Análise da porosidade superficial em materiais reembasadores rígidos. Efeito da desinfecção por irradiação de energia de microondas / The effect of microwave disinfection on the surface porosity of hard denture reline materials

Este estudo avaliou o efeito da desinfecção por irradiação de energia de microondas na porosidade superficial de quatro reembasadores rígidos (Kooliner - K, New Truliner - NT, Tokuso Rebase - TR, Ufi Gel Hard ­ UGH) e uma resina termopolimerizável para base de prótese (Lucitone 550 - L). Vinte amostras de cada material (20 x 10 x 3mm) foram divididas em 4 grupos (n=5): G1 ­ sem tratamento ­ controle; G2 ­ amostras imersas em 200 mL de água destilada e submetidas a 2 ciclos de irradiação (650W/6min) no mesmo dia; G3 ­ 1 ciclo diário de irradiação, por 7 dias, com as amostras imersas em água destilada entre os ciclos; e G4 ­ amostras imersas em água destilada a 370 C, por 7 dias. As amostras foram fotografadas em microscópio eletrônico de varredura e as microfotografias analisadas em analisador de imagem Leica Qwin, para determinar o número e a área total de poros. Para avaliar a porosidade entre a região central e a periferia, foi utilizado o teste não-paramétrico de Wilcoxon ao nível de 5% de significância. Para avaliar a porosidade entre os grupos experimentais foi utilizado o teste de KruskalWallis, seguido por comparações múltiplas não-paramétricas, também ao nível de 5% de significância. Os resultados demonstraram que não houve diferença significativa (P>0,05) entre a região central e a periferia. A avaliação entre os grupos experimentais demonstrou que a porosidade do material K foi significantemente aumentada (P<0,05), após 7 ciclos de irradiação. Nenhuma diferença significante (P>0,05) foi encontrada para os materiais NT e L, em todas as condições avaliadas. Quando comparada ao grupo G1 (sem tratamento), a porosidade da TR e UGH foi significantemente diminuída (P<0,05), após 7 ciclos de irradiação. Concluiu-se que: 1) As irradiações por energia de microondas aumentaram o número de poros para o material K (P<0,05), quando este foi submetido a 7 ciclos, em relação ao G1. Entretanto, a área total de poros não exibiu essa influência (P>0,05) em todos os grupos avaliados. 2) O material NT não sofreu efeito das irradiações para o número de poros em todos os grupos. Entretanto, a área de poros foi reduzida (P<0,05), quando foram utilizados 7 ciclos (G3), em comparação a 2 ciclos (G2). 3) As microondas reduziram o número de poros para o material TR (P<0,05), quando este foi submetido a 7 ciclos, em comparação ao G1 e G2. Sua área total de poros, no G3, exibiu redução significativa, em relação aos demais grupos avaliados. 4) A resina UGH, quando submetida a 7 ciclos de irradiação (G3), teve o número de poros reduzido (P<0,05), em relação ao G1 e G4. Entretanto, a área total de poros foi estatisticamente igual para todos os grupos. 5) O número e a área de poros do material L não foram influenciados (P>0,05) pelas irradiações

