Susceptibility of fluorotic enamel to dental erosion-abrasion

Abstract Dental hard tissue conditions can be of pre- or post-eruptive nature, such as enamel fluorosis and erosive tooth wear (ETW), respectively. Dental enamel fluorosis is caused by the chronic and excessive intake of fluoride during enamel development, leading to increased fluoride concentration and increased porosity. ETW has become a common clinical condition and often impairs dental function and aesthetics. This in vitro study tested the hypothesis that fluorotic enamel presents different susceptibility to dental erosion-abrasion. It consisted of a 3×3×2 factorial design, considering a) fluorosis severity: sound (TF0), mild (TF1-2), moderate (TF3-4); b) abrasive challenge: low, medium, and high; and c) erosive challenge: yes or no. A total of 144 human teeth were selected according to the three fluorosis severity levels (n=48), and subdivided into six groups (n = 8) generated by the association of the different erosive and abrasive challenges. Enamel blocks (4×4 mm) were prepared from each tooth and their natural enamel surfaces subjected to an erosion-abrasion cycling model. After cycling, the depth of the lesions in enamel was assessed by profilometry. ANOVA showed that the three-way and two-way interactions among the factors were not significant (p > 0.20). Enamel fluorosis level (p=0.638) and abrasion level (p = 0.390) had no significant effect on lesion depth. Acid exposure caused significantly more enamel surface loss than water (p < 0.001). Considering the limitations of this in vitro study, fluorosis did not affect the susceptibility of enamel to dental erosion-abrasion.

Fluorotic Enamel Susceptibility to Dental Erosion and Fluoride Treatment

Abstract The purpose of this in vitro study was to test the hypothesis that fluoride treatment can prevent dental erosion on fluorotic enamel of different severities. It followed a 3×2 factorial design, considering a) fluorosis severity: sound (TF0, Thylstrup-Fejerskov Index), mild (TF1-2), moderate (TF3-4); and b) fluoride treatment: 0 (negative control) and 1150ppmF. Human molars with the three fluorosis severities (n=16, each) were selected and randomly assigned to the two fluoride treatments (n=8). Enamel blocks (4×4mm) were prepared from each tooth and subjected to a dental erosion cycling model, for 10 days. The daily cycling protocol consisted of erosive challenges (1% citric acid, pH 2.4), interspersed by periods of immersion in artificial saliva, and three 2-minute treatments with either 0 or 1150ppm F. The enamel volume loss (mm3) was calculated by subtracting values obtained by microtomography before and after cycling. Two-Way ANOVA showed no significant interaction between fluorosis severity and fluoride treatment (p=0.691), and no significant effect for either fluorosis severity (TF0 mean±standard-deviation: 13.5(10-2±0.42(10-2, TF1-2: 1.50(10-2±0.52(10-2, TF3-4: 1.24(10-2±0.52(10-2, p=0.416) or treatment (0ppmF: 1.49(10-2±0.53(10-2; 1150ppmF: 1.21(10-2±0.42(10-2; p=0.093), when evaluated independently. Considering the limitations of this in vitro study, the presence and severity of fluorosis in enamel do not appear to affect its susceptibility to dental erosion. Fluoride treatment was not effective in preventing the development of dental erosion in both sound and fluorotic enamel substrates under our experimental conditions.

Resumo Este estudo in vitro foi testou a hipótese de que o tratamento com flúor pode prevenir a erosão dentária no esmalte fluorótico de diferentes severidades. O objetivo deste estudo foi: investigar o efeito protetor dos fluoretos contra a erosão e abrasão simuladas no esmalte fluorótico. Seguiu um desenho fatorial 3×2, considerando a) severidade da fluorose em 3 níveis: hígido (TF0, Índice Thylstrup-Fejerskov), suave (TF1-2), moderada (TF3-4); b) tratamento com flúor: 0 (controle negativo) e 1150ppmF. Molares humanos com as três severidades de fluorose (n=16, cada) foram selecionados e distribuídos aleatoriamente para os dois tratamentos com flúor (n=8). Blocos de esmalte (4×4mm) foram preparados a partir de cada dente e submetidos a um modelo de ciclo de erosão dentária, por 10 dias. O protocolo de ciclagem diária consistiu em seis desafios erosivos de 5 minutos (1% de ácido cítrico, pH 2,4), intercalados por seis períodos de imersão em saliva artificial e três tratamentos de 2 minutos com 0 ou 1150ppmF. O volume do esmalte perdido foi calculado subtraindo o perfil superficial 3D obtido por microtomografia antes e depois da ciclagem. A ANOVA de dois fatores não mostrou interação significativa entre a severidade da fluorose e o tratamento com flúor (p = 0,691) e nenhum efeito significativo para a severidade da fluorose (TF0 média+/desvio padrão: 13,5(10-2±0,42(10-2, TF1-2: 1,50(10-2±0,52(10-2, TF3-4: 1,24(10-2±0,52(10-2, p=0,416) ou tratamento (0: 1,49(10-2±0,53(10-2; 1150ppmF: 1,21(10-2±0,42(10-2, p=0,093), quando avaliados independentemente. Considerando as limitações deste estudo in vitro, a presença e severidade da fluorose no esmalte não parece afetar sua suscetibilidade à erosão dentária. O tratamento com flúor não foi eficaz na prevenção do desenvolvimento da erosão dentária em esmalte hígido e fluorótico, sob as condições experimentais utilizadas.