeth considering factors such as hue, chroma, luminosity, opacity, translucency and light effects. Eight direct veneers were built up with resin composite taking the optical properties of the material into account and their influence on the thickness of the layers that create specific light effects when superimposed on each other. To obtain excellent results with a predictable working protocol, nanohybrid composite systems facilitate good aesthetics, avoiding more invasive treatment in an economic manner.(AU)

O presente relato de caso ilustra uma técnica conservadora para a re-intervenção em restaurações diretas de resina composta em pacientes jovens. O tratamento consistiu em fotos e planejamento digital para obtenção de um desenho digital do sorriso individual e harmonioso. De acordo com os princípios de máxima conservação da estrutura dentária, as restaurações existentes nos dentes superiores anteriores foram criteriosamente removidas para minimizar a redução do esmalte, seguido do estudo de cor e sombra dos dentes considerando fatores como matiz, croma, valor, opacidade, translucidez e efeitos de luz. Oito facetas diretas foram realizadas em resina composta considerando as propriedades ópticas do material e a influência destas na espessura das camadas de resina para criar efeitos de luz singulares quando sobrepostas. Para a execução de uma odontologia estética e consciente, em associação a um protocolo de trabalho previsível, os sistemas de resinas compostas nanohibridas possibilitam resultados estéticos satisfatórios, evitando tratamentos mais invasivos de maneira economicamente viável.(AU)