This study evaluated the effect of microwave irradiation on the surface porosity of four hard chairside reline materials (Kooliner-K, New TrulinerNT, Tokuso Rebase-TR, Ufi Gel Hard­UGH) and one heat-polymerizing denture base acrylic resin (Lucitone 550-L) Twenty specimens (20X10X3mm) were made for each material and divided into four groups (n=5): G1-no treatment (control), G2­specimens immersed in distilled water and submitted to 2 cycles of microwave irradiation (650W/6 min) consecutively on the same day; G3­daily microwave irradiation for 7 days, with specimens immersed in distilled water at 370 C between exposures; G4­specimens immersed in distilled water at 370 C for 7 days. Scanning electron microphotographs of the specimens (SEM) were analyzed using Leica Qwin image analyser software to determine the number and total area of porosities. Data were statistically analyzed with Wilcoxon test for paired analysis (P=0.05) to determine differences between the center and the periphery. Differences between the experimental groups were tested using the Kruskal-Wallis test. The results demonstrated that the number and the total area of pores did not differ significantly between the central and peripheral zones. The number and the total area of pores of K was significantly increased after 7 cycles (P<.05). Materials NT and L specimens showed no significant differences in the number of pores among all groups evaluated. However, for material NT, significant difference (P<.05) was observed between G2 and G3 in the total area of pores. The number of pores of TR and UGH was significantly decreased (P<.05) after 7 cycles when compared to G1. The area total of pores of the TR was significantly affected after 7 cycles. It was concluded that 1) Microwave irradiation promoted a significant increased (P<.05) in the number of pores for material K after 7 cycles; however, the total area of pores was not affect by irradiation in all groups evaluated. 2) Material NT was not affected by irradiation for the number of pores; however, the total area of pores was decrease after 7 cycles, when compared to G2. 3) For material TR, microwave irradiation decreased (P<.05) the number of pores after 7 cycles, compared to G1 and G2. The total area of pores of G3 was significantly decreased after 7 cycles. 4) Material UGH showed a significant decrease (P<.05) for number of pores when submitted to 7 cycles, compared to G1 and G4; however, the total area of pores was statically equal in all groups evaluated 5) For material L, the number and total area of pores were not affected by irradiations

Análise da porosidade superficial em materiais reembasadores rígidos. Efeito da desinfecção por irradiação de energia de microondas / The effect of microwave disinfection on the surface porosity of hard denture reline materials

Este estudo avaliou o efeito da desinfecção por irradiação de energia de microondas na porosidade superficial de quatro reembasadores rígidos (Kooliner - K, New Truliner - NT, Tokuso Rebase - TR, Ufi Gel Hard - UGH) e uma resina termopolimerizável para base de prótese (Lucitone 550 - L). Vinte amostras de cada material (20x10x3mm) foram divididas em 4 grupos (n=5): G1 - sem tratamento - controle; G2 - amostras imersas em 200mL de água destilada e submetidas a 2 ciclos de irradiação (650W/6min) no mesmo dia; G3 - 1 ciclo diário de irradiação, por 7 dias, com as amostras imersas em água destilada entre os ciclos; e G4 - amostras imersas em água destilada a 37ºC, por 7 dias. As amostras foram fotografadas em microscópio eletrônico de varredura e as microfotografias analisadas em analisador de imagem Leica Qwin, para determinar o número e a área total de poros. Para avaliar a porosidade entre a região central e a periferia, foi utilizado o teste não paramétrico de Wilcoxon ao nível de...

Avaliaçäo da distância intercondilar em pacientes jovens / Evaluation of the intercondylar distance in young patients

O objetivo deste trabalho foi verificar se a distância intercondilar (DI) de uma amostra de 80 pacientes, com idades entre 19 e 26 anos, estava de acordo com a afirmaçäo de DAWSON (1993) de que poucos pacientes têm DI variando mais que 10 mm em relaçäo à média de 110 mm, e discutir a individualizaçäo da DI no articulador. As medidas realizadas com arco facial (modelo 8600A, Gnatus, Ribeiräo Preto, Brasil) revelaram uma média de 118,16 mm de DI, estatisticamente diferente da medida dada por DAWSON (1993), a nível de 1 por cento. A distância intercondilar é um dos determinantes da morfologia oclusal dos dentes e, portanto, sua transferência, para o articulador, para a confecçäo de restauraçöes protéticas é recomendada na literatura mundial. Entretanto, uma padronizaçäo dos arcos faciais auriculares é necessária

O papel funcional da guia anterior na reabilitaçäo oral / The anterior guidance importance in an oral rehabilitation

Em uma reabilitaçäo oral säo os dentes anteriores os primeiros a serem confeccionados e através deste ato satisfazer as necessidades estéticas e fonéticas do paciente, bem como estabilizar a mandíbula na posiçäo cêntrica. Uma guia anterior funcionalmente compatível é benéfica ao sistema mastigatório evitando e previnindo contatos posteriores durante os movimentos mandibulares excêntricos. A GA ocupa um papel de igual importância ao lado da RC e da DV