ABSTRACT
@#Introduction: Application of nano-engineered fingerprint dusting powders has been a recent trend to achieve latent fingermark development with superior ridge clarity. As such, efforts have been made to utilise natural resources to increase the sustainability of these emerging nano-engineered powders. Lithium-doped zinc oxide, primarily used as white pigments, have been previously applied to latent fingermarks with success. In the current study, nanostructured zinc oxide, synthesised using neem extract as the reducing agent, was evaluated for fingermark development on non-porous surfaces. Methods: The reduction of zinc nitrate hexahydrate was facilitated by neem extract, prepared by boiling neem leaves in distilled water. The thick yellow paste recovered was calcined in the furnace to produce a light yellow powder. Physicochemical composition of the powder was determined using microscopic and spectroscopic instruments. The effectiveness of the powder was tested on natural fingermark deposited on several non-porous surfaces. Results: Nanostructured zinc oxide with particle size ranging in between 1 to 3 µm consisting of highly aggregated spherical particle with less than 100 nm dimensions were synthesised. Developed fingermarks revealed excellent ridge details and contrast on dark coloured surfaces. Studying the fingermark closely under scanning electron microscope displayed selective distribution of particle on the ridges of the fingermark residue and very minimal deposition on the fingermark valleys. Conclusion: Nanostructured zinc oxide fabricated using green chemistry approach can be applied for the development of fingermark. Nevertheless, future works can be undertaken to enhance particle dispersity and to confer strong photoluminescence to the zinc oxide nanoparticles.